Chloroprene rubber composition and adhesive composition using said chloroprene rubber composition

Patent metadata

Field	Value
Publication number	US-2016017130-A1
Application number	US-201314377779-A
Country	US
Kind code	A1
Filing date	Feb 7, 2013
Priority date	Feb 13, 2012
Publication date	Jan 21, 2016
Grant date	—

Abstract

An object of the invention is to provide a chloroprene polymer composition resistant to discoloration under heat or light. Provided is a chloroprene rubber composition, prepared by carrying out emulsion polymerization in the presence of 0.5 to 7.0 parts by mass of a rosin acid salt as emulsifier and terminating the emulsion polymerization by addition of a polymerization inhibitor and a phosphorus- or phenol-based compound as antioxidant. It is possible according to the invention to obtain a chloroprene polymer composition superior in discoloration resistance under heat or light. The chloroprene polymer composition according to the present invention can be used favorably for adhesion of cloths, leathers, foamed sheets, papers, woods, shoe parts, and others.

First claim

1 . A chloroprene rubber composition, prepared by carrying out emulsion polymerization of a total 100 parts by mass of monomers at least containing chloroprene in the presence of 0.5 to 7.0 parts by mass of a rosin acid salt as emulsifier and terminating the emulsion polymerization by addition of a polymerization inhibitor and a phosphorus- or phenol-based compound as antioxidant.

2 . The chloroprene rubber composition according to claim 1 , wherein the phosphorus-based compound is at least one phosphorus-based compound selected from 2,2′-methylenebis(4,6-di-butylphenyl)octyl phosphite, 3,9-bis(2,6-di-tert-butyl-4-methylphenoxy)-2,4,8,10-tetraoxa-3,9-diphosphaspiro[5.5]undecane, tris(2,4-di-tertbutylphenyl)phosphite, bis(2,4-di-t-butylphenyl)pentaerythritol diphosphite, and 6-[3-(3-t-butyl-hydroxy-5-methylphenyl)propoxy]-2,4,8,10-tetra-t-butylbenzo[d, f][1,3,2]-dioxaphosphepin.

3 . The chloroprene rubber composition according to claim 1 , wherein the phenol-based compound is at least one phenol-based compound selected from 2,2′-methylenebis(4-ethyl-6 tert-butylphenol), 2,2′-methylenebis(4-methyl-6 tert-butylphenol), pentaerythritol tetrakis[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate)], octadecyl 3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate), ethylenebis(oxyethylene)bis[3-(3,5-t-butyl-4-hydroxy-m-tolylpropionate)], and 2-methyl-4,6-bisoctylthiomethyl-phenol.

4 . The chloroprene rubber composition according to claim 1 , wherein the phenol- and phosphorus-based compounds are used in combination as the antioxidants added to terminate the emulsion polymerization.

5 . The chloroprene rubber composition according to claim 4 , wherein the content ratio of the phenol- and phosphorus-based compounds, phenol-based compound:phosphorus-based compound, is 0.5 to 5:1.

6 . The chloroprene rubber composition according to claim 1 , wherein a surfactant having two kinds of hydrophilic anion groups is used as dispersant during the emulsion polymerization.

7 . The chloroprene rubber composition according to claim 6 , wherein the surfactant is an alkyl sulfosuccinic acid salt and/or a sulfated fatty acid salt.

8 . The chloroprene rubber composition according to claim 1 , wherein a water-soluble initiator is used during the emulsion polymerization.

9 . The chloroprene rubber composition according to claim 8 , wherein at least one promoter selected from sodium sulfite, potassium sulfite, sodium bisulfite, formamidinesulfinic acid, potassium pyrosulfite, and sodium hydrosulfite is used during the emulsion polymerization.

10 . The chloroprene rubber composition according to claim 1 , wherein the rosin acid salt has a Gardner color scale of 4 or less.

11 . The chloroprene rubber composition according to claim 1 , wherein the rosin acid salt has a Hazen scale of 200 or less.

12 . The chloroprene rubber composition according to claim 1 , further comprising a benzotriazole-based ultraviolet absorbent as ultraviolet absorbent.

13 . The chloroprene rubber composition according to claim 1 , further comprising a hindered amine-based photostabilizer as photostabilizer.

14 . The chloroprene rubber composition according to claim 1 , wherein the chloroprene rubber is a graft polymer of 2-chloro-1,3-butadiene and an acrylic monomer.

15 . The chloroprene rubber composition according to claim 14 , wherein the acrylic monomer is methyl methacrylate.

16 . An adhesive composition, at least comprising the chloroprene rubber composition according to claim 1 and an organic solvent.

Assignees

• Denki Kagaku Kogyo Kk

Inventors

• Yashima Hiroyuki
• KISHI Sachiyo
• Otsuka Kunihiko
• Ishigaki Yuhei

Classifications

• C08F36/18 Primary

  containing chlorine · CPC title

• C09J111/02

  Latex · CPC title

• C08L93/04

  Rosin · CPC title

• C09J151/04

  grafted on to rubbers · CPC title

• C08L11/02

  Latex · CPC title