Method for preparing a catalyst comprising a nickel active phase distributed in a crust via impregnation of heptanol

Patent metadata

Field	Value
Publication number	US-12458960-B2
Application number	US-202218576257-A
Country	US
Kind code	B2
Filing date	Jul 12, 2022
Priority date	Jul 22, 2021
Publication date	Nov 4, 2025
Grant date	Nov 4, 2025

Abstract

Process for preparing a catalyst comprising a nickel active phase and an alumina support, said catalyst comprising between 1% and 50% by weight of elemental nickel relative to the total weight of the catalyst, the nickel being distributed both over a crust at the periphery of the support, and at the core of the support, which process comprises the following steps:
a) said support is impregnated with a volume V1 of a heptanol solution of between 0.2 and 0.8 times the total pore volume TPV of said support in order to obtain an impregnated support; b) the impregnated support obtained at the end of step a) is impregnated with a solution comprising a precursor of the nickel active phase in order to obtain a catalyst precursor; c) the catalyst precursor obtained at the end of step b) is dried at a temperature below 250° C.

First claim

The invention claimed is:

1 . A process for preparing a catalyst comprising an active phase based on nickel and alumina support, said catalyst comprising between 1% and 50% by weight of elemental nickel relative to the total weight of the catalyst, the nickel being distributed both over a crust at the periphery of the support, and at the core of the support, the thickness of said crust being between 2% and 15% of the diameter of the catalyst, the size of the nickel particles in the catalyst, measured in oxide form, being less than 15 nm, which process comprises:
a) impregnating said support with a volume V1 of a heptanol solution of between 0.2 and 0.8 times the total pore volume TPV of said support in order to obtain an impregnated support; b) impregnating the impregnated support obtained at the end of a) with a solution comprising at least one precursor of the nickel active phase in order to obtain a catalyst precursor; and c) drying the catalyst precursor obtained at the end of b) at a temperature below 250° C.

2 . The process as claimed in claim 1 , wherein, in b), the volume V2 of the solution comprising at least one precursor of the nickel active phase impregnated on the impregnated support obtained at the end of a) is such that V2=TPV−V1.

3 . The process as claimed in claim 1 , wherein c) is carried out for a time of between 0.5 hour and 12 hours.

4 . The process as claimed in claim 1 , further comprising d) calcining the catalyst obtained at the end of c) at a temperature of between 250° C. and 600° C.

5 . The process as claimed in claim 4 , wherein d) is carried out for between 0.5 hour and 24 hours.

6 . The process as claimed in claim 1 , wherein, in a), said volume V1 of said heptanol solution is between 0.25 and 0.75 times the total pore volume TPV of said support.

7 . The process as claimed in claim 1 , wherein, in a), a solution of n-heptanol is used.

8 . The process as claimed in claim 1 , further comprising b1) wherein either the impregnated support obtained at the end of a), or the catalyst precursor obtained at the end of b), is impregnated with at least one solution containing at least one organic compound comprising at least one carboxylic acid function, or at least one alcohol function, or at least one ester function, or at least one amide function, or at least one amine function, b) and b1) being carried out in any order, or simultaneously.

9 . The process as claimed in claim 8 , wherein the volume V2 of the solution comprising at least one precursor of the active nickel phase and the volume V3 of the solution comprising at least one organic compound which are impregnated on the impregnated support obtained at the end of a) are such that V2+V3=TPV−V1.

10 . The process as claimed in claim 8 , wherein the b) and b1) are carried out simultaneously.

11 . The process as claimed in claim 10 , wherein the volume V2′ of the solution comprising at least one precursor of the active nickel phase and at least one organic compound which are impregnated on the impregnated support obtained at the end of a) is such that V2′=TPV−V1.

12 . The process as claimed in claim 8 , wherein the mole ratio of said organic compound introduced in b1) to the nickel element also introduced in b) is between 0.01 and 5.0 mol/mol.

13 . The process as claimed in claim 8 , wherein the organic compound of b1) is chosen from oxalic acid, malonic acid, glycolic acid, lactic acid, tartronic acid, citric acid, tartaric acid, pyruvic acid, levulinic acid, ethylene glycol, propane-1,3-diol, butane-1,4-diol, glycerol, xylitol, mannitol, sorbitol, diethylene glycol, glucose, gamma-valerolactone, dimethyl carbonate, diethyl carbonate, formamide, N-methylformamide, acetamide, N-methylacetamide, N,N-dimethylmethanamide, 2-pyrrolidone, γ-lactam, lactamide, urea, alanine, arginine, lysine, proline, serine, and EDTA.

14 . The process as claimed in claim 1 , further comprising a1) maturing the impregnated support obtained at the end of a) for 0.5 hour to 40 hours.

15 . The process as claimed in claim 8 , wherein the size of the nickel particles in the catalyst, measured in oxide form, is less than 13 nm.

Assignees

• Ifp Energies Now

Inventors

• Boualleg Malika
• Jothie Laetitia

Classifications

• B01J2235/15

  X-ray diffraction · CPC title

• B01J35/51

  Spheres · CPC title

• C07C2523/755

  Nickel · CPC title

• C07C2521/04

  Alumina · CPC title

• C07C5/11

  Partial hydrogenation · CPC title