Method of coating the surface of a metal substrate

Patent metadata

Field	Value
Publication number	US-2016102406-A1
Application number	US-201514879242-A
Country	US
Kind code	A1
Filing date	Oct 9, 2015
Priority date	Oct 10, 2014
Publication date	Apr 14, 2016
Grant date	—

Abstract

A method of coating the surface of a metal substrate includes a) applying a first composition on the surface of a metal substrate, the first composition being a solution comprising a liquid medium including sol-gel precursors of alcoxysilane type or of metallo-organic type; b) subjecting the first composition to first heat treatment to form an anchor layer on the metal substrate in which the sol-gel precursors are bonded to the metal substrate, a first temperature being imposed during the first heat treatment that is sufficient to eliminate all or part of the liquid medium and to encourage the bonding of the sol-gel precursors to the metal substrate; and c) applying a second composition on the anchor layer. The second composition includes coating compounds to obtain a coating on the anchor layer by forming bonds between the sol-gel precursors and the coating compounds.

First claim

1 - 16 . (canceled)

17 . A method of coating the surface of a metal substrate, the method comprising:
a) applying a first composition on the surface of a metal substrate, the first composition being in the form of a solution comprising a liquid medium including sol-gel precursors of alcoxysilane type or of metallo-organic type, said sol-gel precursors being suitable for bonding with the metal substrate, the sol-gel precursors applied during step a) having the same chemical nature; b) subjecting the first composition to a first heat treatment so as to form an anchor layer on the metal substrate in which the sol-gel precursors are bonded to the metal substrate, a first temperature being imposed during the first heat treatment that is sufficient to eliminate all or part of the liquid medium and to encourage the bonding of the sol-gel precursors to the metal substrate, the first heat treatment being configured to avoid complete condensation among the sol-gel precursors; and c) applying a second composition on the anchor layer, the second composition including coating compounds so as to obtain a coating on the anchor layer by forming bonds between the sol-gel precursors and the coating compounds.

18 . The method according to claim 17 , wherein the sol-gel precursors are sol-gel precursors of alcoxysilane type.

19 . The method according to claim 18 , wherein each of the sol-gel precursors of alcoxysilane type has at least one ligand organic function suitable for bonding to the metal substrate, the ligand organic function including at least one of the following ligand groups: alcoxyl; amine; acryloxy; methacryloxy; dimethyl prosphate; diethyl phosphate; epoxy; vinyl; and thiol.

20 . The method according to claim 19 , wherein the ligand organic function of the sol-gel precursors of alcoxysilane type includes at least one of the following ligand groups: amine; acryloxy; and methacryloxy.

21 . The method according to claim 18 , wherein the sol-gel precursors of alcoxysilane type are methacryloxypropyltrimethoxysilane or (3-aminopropyl)-triethoxysilane.

22 . The method according to claim 17 , wherein the sol-gel precursors are sol-gel precursors of metallo-organic type.

23 . The method according to claim 22 , wherein the sol-gel precursors of metallo-organic type include iron.

24 . The method according to claim 22 , wherein each of the sol-gel precursors of metallo-organic type has at least one ligand organic function suitable for bonding to the metal substrate, the ligand organic function including at least one of the following ligand groups: alcoxyl; amine; acryloxy; methacryloxy; dimethyl prosphate; diethyl phosphate; epoxy; and vinyl.

25 . The method according to claim 24 , wherein the sol-gel precursors of metallo-organic type are iron propionate or iron butyrate.

26 . The method according to claim 17 , wherein the coating compounds are selected from the following compounds:
(methacryloxymethyl)methyldimethoxysilane; (methacryloxymethyl)methyldiethoxysilane; (methacryloxymethyl)dimethylmethoxysilane; diethylphosphatoethylmethyldiethoxysilane; 3-aminopropyltriethoxy silane; methacryloxypropyltriisopropoxysilane; m-aminophenyltrimethoxysilane; 3-(acryloxypropyl)tris(trimethylsiloxy)silane; methacryloxypropyltriethoxysilane; N-(2-aminoethyl)-3-aminopropyltrimethoxysilane; 2-(acryloxyethoxy)trimethylsilane; 3-methacryloxypropyltrimethoxysilane; acetoxypropyltrimethoxysilane; p-aminophenyltrimethoxysilane; 3-(acryloxypropyl)trimethoxysilane; diethylphosphatoethyltriethoxysilane; 3-(acryloxypropyl)trichlorosilane; 3-mercaptopropyltriethoxysilane; 3-(acryloxypropyl)methyldichlorosilane; 3-aminopropylmethyldiethoxysilane; 3-mercaptopropyltrimethoxysilane; carboxyethylsilanetriol in sodium salt form; 3-mercaptopropylmethyldimethoxysilane; 4-aminobutyltriethoxysilane; methacryloxyethoxytrimethylsilane and; mixtures thereof.

27 . The method according to claim 17 , wherein the coating compounds and/or the sol-gel precursors include —OH groups prior to step c).

28 . The method according to claim 17 , wherein the sol-gel precursors applied during step a) are in at least partially hydrolyzed form.

29 . The method according to claim 17 , wherein second heat treatment is performed after applying the second composition on the anchor layer.

30 . The method according to claim 17 , wherein the metal substrate includes aluminum.

31 . The method according to claim 17 , wherein the coating that is obtained constitutes a layer of paint or wherein the coating is obtained by a sol-gel method.

32 . The method according to claim 17 , wherein no step of pickling the surface of the metal substrate is performed before step a).

Assignees

• Messier Bugatti Dowty
• Rbnano

Inventors

• Esteban Julien
• Mafouana Rodrigue Roland
• Rehspringer Jean-Luc

Classifications

• C23C18/1283

  Control of temperature, e.g. gradual temperature increase, modulation of temperature · CPC title

• C23C18/1225

  Deposition of multilayers of inorganic material · CPC title

• C23C18/1254

  Sol or sol-gel processing · CPC title

• C23C18/1216

  Metal oxides (C23C18/1212 takes precedence) · CPC title

• C09D5/1675

  Polyorganosiloxane-containing compositions · CPC title