Negative electrode for lithium secondary battery, method for manufacturing the same, and lithium secondary battery including the same

Patent metadata

Field	Value
Publication number	US-12525612-B2
Application number	US-202117912567-A
Country	US
Kind code	B2
Filing date	Jul 20, 2021
Priority date	Jul 23, 2020
Publication date	Jan 13, 2026
Grant date	Jan 13, 2026

Abstract

Disclosed is a negative electrode for a lithium secondary battery that enables the provision of a lithium secondary battery having a higher energy density and can fundamentally prevent the electrolyte decomposition reaction and the lithium dendrite formation, a method for manufacturing the same and a lithium secondary battery including the same.

First claim

The invention claimed is:

1 . A negative electrode for a lithium secondary battery, the negative electrode comprising:
a negative electrode plate comprising:
a crystalline carbon layer,
an amorphous carbon layer having a network structure on the crystalline carbon layer, and
a lithium ion or lithium carbide compound intercalated into the amorphous carbon layer, and a lithium metal electrodeposited around the lithium ion or lithium carbide compound;
a negative electrode tab protruding from the negative electrode plate and comprising a crystalline carbon layer and an amorphous carbon layer identical to those of the negative electrode plate; and a metal lead adhered to the negative electrode tab with a conductive epoxy resin, wherein the metal lead comprises an alloy of copper and nickel, and the metal lead and at least one of the carbon layers of the negative electrode tab are adhered by the conductive epoxy resin.

2 . The negative electrode for the lithium secondary battery according to claim 1 , wherein:
the amorphous carbon layer of the negative electrode plate comprises a carbon defect structure of electron-deficient carbon atoms, and nanopores ranging in diameter from of 0.5 nm to 2 nm are present in the carbon defect structure.

3 . The negative electrode for the lithium secondary battery according to claim 2 , wherein:
the amorphous carbon layer of the negative electrode plate comprises the carbon defect structure as observed in a transmission electron microscopy image, and when the amorphous carbon layer of the negative electrode plate is analyzed by X-ray photoelectron spectroscopy, a ratio of a peak intensity from the carbon defect structure divided by a peak intensity from carbon having sp 2 orbital hybridization structure is 0.3 or more.

4 . The negative electrode for the lithium secondary battery according to claim 3 , wherein:
when the amorphous carbon layer of the negative electrode plate is subjected to Raman spectrum analysis, a peak of 1500 cm −1 or less from the carbon defect structure shows an intensity equal to or greater than the peak observed at more than 1500 cm −1 and 2000 cm −1 or less.

5 . The negative electrode for the lithium secondary battery according to claim 4 , wherein:
the amorphous carbon layer of the negative electrode plate comprises a plurality of graphene layers, and the result of the Raman spectrum analysis shows an additional peak in a region of 2500 cm −1 or more from the plurality of graphene layers.

6 . The negative electrode for the lithium secondary battery according to claim 1 , wherein:
the crystalline carbon layer of the negative electrode plate comprises a plurality of carbon fibers and the crystalline carbon layer of the negative electrode plate has a thickness of 1 μm to 50 μm.

7 . The negative electrode for the lithium secondary battery according to claim 1 , wherein:
the amorphous carbon layer of the negative electrode plate has a thickness of 1 nm to 100 nm.

8 . The negative electrode for the lithium secondary battery according to claim 1 , wherein:
the lithium ion or lithium carbide compound, and the lithium metal are two-dimensionally bonded on the same plane as the amorphous carbon layer of the negative electrode plate.

9 . The negative electrode for the lithium secondary battery according to claim 2 , wherein:
lithium derived from the lithium ion or lithium carbide compound provides electrons to the electron-deficient carbon atoms, and is bonded to the carbon defect structure.

10 . The negative electrode for the lithium secondary battery according to claim 9 , wherein:
the lithium carbide compound is Li 3 C 8 .

11 . The negative electrode for the lithium secondary battery according to claim 1 , wherein:
the conductive epoxy resin comprises a curable epoxy resin and a conductive metal filler.

12 . The negative electrode for the lithium secondary battery according to claim 1 ,
further comprising a metal current collector that supports the crystalline carbon layer of the negative electrode plate.

13 . A method for manufacturing the negative electrode according to claim 1 , the method comprising:
subjecting a crystalline carbon fabric comprising plural carbon fibers to an oxygen plasma treatment to oxidize a surface of the crystalline carbon fabric to form a surface-oxidized crystalline carbon fabric; reacting the surface-oxidized crystalline carbon fabric, a nitrogen precursor and a metal precursor to form a carbon fabric coated with a metal organic framework; calcinating and carbonizing the carbon fabric coated with the metal organic framework at a temperature of 700° C. or more to form a carbonized carbon fabric; and electrochemically reacting the carbonized carbon fabric within a lithium salt-containing electrolyte, bonding the lithium ion or lithium carbide compound onto the carbonized carbon fabric and electrodepositing the lithium metal around the lithium ion or lithium carbide compound.

14 . The method for manufacturing the negative electrode according to claim 13 , wherein the metal precursor comprises at least one metal-containing compound selected from the group consisting of zinc (Zn), aluminum (Al), copper (Cu), zirconium (Zr), iron (Fe), chromium (Cr), and gadolinium (Gd).

15 . The method for manufacturing the negative electrode according to claim 13 , wherein the metal organic framework is at least one compound selected from the group consisting of Zn 2 DOT, Cu 2 (BDC-Br) 2 (H 2 O) 2 , Zn 4 O(BTB) 2 , [Fe 3 O(BDC) 3 (DMF) 3 ][FeCl 4 ]·(DMF) 3 , Al(OH)(BPYDC), Zn 4 O(BDC) 3 ·7DEF·3H 2 O, Zn 4 O(TPDC) 3 ·17DEF·2H 2 O, Zr 6 O 6 (BDC) 6 , Zr 6 O 6 (BPDC) 6 , Zr 6 O 6 (TPDC) 6 , Al(OH)(BDC), Al(OH)(BDC-NH 2 ), Fe 3 O(MeOH) 3 (O 2 CCH═CHCO2) 3 ·MeCO 2 ·nH 2 O, Fe 3 O(MeOH) 3 (O 2 C(CH 2 )2CO 2 ) 3 ·AcO·(MeOH) 4.5 , 2Fe 3 O(OH)(H 2 O) 2 (BDC-Me 2 ) 3 , Fe III 3 O(H 2 O) 2 F·(BTC) 2 ·nH 2 O, Cr 3 O(H 2 O) 2 F·(BDC) 3 ·nH2O, Cu 3 (BTC) 2 , Gd 2 (BDC-NH 2 ) 3 (DMF) 4 , Zn(MIM) 2 , Zn(FIM) 2 , Cu 2 (PZDC) 2 (4,4′-BPY), [Cu(HFBBA)(phen) 2 ](H2HFBBA) 2 (H 2 O)(HCO 2 ), and Cu 24 (m-BDC) 24 (DMF) 14 (H 2 O) 10 .

16 . A lithium secondary battery comprising:
a positive electrode comprising a positive electrode current collector and a lithium composite oxide-based positive electrode active material layer on the positive electrode current collector; the negative electrode of claim 1 ; and a separator between the positive electrode and the negative electrode; and an electrolyte.

Assignees

• Lg Energy Solution Ltd
• Korea Advanced Inst Sci & Tech

Inventors

• Yoon Jong Keon
• Hwang Sunwoo
• Hah Hoejin
• Lee Jung Pil
• Lee Ju-Hyuk
• Kim Hee-Tak
• Kwon Hyeokjin

Classifications

• H01M2004/027

  Negative electrodes · CPC title

• H01M2004/021

  Physical characteristics, e.g. porosity, surface area · CPC title

• H01M10/052

  Li-accumulators · CPC title

• H01M4/622

  being polymers · CPC title

• H01M50/534

  characterised by the material of the leads or tabs · CPC title