Flame-retardant sheet or film, products comprising the same and process for production thereof

Patent metadata

Field	Value
Publication number	US-2016181576-A1
Application number	US-201414900386-A
Country	US
Kind code	A1
Filing date	Jun 18, 2014
Priority date	Jun 26, 2013
Publication date	Jun 23, 2016
Grant date	—

Abstract

A thin sheet or film excellent in flame retardancy and light-blocking properties is provided. A battery pack case and others with high flame retardancy are each molded from this thin film. A thin sheet or film Including a specific phosphorus-containing flame retardant in a polycarbonate resin is excellent in thickness accuracy, flame retardancy and appearance. A thin sheet or film excellent in flame retardancy and also having a thickness of 0.01 to 0.25 mm was formed when controlling its thickness uniformly during sheet or film molding. Further, upon addition of carbon black, the resulting sheet or film was found to have good light-blocking properties and higher flame retardancy. Moreover, when used as a film packaging material for battery packs, the sheet or film of the present invention was found to be excellent in film strength and ultrasonic weldability.

First claim

1 . A flame-retardant sheet or film having a thickness of 0.01 to 0.25 mm, which is molded from a polycarbonate resin composition containing, relative to 100 parts by mass of a polycarbonate resin, 7 to 30 parts by mass of a flame retardant comprising a phosphorus-containing flame retardant represented by the following general formula (1) or (2) or (3), wherein the thickness distribution at the time of sheet or film molding in the direction (TD) perpendicular to the direction of resin flow is controlled to be within ±10% of the average thickness:

[in formula (1), R 1 , R 2 , R 3 and R 4 each represent an alkyl group containing 1 to 6 carbon atoms or an aryl group containing 6 to 20 carbon atoms which may be substituted with an alkyl group, p, q, r and s are each 0 or 1, k is an integer of 1 to 5, and X 1 represents an arylene group];

[in formula (2), t is an integer of 3 to 25, and R 5 and R 6 , which may be the same or different, each represent an aryl group or an alkylaryl group]; or

[in formula (3), u is an integer of 3 to 10,000, R 9 represents at least one selected from a —N═P(OR 7 ) 3 group, a —N═P(OR 8 ) 3 group, a —N═P(O)OR 7 group and a —N═P(O)OR 8 group, and R 10 represents at least one selected from a —P(OR 7 ) 4 group, a —P(OR 8 ) 4 group, a —P(O)(OR 7 ) 2 group and a —P(O)(OR 8 ) 2 group, wherein R 7 and R 8 , which may be the same or different, each represent an aryl group or an alkylaryl group].

2 . The flame-retardant sheet or film according to claim 1 , wherein the polycarbonate resin composition further contains 12 parts by mass or less of one or more inorganic fillers, relative to 100 parts by mass of the polycarbonate resin.

3 . The flame-retardant sheet or film according to claim 2 , wherein the polycarbonate resin composition further contains carbon black, wherein the content of carbon black is 0.0001 to 10 parts by mass, relative to 100 parts by mass of the polycarbonate resin, and wherein the total light transmittance of the flame-retardant sheet or film is 5% or less.

4 . The flame-retardant sheet or film according to claim 1 , wherein the polycarbonate resin composition further contains 1 part by mass or less of a fibril-forming fluoropolymer, relative to 100 parts by mass of the polycarbonate resin.

5 . The flame-retardant sheet or film according to claim 1 , wherein the polycarbonate resin composition further contains one or more stabilizers selected from the group consisting of antioxidants and UV absorbers.

6 . The flame-retardant sheet or film according to claim 1 , wherein the UL94 flame retardancy is VTM-0 or VTM-1.

7 . The flame-retardant sheet or film according to claim 1 , wherein the flame-retardant sheet or film is produced by extruding the polycarbonate resin composition into a sheet shape through an extruder and cooling the same with a chill roll.

8 . A battery pack case, which is configured such that the flame-retardant sheet or film according to claim 1 is processed into a box shape or a pocket shape to hold batteries therein.

9 . The battery pack case according to claim 8 , wherein the flame-retardant sheet or film is stacked in two layers and processed into a pouch-like pocket shape by heat sealing or ultrasonic welding along the four sides to thereby allow batteries to be held therein.

10 . The battery pack case according to claim 8 , wherein the flame-retardant sheet or film is folded and processed into a pouch-like pocket shape by heat sealing or ultrasonic welding along the three sides to thereby allow batteries to be held therein.

11 . The battery pack case according to claim 8 , wherein the flame-retardant film is rolled into a cylindrical shape and sealed at the top and bottom ends with injection-molded lid members each consisting of the flame-retardant polycarbonate resin composition to thereby allow batteries to be held therein.

12 . The battery pack case according to claim 8 , wherein the flame-retardant film is processed into a box shape by being subjected to film insert molding to form a frame consisting of the flame-retardant polycarbonate resin composition around the edges of the flame-retardant film to thereby allow batteries to be held therein.

13 . A battery pack, which comprises the battery pack case according to claim 8 and batteries held therein.

Assignees

• Mitsubishi Gas Chemical Co
• Mgc Filsheet Co Ltd

Inventors

• ZOUTA Keiichi
• Nakao Kimitaka
• Takagi Yuko
• Ishii Hiroki

Classifications

• C08J5/18 Primary

  Manufacture of films or sheets · CPC title

• C08K5/5399

  Phosphorus bound to nitrogen · CPC title

• C08K5/103

  with polyalcohols · CPC title

• C08J2369/00

  Characterised by the use of polycarbonates; Derivatives of polycarbonates · CPC title

• C08J2427/18

  Homopolymers or copolymers of tetrafluoroethylene · CPC title