Rubber Composition for Tires, and Pneumatic Tire Using Same

Patent metadata

Field	Value
Publication number	US-2016002371-A1
Application number	US-201414770458-A
Country	US
Kind code	A1
Filing date	Feb 25, 2014
Priority date	Feb 25, 2013
Publication date	Jan 7, 2016
Grant date	—

Abstract

Provided is a rubber composition for a tire, comprising: diene rubber contained in a quantity of 100 parts by mass; silica contained in a quantity of 60 to 200 parts by mass; polysiloxanes represented by the average composition formula of Formula (1): (A) a (B) b (C) c (D) d (R 1 ) e SiO (4-2a-b-c-d-e)/2 contained in a quantity from 1 to 20 mass % relative to the quantity of silica; and a thiuram disulfide vulcanization accelerator contained in a quantity from 0.05 to 3.0 parts by mass.

First claim

1 . A rubber composition for a tire, comprising:
silica contained in a quantity from 60 to 200 parts by mass per 100 parts by mass of diene rubber; a polysiloxane represented by Formula (1) as a sulfur-containing silane coupling agent, contained in a quantity from 1 to 20 mass % relative to the content of silica; and a thiuram disulfide vulcanization accelerator represented by Formula (I), contained in a quantity from 0.05 to 3.0 parts by mass;
(A) a (B) b (C) c (D) d (R 1 ) e SiO (4-2a-b-c-d-e)/2   (1)

Formula (1) is an average composition formula, and in Formula (1), A is a divalent organic group containing a sulfide group; B is a monovalent hydrocarbon group having from 5 to 10 carbon atoms; C is a hydrolyzable group; D is an organic group containing a mercapto group; R 1 is a monovalent hydrocarbon group having from 1 to 4 carbon atoms; and a to e satisfy the relational expressions 0≦a<1, 0≦b<1, 0<c<3, 0<d<1, 0≦e<2, and 0<2a+b+c+d+e<4; however, one of either a or b is not 0;

in Formula (I), R 5 , R 6 , R 7 , and R 8 are, each independently, a hydrocarbon group having from 2 to 18 carbon atoms.

2 . The rubber composition for a tire according to claim 1 , further comprising from 0.1 to 3.0 parts by mass of guanidine vulcanization accelerator per 100 parts by mass of the diene rubber, the amount of the thiuram disulfide vulcanization accelerator being from 0.05 to 2.0 parts by mass per 100 parts by mass of the diene rubber.

3 . The rubber composition for a tire according to claim 1 , further comprising a terpene resin.

4 . The rubber composition for a tire according to claim 3 , wherein the amount of the terpene resin is from 1 to 30 parts by mass per 100 parts by mass of the diene rubber, and the terpene resin is an aromatic modified terpene resin having a softening point from 60 to 150° C.

5 . The rubber composition for a tire according to claim 1 , wherein b in Formula (1) is greater than 0.

6 . A pneumatic tire having tire treads formed using the rubber composition for a tire described in claim 1 .

7 . The rubber composition for a tire according to claim 2 , further comprising a terpene resin.

8 . The rubber composition for a tire according to claim 7 , wherein the amount of the terpene resin is from 1 to 30 parts by mass per 100 parts by mass of the diene rubber, and the terpene resin is an aromatic modified terpene resin having a softening point from 60 to 150° C.

9 . The rubber composition for a tire according to claim 2 , wherein b in Formula (1) is greater than 0.

Assignees

• Yokohama Rubber Co Ltd

Inventors

• Sato Masaki
• Mihara Satoshi

Classifications

• C08L21/00 Primary

  Compositions of unspecified rubbers · CPC title

• C08F36/04 Primary

  conjugated · CPC title

• C08L9/00

  Compositions of homopolymers or copolymers of conjugated diene hydrocarbons · CPC title

• C08K5/548

  containing sulfur {(C08K5/5477 takes precedence)} · CPC title

• C08K5/40

  Thiurams, {i.e. compounds containing[IMAGE cpc-sch-C08K-1011.gif] groups} · CPC title