Recycling method of ternary material micropowder, and use thereof

Patent metadata

Field	Value
Publication number	US-12586789-B2
Application number	US-202318229213-A
Country	US
Kind code	B2
Filing date	Aug 2, 2023
Priority date	Sep 30, 2021
Publication date	Mar 24, 2026
Grant date	Mar 24, 2026

Abstract

The present disclosure discloses a recycling method of a ternary material micropowder, and use thereof. The recycling method includes: washing the ternary material micropowder with water, and adding a coating agent and an promotor; subjecting a resulting mixture to a reaction under heating and pressurization, and filtering to obtain a coated base material; subjecting the coated base material to sintering, adding an extracting agent to a resulting sintered material, and stirring and filtering to obtain a filter residue; and subjecting the filter residue to drying, sieving, and iron removal to obtain a ternary cathode material. In the present disclosure, the coating agent and the promotor are added to achieve high-pressure hydrothermal coating for the micropowder. The coating agent can optimize the storage performance of the material and increase the life of the material.

First claim

The invention claimed is:

1 . A recycling method of a ternary material micropowder, comprising the following steps:
S1: mixing a ternary material micropowder with water, stirring a resulting mixture for a specified time to obtain a first slurry, and dewatering the first slurry to obtain a micropowder filter cake; the ternary material is Li(Ni 0.8 Co 0.1 Mn 0.1 )O 2 or Li(Ni 0.5 Co 0.2 Mn 0.3 )O 2 ; S2: adding water to the micropowder filter cake, and stirring a resulting mixture during which a coating agent and a promotor are added to obtain a second slurry, wherein the promotor is one or more selected from the group consisting of polyimide, polyoxyethylene, polyethyleneimine, polypyrrole, tripolycyanamide, ethylene glycol, triethylamine, polyphenylene ether ketone, and polythiophene; S3: subjecting the second slurry to a reaction under heating and pressurization, and filtering to obtain a coated base material; and S4: subjecting the coated base material to sintering; adding an extracting agent to a resulting sintered material, the extracting agent is one or more selected from the group consisting of ethylene glycol, sec-butyl acetate, kerosene, trioctyl tertiary amine, ethyl acetate, glycerin, N-methylpyrrolidone, and benzene; and stirring and filtering to obtain a filter residue; and subjecting the filter residue to drying, sieving, and iron removal to obtain a ternary cathode material.

2 . The method according to claim 1 , wherein in S1, the ternary material micropowder has a particle size of Dv50<3.0 μm; and a liquid-to-solid ratio of the water to the ternary material micropowder is 0.4 to 1.2 L/kg.

3 . The method according to claim 1 , wherein in S1, the stirring is conducted at a rotational speed of 100 rpm to 600 rpm; and the stirring is conducted for 5 min to 30 min.

4 . The method according to claim 1 , wherein in S1, the micropowder filter cake has a moisture content of 5% to 16%.

5 . The method according to claim 1 , wherein in S2, the coating agent is one or more selected from the group consisting of TiO 2 , AL 2 O 3 , ZrO 2 , MgO, SnO 2 , WO 3 , AL(OH) 3 , Li 3 PO 4 , CeO, Li 4 TiO 4 , and In 2 O 3 ; and an amount of the coating agent added is 0.1% to 0.9% of a mass of the ternary material micropowder.

6 . The method according to claim 1 , wherein in S2, an amount of the promotor added is 0.2% to 1.2% of a mass of the ternary material micropowder.

7 . The method according to claim 1 , wherein in S3, the reaction is conducted at 100° C. to 200° C.; the reaction is conducted at 1 MPa to 10 MPa; and the reaction is conducted for 5 h to 10 h.

8 . The method according to claim 1 , wherein in S4, the sintering is conducted with a rotary kiln in an oxygen atmosphere; the sintering is conducted at 300° C. to 900° C.; and the sintering is conducted for 3 h to 10 h.

Assignees

• Guangdong Brunp Recycling Technology Co Ltd
• Hunan Brunp Recycling Tech Co Ltd
• Hunan Brunp Ev Recycling Co Ltd

Inventors

• Wang Quele
• Li Changdong
• Ruan Dingshan
• Liu Weijian
• Cai Yong

Classifications

• H01M6/52

  Reclaiming serviceable parts of waste cells or batteries {, e.g. recycling} · CPC title

• H01M2004/028

  Positive electrodes · CPC title

• H01M10/0525

  Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries · CPC title

• H01M4/366

  as layered products · CPC title

• C01P2006/82

  water content · CPC title