Fluorinated elastomer composition and method for its production, molded product, cross-linked product, and covered electric wire

Patent metadata

Field	Value
Publication number	US-2016196895-A1
Application number	US-201615070459-A
Country	US
Kind code	A1
Filing date	Mar 15, 2016
Priority date	Sep 25, 2013
Publication date	Jul 7, 2016
Grant date	—

Abstract

To provide a fluorinated elastomer composition which is excellent in flexibility, heat resistance and flame retardance, and a molded product, cross-linked product and covered electric wire, using such a fluorinated elastomer composition.
A fluorinated elastomer composition comprising a tetrafluoroethylene/propylene copolymer (a), an ethylene/tetrafluoroethylene copolymer (b), an ethylene copolymer (c) containing epoxy groups and a flame retardant (d), wherein the mass ratio [(a)/(b)] of (a) to (b) is from 70/30 to 40/60, the mass ratio [(b)/(c)] of (b) to (c) is from 100/0.1 to 100/10, and the content of (d) is from 0.1 to 30 parts by mass per 100 parts by mass of the total content of (a), (b) and (c).

First claim

What is claimed is:

1 . A fluorinated elastomer composition comprising a tetrafluoroethylene/propylene copolymer (a), an ethylene/tetrafluoroethylene copolymer (b), an ethylene copolymer (c) containing epoxy groups and a flame retardant (d), wherein
the mass ratio [(a)/(b)] of the tetrafluoroethylene/propylene copolymer (a) to the ethylene/tetrafluoroethylene copolymer (b) is from 70/30 to 40/60, the mass ratio [(b)/(c)] of the ethylene/tetrafluoroethylene copolymer (b) to the ethylene copolymer (c) containing epoxy groups is from 100/0.1 to 100/10, and the content of the flame retardant (d) is from 0.1 to 30 parts by mass per 100 parts by mass of the total content of the tetrafluoroethylene/propylene copolymer (a), the ethylene/tetrafluoroethylene copolymer (b) and the ethylene copolymer (c) containing epoxy groups.

2 . The fluorinated elastomer composition according to claim 1 , wherein the flame retardant (d) is at least one member selected from the group consisting of antimony trioxide, a phosphoric acid ester and polytetrafluoroethylene.

3 . The fluorinated elastomer composition according to claim 1 , wherein the tetrafluoroethylene/propylene copolymer (a) is a copolymer comprising from 35 to 70 mol % of units derived from tetrafluoroethylene, from 25 to 55 mol % of units derived from propylene, and from 0 to 40 mol % of units derived from other monomer, and
the ethylene/tetrafluoroethylene copolymer (b) is a copolymer comprising from 45 to 70 mol % of units derived from tetrafluoroethylene, from 30 to 55 mol % of units derived from ethylene, and from 0 to 10 mol % of units derived from other monomer.

4 . The fluorinated elastomer composition according to claim 1 , wherein the ethylene copolymer (c) containing epoxy groups is at least one member selected from the group consisting of an ethylene/glycidyl methacrylate copolymer, an ethylene/glycidyl methacrylate/vinyl acetate copolymer, an ethylene/methyl acrylate/glycidyl methacrylate copolymer and an ethylene/ethyl acrylate/glycidyl methacrylate copolymer.

5 . The fluorinated elastomer composition according to claim 1 , which has a melt flow rate of from 4 to 50 g/10 min. as measured at a temperature of 297° C. under a load of 49N.

6 . A method for producing the fluorinated elastomer composition as defined in claim 1 , which comprises a step of kneading the tetrafluoroethylene/propylene copolymer (a), the ethylene/tetrafluoroethylene copolymer (b), the ethylene copolymer (c) containing epoxy groups and the flame retardant (d) under a heating condition of from 250 to 320° C.

7 . A molded product obtained by molding the fluorinated elastomer composition as defined in claim 1 .

8 . A cross-linked product obtained by cross-linking the fluorinated elastomer composition as defined in claim 1 .

9 . A covered electric wire comprising a conductor and a covering material for covering the conductor, wherein the covering material is the fluorinated elastomer composition as defined in claim 1 .

10 . A covered electric wire comprising a conductor and a covering material for covering the conductor, wherein the covering material is the cross-linked product as defined in claim 8 .

Assignees

• Asahi Glass Co Ltd

Inventors

• Iruya Ken
• Yasuda Satoko
• Taguchi Daisuke
• Matsuoka Yasuhiko

Classifications

• H01B7/041

  attached to mobile objects, e.g. portable tools, elevators, mining equipment, hoisting cables · CPC title

• H01B3/445 Primary

  from vinylfluorides or other fluoroethylenic compounds · CPC title

• H01B7/0045

  Cable-harnesses · CPC title

• H01B7/295

  using material resistant to flame · CPC title

• C08L27/18 Primary

  Homopolymers or copolymers or tetrafluoroethene · CPC title