Process for manufacturing cold-rolled and annealed steel sheet with a very high strength, and sheet thus produced

Patent metadata

Field	Value
Publication number	US-12590347-B2
Application number	US-202217575300-A
Country	US
Kind code	B2
Filing date	Jan 13, 2022
Priority date	May 11, 2007
Publication date	Mar 31, 2026
Grant date	Mar 31, 2026

Abstract

The present invention provides a cold-rolled and annealed steel sheet with a strength greater than 1200 MPa, the composition of which includes, the contents being expressed by weight: 0.10%≤C≤0.255, 1%≤Mn≤3%, A≥0.010%, Si≤2.990%, S≤0.015%, P≤0.1% s, N≤0.008%, it being understood that 1%≤Si+Al≤3%, it being understood that Cr+3Mo≥0.3%, Ti in an amount such that Ti/N≥4 and Ti≤0.040%. A balance of the composition includes iron and inevitable impurities resulting from the smelting. The microstructure of the steel includes 15 to 90% bainite, the remainder includes martensite and residual austenite.

First claim

What is claimed is:

1 . A cold-rolled steel sheet with a strength greater than 1200 MPa with an elongation at break greater than 8%, a composition of steel, by weight, comprising:
0.10%≤C≤0.25% 1%≤Mn≤3% Al≥0.010% 1.2%≤Si≤1.8% S≤0.015% P≤0.1% N≤0.008%, it being understood that 1.2%≤Si+Al≤3%, Mo≤0.25% Cr≤1.65%, it being understood that Cr+3Mo≥0.3%, and B=0% the composition optionally comprising: 0.05%≤V≤0.15% Ti in an amount so that Ti/N≥4 and Ti≤0.040%,
a balance of the composition consisting of iron and inevitable impurities resulting from processing,
a microstructure of the steel comprising 65 to 90% bainite, the remainder consisting of islands of martensite and residual austenite.

2 . The steel sheet as recited in claim 1 wherein the composition of the steel includes by weight:
0.19%≤C≤0.23%.

3 . The steel sheet as recited in claim 1 wherein the composition of the steel includes by weight:
1.5%≤Mn≤2.5%.

4 . The steel sheet as recited in claim 1 wherein the composition of the steel includes by weight:
1.2% Al≤1.8%.

5 . The steel sheet as recited in claim 1 wherein the composition of the steel includes by weight:
0.05%≤V≤0.15%
0.004≤N≤0.008%.

6 . The steel sheet as recited in claim 1 wherein the composition of the steel includes, by weight: 0.12%≤V≤0.15%.

7 . The steel sheet as recited in claim 1 wherein the average size of the islands of martensite and residual austenite is less than 1 micron, and the average distance between the islands is less than 6 microns.

8 . A cold-rolled steel sheet with a strength greater than 1400 MPa with an elongation at break greater than 8%, with a composition of steel, by weight, comprising:
0.10%≤C≤0.25% 1%≤Mn≤3% Al≥0.010% 1.2%≤Si≤1.8% S≤0.015% P≤0.1% N≤0.008%, it being understood that 1.2%≤Si+Al≤3%, Mo≤0.25%, and Cr≤1.65%, it being understood that Cr+3Mo≥0.3%, the composition optionally comprising: 0.05%≤V≤0.15% B≤0.005% Ti in an amount so that Ti/N≥4 and Ti≤0.040%, a balance of the composition consisting of iron and inevitable impurities resulting from processing, a microstructure of the steel comprising 45 to 65% bainite, the remainder consisting of islands of martensite and residual austenite.

9 . The steel sheet as recited in claim 8 wherein the composition of the steel includes by weight:
0.19%≤C≤0.23%.

10 . The steel sheet as recited in claim 8 wherein the composition of the steel includes by weight:
1.5%≤Mn≤2.5%.

11 . The steel sheet as recited in claim 8 wherein the composition of the steel includes by weight:
1.2% Al≤1.8%.

12 . The steel sheet as recited in claim 8 wherein the composition of the steel includes by weight:
0.05%≤V≤0.15%
0.004≤N≤0.008%.

13 . The steel sheet as recited in claim 8 wherein the composition of the steel includes by weight: 0.12%≤V≤0, 15%.

14 . The steel sheet as recited in claim 8 wherein the average size of the islands of martensite and residual austenite is less than 1 micron, and the average distance between the islands is less than 6 microns.

15 . A cold-rolled steel sheet with a strength greater than 1600 MPa with an elongation at break greater than 8%, with a composition of steel, by weight, comprising:
0.10%≤C≤0.25% 1%≤Mn≤3% Al≥0.010% 1.2%≤Si≤1.8% S≤0.015% P≤0.1% N≤0.008%, it being understood that 1.2%≤Si+Al≤3%, Mo≤0.25% Cr≤1.65%, it being understood that Cr+3Mo≥0.3%, and 0.0005≤B≤0.005% the composition optionally comprising: 0.05%≤V≤0.15% and Ti in an amount so that Ti/N≥4 and Ti≤0.040%, a balance of the composition consisting of iron and inevitable impurities resulting from processing, a microstructure of the steel comprising 15 to 45% bainite, the remainder consisting of martensite and residual austenite.

16 . The steel sheet as recited in claim 15 wherein the composition of the steel includes by weight:
0.19%≤C≤0.23%.

17 . The steel sheet as recited in claim 15 wherein the composition of the steel includes by weight:
1.5%≤Mn≤2.5%.

18 . The steel sheet as recited in claim 15 wherein the composition of the steel includes by weight:
1.2% Al≤1.8%.

19 . The steel sheet as recited in claim 15 wherein the composition of the steel includes by weight:
0.05%≤V≤0.15%
0.004≤N≤0.008%.

20 . The steel sheet as recited in claim 15 wherein the composition of the steel includes by weight: 0.12%≤V≤0.15%.

21 . The steel sheet as recited in claim 15 wherein the martensite and residual austenite are in the form of islands and the average size of the islands of martensite and residual austenite is less than 1 micron, and the average distance between the islands is less than 6 microns.

Assignees

• Arcelormittal

Inventors

• Gil Otin Javier
• Moulin Antoine

Classifications

• C23G1/00

  Cleaning or pickling metallic material with solutions or molten salts (with organic solvents C23G5/02) · CPC title

• C22C38/38

  with more than 1.5% by weight of manganese · CPC title

• C22C38/32

  with boron · CPC title

• C22C38/28

  with titanium or zirconium · CPC title

• C22C38/22

  with molybdenum or tungsten · CPC title