Method and apparatus for producing thin glass and thin glass ribbon produced thereby

Patent metadata

Field	Value
Publication number	US-12497320-B2
Application number	US-202117326443-A
Country	US
Kind code	B2
Filing date	May 21, 2021
Priority date	Nov 21, 2018
Publication date	Dec 16, 2025
Grant date	Dec 16, 2025

Abstract

A method for producing a flat thin glass ribbon is provided. The method includes the steps of drawing melted glass downward away from a tank in a pulling direction while applying tensile forces which act in the pulling direction to form the thin glass ribbon having a thickness of at most 250 μm and cooling the thin glass ribbon until a temperature of the thin glass ribbon undershoots a glass transition temperature. The tensile forces are transferred to the thin glass ribbon by at least two pairs of drawing rollers. The at least two pairs of drawing rollers are spaced apart transversely to the pulling direction and contact the thin glass ribbon on longitudinal edges of the thin glass ribbon. The thin glass ribbon only makes contact with the at least two pairs of drawing rollers at a position where the temperature of the thin glass ribbon is at most at or below 500° C.

First claim

What is claimed is:

1 . A method for producing a flat thin glass ribbon, comprising:
drawing melted glass downward away from a tank in a pulling direction while applying tensile forces which act in the pulling direction to form the thin glass ribbon having a thickness of at most 250 μm; and cooling the thin glass ribbon until a temperature of the thin glass ribbon undershoots a glass transition temperature, wherein the tensile forces are transferred to the thin glass ribbon by at least two pairs of drawing rollers, the at least two pairs of drawing rollers are spaced apart transversely to the pulling direction and contact the thin glass ribbon on longitudinal edges of the thin glass ribbon, and wherein the thin glass ribbon only makes contact with the at least two pairs of drawing rollers at a position where the temperature of the thin glass ribbon is below the glass transition temperature and at most at or below 500° C.

2 . The method of claim 1 , wherein the thickness is at most 70 μm.

3 . The method of claim 1 , wherein the thickness is at most 50 μm.

4 . The method of claim 1 , wherein the tank is a trough and wherein the step of drawing the melted glass away from the tank comprises:
overflowing the melted glass from the trough so that the melted glass emerges at a top of the trough and runs over two sides of the trough forming a glass stream from each of the two sides; combining the glass stream from the two sides underneath the trough to form the thin glass ribbon.

5 . The method of claim 1 , wherein the tank comprises an elongated nozzle and wherein the step of drawing the melted glass away from the tank comprises:
flowing the melted glass from the elongate nozzle away in a downward direction.

6 . The method of claim 1 , wherein the thin glass ribbon only makes contact with the at least two pairs of drawing rollers drawing rollers where the temperature of the thin glass ribbon is at most at or below 100° C.

7 . The method of claim 1 , wherein the thin glass ribbon only makes contact with the at least two pairs of drawing rollers at a position where the temperature of the thin glass ribbon is below a strain point.

8 . The method of claim 1 , further comprising deflecting the thin glass ribbon from a vertical to a horizontal position after passing the at least two pairs of drawing rollers.

9 . The method of claim 8 , further comprising:
guiding the thin glass ribbon horizontally in a freely hanging manner after being deflected to the horizontal position; and cutting off borders from the thin glass ribbon at the longitudinal edges while the thin glass ribbon is in the horizontal position.

10 . The method of claim 1 , wherein the drawing step comprises a feature selected from a group consisting of:
drawing the thin glass ribbon at a drawing speed in a range of 0.4 meters per minute to 50 meters per minute;
rotating the at least two pairs of drawing rollers at a rotational speed in a range of 1.5 revolutions per minute to 180 revolutions per minute;
adjusting the drawing speed of the thin glass ribbon based on the thickness so that a product of the drawing speed, in meters per minute, and the thickness, in micrometers, is between 200 and 1000;
adjusting the drawing speed of the thin glass ribbon based on the thickness so that a product of the drawing speed, in meters per minute, and the thickness, in micrometers, is between 500 to 900; and
any combinations thereof.

11 . The method of claim 1 , further comprising mechanically dampening transmission of vibrations to the thin glass ribbon at frequencies smaller than 1 hertz by at least 10 dB.

12 . The method of claim 1 , wherein the at least two pairs of drawing rollers have a contact width in a range of 10 mm to 50 mm.

13 . The method of claim 1 , further comprising adjusting the at least two pairs of drawing rollers to the position where the temperature of the thin glass ribbon is at most at or below 500° C.

14 . An apparatus for producing a flat thin glass ribbon, comprising:
a tank configured to receive and/or produce a glass melt so that the glass melt is drawn off downward to form a thin glass ribbon; a cooling device configured to the thin-glass ribbon; and a pulling device configured to exert tension on the thin glass ribbon so that the thin glass ribbon is drawn to a thickness of at most 250 μm, wherein the pulling device comprises at least two pairs of drawing rollers that are spaced to contact edges of the thin glass ribbon, wherein the pulling device is arranged downstream, in a pulling direction, of the cooling device and is positioned to only make contact with the thin glass ribbon at position where the thin glass ribbon has a temperature below the glass transition temperature and of at most 500° C.

15 . The apparatus of claim 14 , wherein the pulling device is arranged underneath the tank so that the at least two pairs of drawing rollers exert downward vertical tension on the thin glass ribbon.

16 . The apparatus of claim 14 , wherein the tank comprises an overflow trough configured so that the glass melt emerges at a top of the overflow trough, runs in two glass streams over sides of the overflow trough, and combine underneath the overflow trough to form the thin glass ribbon.

17 . The apparatus of claim 14 , wherein the tank comprises an elongate nozzle from which the glass melt flows away downward.

Assignees

• Schott Ag

Inventors

• Zimmer José
• Wegener Holger
• Storch Alexander

Classifications

• C03C3/093

  containing zinc or zirconium · CPC title

• C03B33/0235

  Ribbons · CPC title

• C03B17/068 Primary

  Means for providing the drawing force, e.g. traction or draw rollers · CPC title

• C03C3/091

  containing aluminium · CPC title

• C03C3/083

  containing aluminium oxide or an iron compound · CPC title