Asphalt composition comprising a mixture of an isocyanate and a polymer as performance additives

Patent metadata

Field	Value
Publication number	US-12509586-B2
Application number	US-201917268584-A
Country	US
Kind code	B2
Filing date	Aug 9, 2019
Priority date	Aug 15, 2018
Publication date	Dec 30, 2025
Grant date	Dec 30, 2025

Abstract

An asphalt composition comprising 0.1 to 8 wt.-% based on the total weight of the composition of an Isocyanate as thermosetting reactive compound and 0.1 to 8 wt.-% based on the total weight of the composition of a polymer selected from the group consisting of styrene/butadiene/styrene copolymer (SBS), styrene butadiene rubber (SBR), neoprene, polyethylene, low density polyethylene, oxidized high density polyethylene, polypropylene, oxidized high density polypropylene, maleated polypropylene, ethylene-butyl-acrylate-glycidyl-methacrylate terpolymer, ethyl vinyl acetate (EVA) and polyphosphoric acid (FRA).

First claim

The invention claimed is:

1 . An asphalt composition comprising 0.1 to 8 wt.-% based on the total weight of the composition of an Isocyanate, wherein the isocyanate is polymeric MDI, wherein the polymeric MDI has a viscosity in the range of from 10 to 5000 cps/mPas at 25° C., and 0.1 to 8 wt.-% based on the total weight of the composition of a polymer selected from the group consisting of styrene/butadiene/styrene copolymer (SBS), and polyphosphoric acid (PPA).

2 . The asphalt composition according to claim 1 , wherein the isocyanate has a functionality of at least 2.0.

3 . The asphalt composition according to claim 1 , wherein the amount of polymeric MDI is of from 0.5 to 5.0 wt.-% based on the total weight of the composition.

4 . The asphalt composition according to claim 1 , wherein the polymer is a styrene/butadiene/styrene copolymer (SBS).

5 . The asphalt composition according to claim 4 , wherein the styrene/butadiene/styrene copolymer (SBS) is linear.

6 . The asphalt composition according to claim 4 , wherein the styrene/butadiene/styrene copolymer (SBS) has a styrene content of from 25 to 40 wt. % based on the total weight of the polymer.

7 . The asphalt composition according to claim 4 , wherein the amount of styrene/butadiene/styrene copolymer (SBS) is of from 0.8 to 3.0 wt.-% based on the total weight of the composition.

8 . The asphalt composition according to claim 1 , wherein the polymer is polyphosphoric acid (PPA).

9 . The asphalt composition according to claim 8 , wherein the polyphosphoric acid (PPA) has a calculated H 3 PO 4 content in the range of from 100 to 120%.

10 . The asphalt composition according to claim 8 , wherein the polyphosphoric acid (PPA) is water-free.

11 . The asphalt composition according to claim 8 , wherein the amount of polyphosphoric acid (PPA) is of from 0.8 to 2.0 wt.-% based on the total weight of the composition.

12 . A process for the preparation of an asphalt composition according to claim 1 comprising the following steps:
a) Heating up the starting asphalt to a temperature of from 110 to 190° C.
b) Adding the desired amount of isocyanate and the respective polymer under stirring, wherein the order of adding the desired additives is not decisive
c) After step b) the reaction mixture is stirred at a temperature in the range of from 110 to 190° C.
d) The end of the reaction is determined by IR spectroscopy
wherein the reaction is under an oxygen atmosphere.

13 . A process according to claim 12 , wherein the temperature is in the range of from 110 to 165° C.

14 . A process according to claim 12 , wherein the temperature in step a) and step c) are the same and in the range of from 110 to 165° C.

15 . A process according to claim 12 , wherein the temperature is in the range of from 110 to 165° C. and the reaction mixture is stirred for at least 2 h after the addition step b).

16 . A process according to claim 12 , wherein the end of the reaction is determined by IR spectroscopy.

17 . A method comprising providing the asphalt composition according to claim 1 and preparing an asphalt mix composition.

Assignees

• Basf Se

Inventors

• Praw Michael
• Schatz Waldemar
• Kadrmas Arlis A
• Kirk William J
• Andrews James T
• Otero Martinez Iran
• Malonson Bernie Lewis
• Fleischel Olivier

Classifications

• C08L2555/84

  Polymers comprising styrene, e.g. , polystyrene, styrene-diene copolymers or styrene-butadiene-styrene copolymers · CPC title

• C08L2555/24

  Asphalt produced between 100°C and 140°C, e.g. warm mix asphalt · CPC title

• C08L2555/22

  Asphalt produced above 140°C, e.g. hot melt asphalt · CPC title

• C08L85/02

  containing phosphorus · CPC title

• C08L53/02

  of vinyl-aromatic monomers and conjugated dienes · CPC title