Gas barrier film and method for producing the same

Patent metadata

Field	Value
Publication number	US-12534585-B2
Application number	US-202217899507-A
Country	US
Kind code	B2
Filing date	Aug 30, 2022
Priority date	Mar 5, 2020
Publication date	Jan 27, 2026
Grant date	Jan 27, 2026

Abstract

A gas barrier film comprising a resin base material, an oxygen barrier coating provided on at least one surface of the resin base material, and a base layer and/or an inorganic oxide layer provided between the resin base material and the oxygen barrier coating, wherein the black area ratio of one surface measured by the following measuring method is 0.15% or less: <Measuring method> An arbitrary region of 1281 μm square on one surface of a resin base material is photographed with an optical microscope to acquire a photographed image of 1024×1024 pixels, the photographed image is converted into a monochrome image of 256 gradations using an image analysis software, and the value obtained by subtracting 30 from the most frequent value of the luminance in the monochrome image is set as the threshold, the value less than the threshold is set to black, and the value not less than the threshold is set to white, thus binarizing the luminance, and the ratio of the total area of the black regions having a size of 100 μm 2 or more in the 1281 μm square region is defined as the black area ratio.

First claim

What is claimed is:

1 . A gas barrier film comprising
a resin base material, an oxygen barrier coating provided on at least one surface side of the resin base material, and one or both of a base layer and an inorganic oxide layer provided between the resin base material and the oxygen barrier coating, wherein one surface of the resin base material has a black area ratio of 0.15% or less as measured by the following measuring method <Measuring method> An arbitrary region of 1281 μm square on one surface of a resin base material is photographed with an optical microscope to acquire a photographed image of 1024×1024 pixels, the photographed image is converted into a monochrome image of 256 gradations using an image analysis software, and the value obtained by subtracting 30 from the most frequent value of the luminance in the monochrome image is set as the threshold, the value less than the threshold is set to black, and the value not less than the threshold is set to white, thus binarizing the luminance, and the ratio of the total area of the black regions having a size of 100 μm 2 or more in the 1281 μm square region is defined as the black area ratio.

2 . The gas barrier film according to claim 1 , wherein the resin base material contains an anti-blocking agent.

3 . The gas barrier film according to claim 1 , wherein the resin base material is made of one selected from polypropylene, polyethylene terephthalate, and nylon.

4 . The gas barrier film according to claim 1 , wherein the base layer has a thickness of 0.01 to 1 μm.

5 . The gas barrier film according to claim 1 , wherein the base layer contains an organic polymer as the main component, and
the organic polymer contains at least one of a polyacrylic resin, a polyol-based resin, a polyurethane-based resin, a polyamide-based resin, and a reaction product of these resins.

6 . The gas barrier film according to claim 1 , wherein the inorganic oxide layer has a thickness of 1 to 200 nm.

7 . The gas barrier film according to claim 1 , wherein the inorganic oxide layer is made of aluminum oxide or silicon oxide.

8 . The gas barrier film according to claim 1 , wherein the oxygen barrier coating has a thickness of 0.05 to 1 μm.

9 . The gas barrier film according to claim 1 , wherein the oxygen barrier coating is a coating containing at least one of a metal alkoxide, a hydrolyzate of a metal alkoxide, and a reaction product of a metal alkoxide or a hydrolyzate of a metal alkoxide, and a water-soluble polymer.

10 . The gas barrier film according to claim 9 , wherein the oxygen barrier coating contains at least one of a silane coupling agent, a hydrolyzate of a silane coupling agent, and a reaction product of a silane coupling agent or a hydrolyzate of a silane coupling agent.

11 . The gas barrier film according to claim 1 , wherein the oxygen barrier coating contains a carboxylic acid polyvalent metal salt which is a reaction product of a carboxy group of a polycarboxylic acid-based polymer (A) and a polyvalent metal compound (B).

12 . A method for producing the gas barrier film of claim 1 , comprising
measuring the black area ratio on the surface of a resin base material by the following measuring method, and preparing a resin base material having the black area ratio on at least one surface of 0.15% or less as the resin base material, and applying a coating agent to at least one surface side of the resin base material to form at least the oxygen barrier coating: <Measuring method> An arbitrary region of 1281 μm square on one surface of a resin base material is photographed with an optical microscope to acquire a photographed image of 1024×1024 pixels, the photographed image is converted into a monochrome image of 256 gradations using an image analysis software, and the value obtained by subtracting 30 from the most frequent value of the luminance in the monochrome image is set as the threshold, the value less than the threshold is set to black, and the value not less than the threshold is set to white, thus binarizing the luminance, and the ratio of the total area of the black regions having a size of 100 μm 2 or more in the 1281 μm square region is defined as the black area ratio.

13 . A gas barrier film comprising
a resin base material, an oxygen barrier coating provided on at least one surface side of the resin base material, and one or both of a base layer and an inorganic oxide layer provided between the resin base material and the oxygen barrier coating, wherein the resin base material is a polyolefin-based resin film, and one surface of the resin base material has a black area ratio of 0.15% or less as measured by the following measuring method <Measuring method> An arbitrary region of 1281 μm square on one surface of a resin base material is photographed with an optical microscope to acquire a photographed image of 1024×1024 pixels, the photographed image is converted into a monochrome image of 256 gradations using an image analysis software, and the value obtained by subtracting 30 from the most frequent value of the luminance in the monochrome image is set as the threshold, the value less than the threshold is set to black, and the value not less than the threshold is set to white, thus binarizing the luminance, and the ratio of the total area of the black regions having a size of 100 μm 2 or more in the 1281 μm square region is defined as the black area ratio.

14 . The gas barrier film according to claim 13 , wherein the resin base material contains an anti-blocking agent.

15 . The gas barrier film according to claim 13 , wherein the base layer has a thickness of 0.01 to 1 μm.

16 . The gas barrier film according to claim 13 , wherein the base layer contains an organic polymer as the main component, and
the organic polymer contains at least one of a polyacrylic resin, a polyol-based resin, a polyurethane-based resin, a polyamide-based resin, and a reaction product of these resins.

17 . The gas barrier film according to claim 13 , wherein the inorganic oxide layer has a thickness of 1 to 200 nm.

18 . The gas barrier film according to claim 13 , wherein the inorganic oxide layer is made of aluminum oxide or silicon oxide.

19 . The gas barrier film according to claim 13 , wherein the oxygen barrier coating has a thickness of 0.05 to 1 μm.

20 . The gas barrier film according to claim 13 , wherein the oxygen barrier coating is a coating containing at least one of a metal alkoxide, a hydrolyzate of a metal alkoxide, and a reaction product of a metal alkoxide or a hydrolyzate of a metal alkoxide, and a water-soluble polymer.

Assignees

• Toppan Inc

Inventors

• Kaminaga Junichi
• Takei Ryo
• Koshiyama Yoshiki
• Nishikawa Takeshi
• Fukugami Miki
• Tanaka Ayumi
• Yanagisawa Takayuki

Classifications

• C08J2483/16

  in which all the silicon atoms are connected by linkages other than oxygen atoms · CPC title

• C08J2323/12

  Polypropene · CPC title

• C09D183/16

  in which all the silicon atoms are connected by linkages other than oxygen atoms · CPC title

• C09D7/63

  organic · CPC title

• C08J7/0423

  with at least one layer of inorganic material and at least one layer of a composition containing a polymer binder · CPC title