High-carbon biogenic reagents and uses thereof

Patent metadata

Field	Value
Publication number	US-12497570-B2
Application number	US-202117390665-A
Country	US
Kind code	B2
Filing date	Jul 30, 2021
Priority date	Apr 15, 2011
Publication date	Dec 16, 2025
Grant date	Dec 16, 2025

Abstract

This invention provides processes and systems for converting biomass into high-carbon biogenic reagents that are suitable for a variety of commercial applications. Some embodiments employ pyrolysis in the presence of an inert gas to generate hot pyrolyzed solids, condensable vapors, and non-condensable gases, followed by separation of vapors and gases, and cooling of the hot pyrolyzed solids in the presence of the inert gas. Additives may be introduced during processing or combined with the reagent, or both. The biogenic reagent may include at least 70 wt %, 80 wt %, 90 wt %, 95 wt %, or more total carbon on a dry basis. The biogenic reagent may have an energy content of at least 12,000 Btu/lb, 13,000 Btu/lb, 14,000 Btu/lb, or 14,500 Btu/lb on a dry basis. The biogenic reagent may be formed into fine powders, or structural objects. The structural objects may have a structure and/or strength that derive from the feedstock, heat rate, and additives.

First claim

We claim:

1 . A biogenic metallurgical coke composition comprising, on a dry basis:
at least about 85 wt % total carbon; at least trace amounts of and at most about 5 wt % hydrogen; at least trace amounts of and at most about 1 wt % nitrogen; at most about 0.5 wt % phosphorus; at most about 0.2 wt % sulfur; and at least trace amounts of an additive selected from a metal, a metal oxide, a metal hydroxide, a metal halide, or a combination thereof, wherein the additive is selected from magnesium, manganese, aluminum, nickel, chromium, silicon, boron, cerium, molybdenum, phosphorus, tungsten, vanadium, iron halide, iron chloride, iron bromide, magnesium oxide, dolomite, dolomitic lime, fluorite, fluorospar, bentonite, calcium oxide, lime, or a combination thereof; and wherein the biogenic metallurgical coke composition is substantially free of fossil fuel.

2 . The biogenic metallurgical coke composition of claim 1 , wherein the total carbon consists essentially of biogenic carbon.

3 . The biogenic metallurgical coke composition of claim 1 , comprising a heat value of at least about 11,000 BTU per pound.

4 . The biogenic metallurgical coke composition of claim 1 , comprising at least about 2 wt. % to at most about 15 wt. % dolomite.

5 . The biogenic metallurgical coke composition of claim 1 , comprising at least about 2 wt. % to at most about 15 wt. % of dolomite, at least about 2 wt. % to at most about 15 wt. % of bentonite, at least about 2 wt. % to at most about 15 wt. % of calcium oxide, at least about 2 wt. % to at most about 15 wt. % of dolomitic lime, or a combination thereof.

6 . A biogenic metallurgical coke composition comprising, on a dry basis:
at least about 85 wt % total carbon; at least trace amounts of and at most about 5 wt % hydrogen; at least trace amounts of and at most about 1 wt % nitrogen; at most about 0.5 wt % phosphorus; at most about 0.2 wt % sulfur; and at least trace amounts of an additive selected from an acid or a salt thereof, or a base or a salt thereof, wherein the additive is selected from the group consisting of sodium hydroxide, potassium hydroxide, magnesium oxide, hydrogen bromide, hydrogen chloride, sodium silicate, potassium permanganate, and combinations thereof; and wherein the biogenic metallurgical coke composition is substantially free of fossil fuel.

7 . The biogenic metallurgical coke composition of claim 6 , wherein the total carbon consists essentially of biogenic carbon.

8 . The biogenic metallurgical coke composition of claim 6 , comprising a heat value of at least about 11,000 BTU per pound.

9 . The biogenic metallurgical coke composition of claim 6 , comprising at least about 2 wt. % to at most about 15 wt. % dolomite.

10 . The biogenic metallurgical coke composition of claim 6 , comprising at least about 2 wt. % to at most about 15 wt. % of dolomite, at least about 2 wt. % to at most about 15 wt. % of bentonite, at least about 2 wt. % to at most about 15 wt. % of calcium oxide, at least about 2 wt. % to at most about 15 wt. % of dolomitic lime, or a combination thereof.

Assignees

• Carbon Tech Holdings Llc

Inventors

• Despen Daniel J
• Mennell James A
• Filips Steve

Classifications

• C01B32/312

  Preparation · CPC title

• C01B32/318

  characterised by the starting materials · CPC title

• C21C5/52

  Manufacture of steel in electric furnaces {(C21C5/005 takes precedence)} · CPC title

• C10L5/442

  Wood or forestry waste · CPC title

• C10L5/36

  Shape · CPC title