Mash filter membrane

Patent metadata

Field	Value
Publication number	US-12570937-B2
Application number	US-201917261619-A
Country	US
Kind code	B2
Filing date	Aug 29, 2019
Priority date	Aug 29, 2018
Publication date	Mar 10, 2026
Grant date	Mar 10, 2026

Abstract

The invention is directed to a mash filter membrane comprising an elastomeric composition that comprises more than 50 wt % of one or more elastomer, based on the total weight of polymers in the elastomeric composition.

First claim

The invention claimed is:

1 . Mash filter membrane comprising an elastomeric composition that comprises 100 wt % of copolymer ethylene propylene diene monomer (EPDM), based on a total weight of polymers in the elastomeric composition,
wherein the elastomeric composition is a food grade composition, wherein the elastomeric composition, before use of said membrane, has a Shore A hardness determined according to UNI ISO 7619-1, in the range of 60 to 71 ShA.

2 . Mash filter membrane in accordance with claim 1 , having a compression set determined after 72 hours at 70° C. according to ISO 815-1:2014, method A, test piece B, of less than 35%, wherein the compression set is determined before use of said membrane.

3 . Mash filter membrane in accordance with claim 1 , having a compression set determined after 72 hours at 70° C. according to ISO 815-1:2014, method A, test piece B, of less than 50% wherein the compression set is determined after 4700 brews or 90 weeks of using said membrane.

4 . Mash filter membrane in accordance with claim 1 , wherein the elastomeric composition, before use of said membrane, has one or more, of the following material properties:
a tensile strength determined according to ISO 37:2011, type 2, of more than 5 MPa; a modulus M300 deformation determined according to ISO 37:2011, type 2, of more than 4 MPa; an elongation at break determined according to ISO 37:2011, type 2, of more than 200%; a density determined according to UNI EN ISO 1183-1, of more than 1 g/cm 3 a Shore A hardness determined according to UNI ISO 7619-1, in the range of 60 to 75 ShA.

5 . Mash filter membrane in accordance with claim 1 , wherein the elastomeric composition is a food grade composition according to EU Directive 95/2001/EC on general product safety, Regulation (EC) N. 1935/2004 on materials and articles intended to come into contact with food, EU Regulation 2023/2006 on good manufacturing practice for materials and articles intended to come into contact with food, Dutch Food and consumer items law (including but not limited to the (Commodities Act) decree and regulation on packaging and consumer items (“Warenwetbesluit en-regeling verpakkingen en gebruiksartikelen”), article 33 of EU Regulation (EC) 1907/2006 such that no substances of very high concern as defined by the REACH legislation are present above 0.1% by weight, and/or according to Food and Drug Administration (FDA) CFR Title 21—Part 177—Indirect Food Additives: Polymers § 177.2600 Rubber articles intended for repeated use.

6 . Mash filter membrane in accordance with claim 1 , having a one-sided surface area of more than 1 m 2 .

7 . Mash filter membrane in accordance with claim 1 , wherein the elastomeric composition is cured or crosslinked by peroxide.

8 . Mash filtration unit comprising the mash filter membrane in accordance with claim 1 .

9 . Mash filter membrane in accordance with claim 1 , having a compression set determined after 72 hours at 70° C. according to ISO 815-1:2014, method A, test piece B, of less than 25% wherein the compression set is determined before use of said membrane.

10 . Mash filter membrane in accordance with claim 1 , having a compression set determined after 72 hours at 70° C. according to ISO 815-1:2014, method A, test piece B, of less than 25% wherein the compression set is determined after 4700 brews or 90 weeks of using said membrane.

11 . Mash filter membrane in accordance with claim 1 , having a compression set determined after 72 hours at 70° C. according to ISO 815-1:2014, method A, test piece B, of less than 20% wherein the compression set is determined after 4700 brews or 90 weeks of using said membrane.

12 . Mash filter membrane in accordance with claim 1 , wherein the elastomeric composition, before use of said membrane, has one or more of the following material properties:
a tensile strength determined according to ISO 37:2011, type 2, of more than 8 MPa; a modulus M300 deformation determined according to ISO 37:2011, type 2, of more than 4 MPa; an elongation at break determined according to ISO 37:2011, type 2, of more than 300; a density determined according to UNI EN ISO 1183-1, of more than 1 g/cm 3 ; a Shore A hardness determined according to UNI ISO 7619-1, in the range of 65 to 71 ShA.

13 . Mash filter membrane in accordance with claim 1 , wherein the elastomeric composition, before use of said membrane, has one or more of the following material properties:
a tensile strength determined according to ISO 37:2011, type 2, of more than 10 MPa; a modulus M300 deformation determined according to ISO 37:2011, type 2, of more than 5 MPa; an elongation at break determined according to ISO 37:2011, type 2, of more than 400; a density determined according to UNI EN ISO 1183-1, of more than 1 g/cm 3 ; a Shore A hardness determined according to UNI ISO 7619-1, in the range of 65 to 71 ShA.

14 . Mash filter membrane in accordance with claim 1 , wherein the elastomeric composition, before use of said membrane, has one or more of the following material properties:
a tensile strength determined according to ISO 37:2011, type 2, of about 12 MPa; a modulus M300 deformation determined according to ISO 37:2011, type 2, of about 8.6 MPa; an elongation at break determined according to ISO 37:2011, type 2, of about 420; a density determined according to UNI EN ISO 1183-1, of about 1.06 g/cm 3 ; a Shore A hardness determined according to UNI ISO 7619-1, of about 66 ShA.

15 . Mash filter membrane in accordance with claim 1 , having a one-sided surface area of more than 2 m 2 .

16 . Mash filter membrane in accordance with claim 1 , having a one-sided surface area of more than 3 m 2 .

17 . Mash filter membrane in accordance with claim 1 , having a one-sided surface area of about 3.6 m 2 .

18 . Mash filter membrane in accordance with claim 1 , further comprising one or more of a filler, a curing agent, a stabilizer or a plasticizer.

Assignees

• Heineken Supply Chain Bv

Inventors

• Van Nuus Martinus Adrianus

Classifications

• B01D2325/24

  Mechanical properties, e.g. strength · CPC title

• B01D2323/30

  Cross-linking · CPC title

• B01D71/80 Primary

  Block polymers · CPC title

• B01D71/24

  Rubbers · CPC title

• B01D69/02

  characterised by their properties · CPC title