Lithium secondary battery

Patent metadata

Field	Value
Publication number	US-12542271-B2
Application number	US-201816757893-A
Country	US
Kind code	B2
Filing date	Nov 6, 2018
Priority date	Nov 6, 2017
Publication date	Feb 3, 2026
Grant date	Feb 3, 2026

Abstract

A lithium secondary battery includes a positive electrode including a lithium manganese-based first positive electrode active material having a spinel structure doped and coated and a lithium nickel-manganese-cobalt-based second positive active material, a negative electrode including artificial graphite having a specific surface area (BET) of 0.1-1.2 m 2 /g and at least one selected from the group consisting of soft carbon and natural graphite which have a greater specific surface area than the artificial graphite, a separator interposed between the positive electrode and the negative electrode, and an electrolyte.

First claim

The invention claimed is:

1 . A lithium secondary battery comprising:
a positive electrode including
a lithium manganese-based first positive electrode active material having a spinel structure, and
a lithium nickel-manganese-cobalt-based second positive active material;
a negative electrode including artificial graphite having a specific surface area (BET) of 0.1 m 2 /g to 1.2 m 2 /g and at least one selected from the group consisting of soft carbon and natural graphite, wherein the at least one selected from the group consisting of soft carbon and the natural graphite have a greater specific surface area than the artificial graphite; a separator interposed between the positive electrode and the negative electrode; and an electrolyte, wherein the first positive electrode active material includes a lithium manganese oxide represented by Formula 1 below, and a coating layer positioned on the surface of the lithium manganese oxide and including one or more elements selected from the group consisting of Al, Ti, Zn, W, and B, wherein the second positive electrode active material is a lithium nickel-manganese-cobalt oxide having a nickel molar ratio of 0.5 or more and less than 1.0:
Li 1+a Mn 2−b M 1 b O 4−c A c   [Formula 1]

wherein, in Formula 1, M 1 is one or more doping elements selected from the group consisting of Al, Li, Mg, and Zn and A is one or more elements selected from the group consisting of F, Cl, Br, I, At, and S, and 0≤a≤0.2, 0<b≤0.5, and 0≤c≤0.1.

2 . The lithium secondary battery of claim 1 , wherein the lithium nickel-manganese-cobalt oxide is represented by Formula 2 below:
Li 1+x [Ni y CO 2 Mn w M 2 v ]O 2-p X p   [Formula 2]
wherein, in Formula 2, M 2 is one or more selected from the group consisting of W, Cu, Fe, V, Cr, Ti, Zr, Zn, Al, In, Ta, Y, In, La, Sr, Ga, Sc, Gd, Sm, Ca, Ce, Nb, Mg, B, and Mo; X is one or more elements selected from the group consisting of F, Cl, Br, I, At, and S; and 0≤x≤0.3, 0.50≤y<1, 0<z<0.35, 0<w<0.35, 0≤v≤0.1, and 0≤p≤0.1.

3 . The lithium secondary battery of claim 1 , wherein the first positive electrode active material and the second positive electrode active material are included at a weight ratio of 10:90 to 90:10.

4 . The lithium secondary battery of claim 1 , wherein the positive electrode comprises a positive electrode active material having a bimodal particle diameter distribution including large diameter particles and small diameter particles having different average particle diameters (D 50 ).

5 . The lithium secondary battery of claim 4 , wherein the first positive electrode active material is the small diameter particles and the second positive electrode active material is the large diameter particles.

6 . The lithium secondary battery of claim 1 , wherein the positive electrode comprises a positive electrode current collector, a first positive electrode active material layer formed on the positive electrode current collector and a second positive electrode active material layer formed on the first positive electrode active material layer.

7 . The lithium secondary battery of claim 6 , wherein the first positive electrode active material and the second positive electrode active material are included in different layers.

8 . The lithium secondary battery of claim 6 , wherein the first positive electrode active material layer and the second positive electrode active material layer have different compositions.

9 . The lithium secondary battery of claim 6 , wherein
the first positive electrode active material layer comprises the first positive electrode active material in an amount of 50 wt % to 100 wt % based on the total positive electrode active materials included in a first positive electrode active material layer, and the second positive electrode active material layer comprises the second positive electrode active material in an amount of 50 wt % to 100 wt % of the total positive electrode active materials included in a second positive electrode active material layer.

10 . The lithium secondary battery of claim 6 , wherein
the first positive electrode active material layer and the second positive electrode active material layer comprise a binder, and the first positive electrode active material layer includes a binder in an amount of 1 wt % to 4 wt %, and the second positive electrode active material layer includes a binder in an amount of 3 wt % or less.

11 . The lithium secondary battery of claim 1 , wherein the negative electrode comprises artificial graphite and soft carbon at a weight ratio of 50:50 to 95:5.

12 . The lithium secondary battery of claim 1 , wherein the soft carbon has a specific surface area (BET) of 7 m 2 /g to 10 m 2 /g.

13 . The lithium secondary battery of claim 1 , wherein the negative electrode comprises a negative electrode current collector, a first negative electrode active material layer formed on the negative electrode current collector and a second negative electrode active material layer formed on the first negative electrode active material layer.

Assignees

• Lg Chemical Ltd
• Lg Energy Solution Ltd

Inventors

• Suh Min Won
• Kim So Yeon
• Yun Nan Ji
• Kim Yo Jin
• Oh Sae Young
• Kim Hui Kyoung

Classifications

• H01M2004/028

  Positive electrodes · CPC title

• H01M2004/021

  Physical characteristics, e.g. porosity, surface area · CPC title

• C01P2006/40

  Electric properties · CPC title

• C01P2004/53

  bimodal size distribution · CPC title

• C01P2002/32

  spinel-type (AB2O4) · CPC title