Abstract

The present invention relates to a positive temperature coefficient composition comprising a semi-crystalline material, at least one binder, from 0.5 to 9.5% by weight of an electronically conductive material and a solvent. Furthermore, the present invention relates to use of a positive temperature coefficient composition according to the present invention in heating elements and sensors. A positive temperature coefficient composition according to the present invention provides low and stable resistance till self-regulating temperature, which allows fast heating of the heating element. Furthermore, the positive temperature coefficient composition according to the present invention has high PTC ration and therefore, has higher safety and more power can be applied to the heating element.

First claim

The invention claimed is:

1 . A positive temperature coefficient composition comprising:
a) a semi-crystalline material; b) at least one binder; c) from 4.5 to 8% by weight of an electronically conductive filler; and d) a solvent.

2 . The positive temperature coefficient composition according to claim 1 , wherein said semi-crystalline material is selected from the group consisting of polyethylene, polypropylene, polyvinyls, nylon, polyethylene terephthalate, polybutylene terephthalate, polyoxymethylene, natural polymers, refined hydrocarbon waxes and mixtures thereof.

3 . The positive temperature coefficient composition according to claim 1 , wherein said semi-crystalline material has a melt enthalpy greater than 150 J/g, measured according to ASTM E793.

4 . The positive temperature coefficient composition according to claim 1 , wherein said composition comprises a semi-crystalline material from 0.5 to 70% by weight of the total composition.

5 . The positive temperature coefficient composition according to claim 1 , wherein said at least one binder is selected from the group consisting of thermoplastic polyurethanes, polyesters, polyacrylates, polysiloxanes, halogenated vinyl polymers, vinylidene polymers, polyamide copolymers, phenoxy resins, polyethers, polyketones, polyvinyl butyral, polyvinyl pyrrolidone, polyacrylates and mixtures thereof.

6 . The positive temperature coefficient composition according to claim 1 , wherein said composition comprises at least two binders, wherein the first binder is selected from the group consisting of thermoplastic polyurethanes, polyesters, polyacrylates, polysiloxanes, halogenated vinyl polymers, vinylidene polymers, polyamide copolymers, phenoxy resins, polyethers, polyketones, polyvinyl butyral, polyvinyl pyrrolidone, polyacrylates and mixtures thereof, and wherein the second binder is selected from the group consisting of ethylene vinyl acetate polymers, poly vinyl alcohol, ethylene alkyl acrylate copolymers and mixtures thereof.

7 . The positive temperature coefficient composition according to claim 1 , wherein said composition comprises at least one binder from 0.5 to 8.5% by weight of the total weight of the composition.

8 . The positive temperature coefficient composition according to claim 1 , wherein said composition comprises at least two binders from 1 to 10% by weight of the total weight of the composition.

9 . The positive temperature coefficient composition according to claim 1 , wherein said electronically conductive filler is selected from the group consisting of silver, nickel, carbon, carbon black, graphite, graphene, copper, silver coated copper, silver coated graphite, gold, platinum, aluminum, iron, zinc, cobalt, lead, tin alloys and mixtures thereof.

10 . The positive temperature coefficient composition according to claim 1 , wherein said solvent is selected from the group consisting of ketones, esters, glycol esters, glycol ethers and mixtures thereof.

11 . The positive temperature coefficient composition according to claim 1 , wherein said composition comprises solvent from 5 to 80% by weight of the total weight of the composition.

12 . The positive temperature coefficient composition according to claim 1 , wherein said composition is formulated as an ink, an adhesive, a film, a tape or a hotmelt.

13 . An article comprising a positive temperature coefficient composition according to claim 1 , wherein said article is selected from the group consisting of self-controlled heaters, over-current protection devices, air conditioning units, defogging, defreezing, de-icing devices, and snow-removal devices, or said article is an automotive application selected from the group consisting of heated seats, heated mirrors, heated windows, heated steering wheels, circuit protection devices, perfume dispensers, and sensors.

Assignees

• Henkel Ag & Co Kgaa

Inventors

• Oldenzijl Rudolf Warmold
• Gillissen Stijn
• Dreezen Gunther

Classifications

• H05B2203/02

  Heaters using heating elements having a positive temperature coefficient · CPC title

• H02H9/026

  Current limitation using PTC resistors, i.e. resistors with a large positive temperature coefficient · CPC title

• H01C17/06586

  composed of organic material · CPC title

• H01C7/028 Primary

  consisting of organic substances · CPC title

• H01C17/06513

  characterised by the resistive component · CPC title