Direct recycling and converting cathode materials into high-performance single crystal cathode materials

Patent metadata

Field	Value
Publication number	US-12463267-B2
Application number	US-202217974022-A
Country	US
Kind code	B2
Filing date	Oct 26, 2022
Priority date	Oct 26, 2022
Publication date	Nov 4, 2025
Grant date	Nov 4, 2025

Abstract

A solid-state method for recycling spent and/or scrap cathode material includes heating a cathode material comprising lithium nickel manganese cobalt oxide in an oxygen-containing atmosphere at a temperature T1 for an effective period of time t1 to convert the cathode material to a solid precursor, combining the solid precursor with a lithium compound, and heating the solid precursor and the lithium compound in an oxygen-containing atmosphere at a temperature T2 for an effective period of time t2 to form a product comprising monocrystalline lithium nickel manganese cobalt oxide having a formula LiNixMnyMzCo1-x-y-zO2, where M represents one or more dopant metals, x≥0.33, 0.01≤y<0.33, 0≤z≤0.05, and x+y+≤z 1.0.

First claim

We claim:

1 . A solid-state method for recycling a cathode material, comprising:
(a) heating a cathode material comprising lithium nickel manganese cobalt oxide in an oxygen-containing atmosphere at a temperature T 1 of 400° C. to 1000° C. for an effective period of time t 1 to convert the cathode material to a solid precursor; and (b) converting the solid precursor to a product comprising monocrystalline lithium nickel manganese cobalt oxide, wherein converting the solid precursor to the product consists of steps (i) and (ii), wherein step (i) is mixing, without reducing particle size of the solid precursor, the solid precursor with a lithium compound at a Li: precursor molar ratio of from 0.1:1 to 1.5:1 to form a first mixture in a solid state, and step (ii) is heating the first mixture in the solid state in an oxygen-containing atmosphere at a temperature T 2 of 400° C. to 1000° C. for an effective period of time t 2 to form the product, the product having a formula LiNi x Mn y M z CO 1-x-y-2 O 2 , where M represents one or more dopant metals, x≥0.33, 0.01≤y<0.33, 0≤z≤0.05, and x+y+z≤1.0.

2 . The solid-state method of claim 1 , wherein:
x≥0.6; y=0.1-0.2; and z=0-0.05.

3 . The solid-state method of claim 1 , wherein the cathode material further comprises a binder, an additive, an electrolyte component, or any combination thereof, and heating the cathode material in the oxygen-containing atmosphere at the temperature T 1 for the effective period of time t 1 further removes the binder, the additive, the electrolyte component, or the combination thereof from the cathode material.

4 . The solid-state method of claim 1 , wherein:
the effective period of time t 1 is 1 hour to 30 hours.

5 . The solid-state method of claim 1 , wherein:
(i) the temperature T 1 is 550° C. to 650° C.; or (ii) the effective period of time t 1 is 15 hours to 25 hours; or (iii) both (i) and (ii).

6 . The solid-state method of claim 1 , wherein:
the effective period of time t 2 is 1 hour to 30 hours.

7 . The solid-state method of claim 1 , wherein:
(i) the temperature T 2 is 850° C. to 950° C.; or (ii) the effective period of time t 2 is 5 hours to 15 hours; or (iii) both (i) and (ii).

8 . The solid-state method of claim 1 , wherein the lithium compound is Li 2 O.

9 . The solid-state method of claim 8 , wherein:
(i) the Li 2 O has a mean particle size of less than or equal to 150 μm; or (ii) the Li: precursor molar ratio is from 1.1:1 to 1.3:1; or (iii) both (i) and (ii).

10 . The solid-state method of claim 1 , further comprising washing the product to remove excess lithium compound and provide a washed product.

11 . The solid-state method of claim 10 , further comprising heating the washed product at a temperature T 3 for a period of time t 3 .

12 . The solid-state method of claim 11 , wherein:
(i) the temperature T 3 is 400° C. to 1000° C.; or (ii) the effective period of time t 3 is 1 hour to 30 hours; or (iii) both (i) and (ii).

13 . The solid-state method of claim 11 , wherein:
(i) the temperature T 3 is 550° C. to 650° C.; or (ii) the effective period of time t 3 is 2 hours to 6 hours; or (iii) both (i) and (ii).

14 . The solid-state method of claim 1 , wherein z=0, and the monocrystalline lithium nickel manganese cobalt oxide has a formula LiNi x Mn y Co 1-x-y O 2 .

15 . The solid-state method of claim 1 , wherein the cathode material comprises one or more dopant metals M, where M comprises Mg, T 1 , Al, Zn, Fe, Zr, Sn, Sc, V, Cr, Fe, Cu, Ga, Y, Zr, Nb, Mo, Ru, Ta, W, Ir, or any combination thereof.

16 . The solid-state method of claim 1 , wherein the cathode material comprises a mixture of lithium nickel manganese cobalt oxide obtained from two or more spent cathodes having different lithium nickel manganese cobalt oxide compositions, two or more scrap cathode materials having different lithium nickel manganese cobalt oxide compositions, or a combination of spent cathode and scrap cathode materials having different lithium nickel manganese cobalt oxide compositions.

17 . The solid-state method of claim 1 , further comprising:
(i) disassembling a cell comprising a spent cathode, the cathode comprising the cathode material and a current collector; (ii removing the cathode material from the current collector; and (iii) then performing step (a).

18 . A solid-state method for recycling a cathode material, comprising:
(a) heating a cathode material comprising lithium nickel manganese cobalt oxide, and optionally one or more transition metal oxides, transition metal hydroxides, or any combination thereof, in an oxygen-containing atmosphere at a temperature T 1 of 400° C. to 1000° C. for an effective period of time t 1 to convert the cathode material, and the optional one or more transition metal oxides, transition metal hydroxides, or any combination thereof, to a solid precursor; and (b) converting the solid precursor to a product comprising monocrystalline lithium nickel manganese cobalt oxide, wherein converting the solid precursor to the product consists of steps (i) and (ii), wherein step (i) is mixing, without reducing particle size of the solid precursor, the solid precursor with (a) a lithium compound at a Li: precursor molar ratio of from 0.1:1 to 1.5:1, and (b) optionally one or more transition metal oxides, transition metal hydroxides, or any combination thereof, to form a first mixture in a solid state, and step (ii) is heating the first mixture in the solid state in an oxygen-containing atmosphere at a temperature T 2 of 400° C. to 1000° C. for an effective period of time t 2 to form a product comprising monocrystalline lithium nickel manganese cobalt oxide having a formula LiNi x Mn y M z Co 1-x-y-2 O 2 , where M represents one or more dopant metals, x≥0.33, 0.01≤y<0.33, 0≤z≤0.05, and x+y+z≤1.0.

19 . A method for recycling cathode material, comprising:
performing solid-state steps of
heating a cathode material comprising lithium nickel manganese cobalt oxide in an oxygen-containing atmosphere at a temperature T 1 of 400° C. to 1000° C. for a time t 1 of 1 hour to 30 hours to convert the cathode material to a solid precursor; and
converting the solid precursor to a product comprising monocrystalline lithium nickel manganese cobalt oxide, wherein converting the solid precursor to the product consists of steps (i) and (ii), wherein
step (i) is mixing, without reducing particle size of the solid precursor, the solid precursor with Li 2 O at a Li: precursor molar ratio of from 0.1:1 to 1.5:1, and
step (ii) is heating the solid precursor and the Li 2 O in an oxygen-containing atmosphere at a temperature T 2 of 400° C. to 1000° C. for a time t 2 of 1 hour to 30 hours to form the product, the product having a formula LiNi x Mn y M z Co 1-x-y-z O 2 , where M represents one or more dopant metals, x≥0.33, 0.01≤y<0.33, 0≤z≤0.05, and x+y+z≤1.0.

20 . The method of claim 19 , wherein T 1 is 550° C. to 650° C., t 1 is 15 hours to 25 hours, T 2 is 850° C. to 950° C., t 2 is 5 hours to 15 hours, and the Li: precursor molar ratio is from 1:1 to 1.3:1.

Assignees

• Battelle Memorial Institute

Inventors

• Xiao Jie
• Yi Ran
• Wu Bingbin
• Bi Yujing

Classifications

• C01G53/50

  of the type (MnO2)n-, e.g. Li(NixMn1-x)O2 or Li(MyNixMn1-x-y)O2 · CPC title