Crosslinked polyolefin separator and manufacturing method therefor

Patent metadata

Field	Value
Publication number	US-12583988-B2
Application number	US-202318209275-A
Country	US
Kind code	B2
Filing date	Jun 13, 2023
Priority date	Jul 26, 2018
Publication date	Mar 24, 2026
Grant date	Mar 24, 2026

Abstract

A crosslinked polyolefin separator which has gels with a longer side length of 50 μm or more in a number ranging from 0 to 3 per 1 m 2 of the separator, and shows a standard deviation of absorbance ratio between the center of the separator and the side thereof ranging from 0.01 to 0.5 is provided. A method for manufacturing the crosslinked polyolefin separator is also provided. The method includes (S 1 ) preparing a polyolefin porous membrane, and (S 2 ) applying a coating solution containing an initiator and alkoxy group-containing vinylsilane onto at least one surface of the porous membrane. The coating solution can permeate even to the inside of exposed pores. Thus, it is possible to provide a crosslinked polyolefin separator in which silane crosslinking occurs uniformly even inside of the pores.

First claim

What is claimed is:

1 . A method for manufacturing a crosslinked polyolefin separator, comprising:
(S 1 ) preparing a polyolefin porous membrane; (S 2 ) applying a coating solution containing an initiator and alkoxy group-containing vinylsilane onto at least one surface of the porous membrane; (S 3 ) drying and thermally fixing the porous membrane coated with the coating solution; and (S 4 ) crosslinking the thermally fixed porous membrane in the presence of water.

2 . The method according to claim 1 , wherein (S 1 ) comprises:
introducing and mixing polyolefin and a diluting agent to an extruder and carrying out extrusion to prepare a polyolefin composition; molding and orienting the extruded polyolefin composition in a form of a sheet; and extracting the diluting agent from the oriented sheet to obtain the porous membrane.

3 . The method according to claim 1 , wherein silane grafting occurs simultaneously in the porous membrane, in the thermal fixing (S 3 ).

4 . The method according to claim 1 , wherein the alkoxy group-containing vinylsilane comprises trimethoxyvinylsilane, triethoxyvinylsilane, triacetoxyvinylsilane, or a mixture of two or more of them.

5 . The method according to claim 1 , wherein the thermal fixing is carried out at a temperature of 110-145° C.

6 . The method according to claim 1 , wherein the thermal fixing is carried out at a temperature of 110-145° C., and the alkoxy group-containing vinylsilane comprises two types of alkoxy group-containing vinylsilane having different boiling points.

7 . The method according to claim 1 , wherein the alkoxy group-containing vinylsilane is a mixture of trimethoxyvinylsilane with triethoxyvinylsilane, and the weight ratio of the trimethoxyvinylsilane to triethoxyvinylsilane is 90:10-30:70.

8 . The method according to claim 1 , wherein the thermal fixing is carried out at a temperature of 110-145° C., the alkoxy group-containing vinylsilane is a mixture of trimethoxyvinylsilane with triethoxyvinylsilane, and the weight ratio of the trimethoxyvinylsilane to triethoxyvinylsilane is 90:10-30:70.

9 . The method according to claim 1 , wherein the thermal fixing step is started at a temperature lower than a boiling point of the alkoxy group-containing vinylsilane and is completed at a temperature higher than the boiling point of the alkoxy group-containing vinylsilane.

10 . The method according to claim 1 , wherein the coating solution further comprises a crosslinking catalyst.

11 . The method according to claim 10 , wherein the crosslinking catalyst comprises dibutyltin dilaurate, dibutyltin diacetate, stannous acetate, stannous caprylate, zinc naphthenate, zinc caprylate, cobalt naphthenate, ethylamine, dibutylamine, hexylamine, pyridine, sulfuric acid, hydrochloric acid, toluene, sulfonic acid, acetic acid, stearic acid, maleic acid, or a mixture of two or more of them.

12 . The method according to claim 1 , further comprising:
removing the coating solution between (S 2 ) and (S 3 ).

13 . The method according to claim 12 , wherein the removing of the coating solution is carried out by removing the surplus coating solution by pressurizing the porous membrane coated with the coating solution.

14 . The method according to claim 13 , wherein the pressurization is controlled at a linear pressure of 0.1-100 kgf/cm.

15 . The method according to claim 12 , wherein the removing of the coating solution is carried out by passing the porous membrane through a gap between a first roller and a second roller facing each other to remove the surplus coating solution.

16 . The method according to claim 15 , wherein the gap between the first roller and the second roller is +10 μm to −10 μm, and the gap, S, is defined by a formula of S=D−(R 1 +R 2 +T), wherein D represents a distance between the first roller center and the second roller center, R 1 represents a first roller radius, R 2 represents a second roller radius, and T represents a thickness of the polyolefin porous membrane.

17 . The method according to claim 12 , further comprising:
rubbing and absorbing the surplus coating solution between the removing of the coating solution and thermal fixing step (S 3 ).

18 . The method according to claim 17 , wherein the rubbing is carried out by using a rubbing roller or rubbing cloth.

19 . The method according to claim 18 , wherein the rubbing roller or rubbing cloth comprises a non-woven web, cotton, paper, liquid-absorbing sheet, or at least two absorption members of them.

Assignees

• Lg Chemical Ltd

Inventors

• Lee Joo-Sung
• Ryu Bi-Oh
• Bae Won-Sik
• Lee A-Young
• Song Heon-Sik

Classifications

• H01M50/406

  Moulding; Embossing; Cutting · CPC title

• H01M50/489

  Separators, membranes, diaphragms or spacing elements inside the cells, characterised by their physical properties, e.g. swelling degree, hydrophilicity or shut down properties · CPC title

• H01M50/417 Primary

  Polyolefins · CPC title

• H01M50/403

  Manufacturing processes of separators, membranes or diaphragms · CPC title

• C08J2323/06

  Polyethene · CPC title