Water-based extrusion primer for polyethylene

Patent metadata

Field	Value
Publication number	US-12473454-B2
Application number	US-202117445237-A
Country	US
Kind code	B2
Filing date	Aug 17, 2021
Priority date	Feb 21, 2019
Publication date	Nov 18, 2025
Grant date	Nov 18, 2025

Abstract

The invention relates to a method of manufacturing a multilayer laminate, the multilayer laminate obtained by the method according to the invention and to forming an extrusion primer for making the multilayer laminate using an aqueous coating composition comprising at least one specific copolymer.

First claim

What is claimed is:

1 . A method of manufacturing a multilayer laminate, comprising steps of:
(i) providing a substrate comprising metal, polyethylene terephthalate, polyamide, polypropylene, polyamide or combinations thereof; (ii) applying an aqueous coating composition to at least one surface of the substrate, the aqueous coating comprising (a) at least one copolymer obtained by reacting at least one compound which is catechol or a derivative thereof with at least one polyethyleneimine and (b) water such that an amount of further components in the aqueous coating is below 5 wt.-%; (iii) subsequently drying the aqueous coating composition thereby forming a tack-free coating layer on the at least one surface of the substrate; then (iv) applying a polyolefin layer or polyolefin film onto the tack-free coating layer; and (v) applying pressure at 100 to 250° C. sufficient to melt the polyolefin layer or polyolefin film thereby forming a multilayer laminate; wherein the polyolefin layer or polyolefin film has a first surface and a second surface opposite the first surface, the first surface being corona or ozone treated and the polyolefin layer or polyolefin film being arranged such that the first surface contacts but does not adhere to the tack-free coating layer until step (v).

2 . The method of claim 1 , wherein the substrate is selected from oriented polyamide, cast polyamide, oriented polypropylene and combinations thereof.

3 . The method of claim 1 , wherein the aqueous coating composition contains the at least one copolymer in 0.01 to 1.1 wt.-%, based on total weight of the aqueous coating composition.

4 . The method of claim 1 , wherein the coating layer has an application weight of about 0.001 to 0.5 g/m 2 and the drying step (iii) is performed at 35 to 100° C., for a time of up to 10 minutes.

5 . The method of claim 1 , wherein the drying step (iii) is performed at 50 to 90° C., for a time of up to 1 minute.

6 . The method of claim 1 , wherein the substrate is a metal film.

7 . The method of claim 1 , wherein the substrate is an aluminum film.

8 . The method according to claim 7 , wherein the substrate surface comprises a polyethylene terephthalate-aluminum prelaminate and the drying step is at 90° C. for 1 minute.

9 . The method of claim 1 , wherein the substrate is an aluminum film, bonded to a polyethylene terephthalate layer.

10 . The method of claim 1 , wherein the polyolefin layer or polyolefin film is
(i) a polyethylene, polypropylene or polybutylene layer or film; or (ii) a pretreated polyolefin film.

11 . The method of claim 10 , wherein the polyolefin melt layer or polyolefin film is a polyethylene, polypropylene or polybutylene.

12 . The method according to claim 1 , wherein the at least one compound, which is catechol or a derivative thereof is selected from the group consisting of 4-(2-aminoethyl) benzene-1,2-diol, their salts and mixtures thereof.

13 . The method according to claim 1 , wherein the at least one compound, which is catechol or a derivative thereof comprises dopamine and the polyethyleneimine has a number average molecular weight of 200 to 100,000 g/mol or is an ethoxylated polyethyleneimine.

14 . The method according to claim 1 , wherein the amount of further components in the aqueous coating is below 1 wt.-%.

15 . The method according to claim 1 , wherein the amount of further components in the aqueous coating is below 0.001 wt.-%.

16 . The method according to claim 1 , wherein the at least one compound which is catechol or a derivative thereof to polyethyleneimine groups of the at least one polyethyleneimine is present in amounts such that there is a respective molar ratio from 1:0.05 to 1:25.

17 . The method of claim 1 , wherein step (v) is applied for up to 1 minute.

Assignees

• Henkel Ag & Co Kgaa

Inventors

• Blodau Marcel
• Kinzelmann Hans-Georg

Classifications

• B32B37/06

  characterised by the heating method · CPC title

• C23C22/05

  using aqueous solutions · CPC title

• B29C66/7392

  characterised by the material of at least one of the parts being a thermoplastic · CPC title

• B32B15/085

  comprising polyolefins · CPC title

• B05D7/544

  the first layer is let to dry at least partially before applying the second layer · CPC title