Room temperature vulcanisable silicone compositions

Patent metadata

Field	Value
Publication number	US-12454616-B2
Application number	US-202017621650-A
Country	US
Kind code	B2
Filing date	Jun 23, 2020
Priority date	Jun 27, 2019
Publication date	Oct 28, 2025
Grant date	Oct 28, 2025

Abstract

A silicone elastomer composition which is generally storage stable, and cures to an elastomeric body, comprising; (i) an organopolysiloxane polymer having at least two hydroxyl or hydrolysable groups; (ii) a siloxane and/or silane cross-linker having at least three groups per molecule which are reactable with the hydroxyl or hydrolysable groups in the organopolysiloxane polymer (i); (iii) a solid organosilicate resin which is substantially unreactive with components (i) and (ii) and comprising R32SiO1/2 and SiO4/2 siloxane units, wherein the molar ratio of the R32SiO1/2 siloxane units to SiO4/2 siloxane units is from 0.5:1 to 1.2:1, and R2 is selected from hydrocarbon groups; and optionally (iv) a suitable condensation cure catalyst. The solid organosilicate resin (iii) is generally utilised to create a low modulus room temperature vulcanisable (RTV) silicone composition which when cured may be used as a coating, an adhesive or a sealant having high movement capability.

First claim

What is claimed is:

1. A silicone elastomer composition which is storage stable, and capable of cure to an elastomeric body, the composition comprising:
(i) an organopolysiloxane polymer having at least two hydroxyl or hydrolysable groups per molecule and of the general formula
X 3-n R n Si—(Z)—(R 1 y SiO (4-y)/2)z —(SiR 1 2 —Z)—Si—R n X 3-n

in which each X is an alkoxy group, each R is an alkyl, alkenyl or aryl group, each R 1 is an X group, alkyl group, alkenyl group or aryl group, and Z is a divalent organic group; and n is 0 or 1, y is 0, 1 or 2, and z is an integer such that the organopolysiloxane polymer (i) has a viscosity of from 1,000 to 75,000 mPa·s at 25° C.;
(ii) a siloxane and/or silane cross-linker having at least three groups per molecule which are reactable with the hydroxyl or hydrolysable groups in the organopolysiloxane polymer (i);
(iii) a solid organosilicate resin which is a product of a reaction of an organosilicate resin precursor with a treating agent such that the solid organosilicate resin is substantially unreactive with components (i) and (ii) and comprising R 2 3 SiO 1/2 siloxane units and SiO 4/2 siloxane units, wherein the molar ratio of the R 2 3 SiO 1/2 siloxane units to SiO 4/2 siloxane units is from 0.5:1 to 1.2:1, and R 2 is selected from hydrocarbon groups; the solid organosilicate resin (iii) having a weight average molecular weight of from 3,000 to 30,000 g/mol; and optionally
(iv) a suitable condensation cure catalyst; and
wherein the solid organosilicate resin (iii) comprises vinyl functional groups.

2. The silicone elastomer composition in accordance with claim 1 , wherein the molar ratio of the total M siloxane units to total Q siloxane units of the organosilicate resin (iii) is from 0.6:1 to 0.8:1.

3. The silicone elastomer composition in accordance with claim 1 , wherein the composition further comprises one or more reinforcing fillers and/or non-reinforcing fillers.

4. The silicone elastomer composition in accordance with claim 1 , wherein the composition is further defined as a moisture curable sealant composition, an elastomeric coating composition, or an adhesive composition.

5. The silicone elastomer composition in accordance with claim 4 , which is gunnable and/or self-levelling.

6. The silicone elastomer composition in accordance with claim 4 , being the moisture curable sealant composition and which is capable of being applied as a paste to a joint between two adjacent substrate surfaces where it can be worked, prior to curing, to provide a smooth surfaced mass which will remain in its allotted position until it has cured into an elastomeric body adherent to the adjacent substrate surfaces.

7. A silicone elastomer which is the reaction product obtained by curing the silicone elastomer composition in accordance with claim 1 .

8. An elastomeric coating obtained by curing the silicone elastomer composition in accordance with claim 5 on a substrate,
(i) as a weatherproof coating for concrete and/or construction substrate surfaces;
(ii) as or in a flashing agent;
(iii) as or in a roof seal; and/or
(iv) in an intumescent coating.

9. A method of applying the silicone elastomer composition in accordance with claim 1 over a roofing surface or substrate by applying the silicone elastomer composition in the form of a moisture curable elastomeric coating composition with an applicator and allowing the composition to cure.

10. The method of applying in accordance with claim 9 , wherein the applicator is a sprayer, a brush, a roller, or a squeegee.

11. The method of applying in accordance with claim 9 , wherein the composition at least partially penetrates into a roofing fabric prior to cure and as such the resulting elastomeric coating is in and/or on the roofing fabric once cured.

12. The silicone elastomer composition in accordance with claim 1 , wherein each R 2 is selected from alkyl groups, cycloaliphatic groups, aryl groups, alkenyl groups, and chlorinated hydrocarbon groups.

13. The silicone elastomer composition in accordance with claim 1 , wherein the solid organosilicate resin (iii) has a weight average molecular weight of from 21,000 g/mol to 30,000 g/mol.

14. A method for filling a space between two substrates to create a seal therebetween, the method comprising:
a) providing a silicone composition; and either
b1) applying the silicone composition to a first substrate, and bringing a second substrate in contact with the silicone composition that has been applied to the first substrate, or
b2) filling a space formed by the arrangement of a first substrate and a second substrate with the silicone composition and curing the silicone composition;
wherein the silicone composition is the silicone elastomer composition in accordance with claim 1 .

15. The method for filling a space between two substrates in accordance with claim 14 , wherein the space is filled by introducing the silicone composition by way of extrusion or through a sealant gun.

16. A method of reducing modulus and/or increasing elasticity of an elastomeric body obtained or obtainable by curing a moisture curable composition, the composition comprising:
(i) an organopolysiloxane polymer having at least two hydroxyl or hydrolysable groups per molecule and of the general formula
X 3-n R n Si—(Z)—(R 1 y SiO (4-y)/2)z —(SiR 1 2 —Z)—Si—R n X 3-n

in which each X is an alkoxy group, each R is an alkyl, alkenyl or aryl group, each R 1 is an X group, alkyl group, alkenyl group or aryl group, and Z is a divalent organic group; and n is 0 or 1, y is 0, 1 or 2, and z is an integer such that the organopolysiloxane polymer (i) has a viscosity of from 1,000 to 75,000 mPa·s at 25° C.;
(ii) a siloxane and/or silane cross-linker having at least three groups per molecule which are reactable with the hydroxyl or hydrolysable groups in the organopolysiloxane polymer (i); and
optionally
(iv) a suitable condensation cure catalyst;
the method comprising introducing (iii) a solid organosilicate resin into the composition prior to cure, and subsequently curing the composition;
wherein the solid organosilicate resin (iii) is a product of a reaction of an organosilicate resin precursor with a treating agent such that the solid organosilicate resin is substantially unreactive with components (i) and (ii), comprises R 2 3 SiO 1/2 siloxane units and SiO 4/2 siloxane units, the molar ratio of the R 2 3 SiO 1/2 siloxane units to SiO 4/2 siloxane units is from 0.5:1 to 1.2:1, and R 2 is selected from hydrocarbon groups; the solid organosilicate resin (iii) having a weight average molecular weight of from 3,000 to 30,000 g/mol; and

wherein the solid organosilicate resin (iii) comprises vinyl functional groups.

17. A method of preparing a silicone elastomeric sealant composition which is stable in the absence of moisture and cures upon exposure to moisture, the method comprising:
(A) mixing in the absence of moisture components (i), (ii), and (iii), and optionally component (iv), to form a mixture;
(i) an organopolysiloxane polymer having at least two hydroxyl or hydrolysable groups per molecule and of the general formula
X 3-n R n Si—(Z)—(R 1 y SiO (4-y)/2)z —(SiR 1 2 —Z)—Si—R n X 3-n

in which each X is an alkoxy group, each R is an alkyl, alkenyl or aryl group, each R 1 is an X group, alkyl group, alkenyl group or aryl group, and Z is a divalent organic group; and n is 0 or 1, y is 0, 1 or 2, and z is an integer such that the organopolysiloxane polymer (i) has a viscosity of from 1,000 to 75,000 mPa·s at 25° C.;
(

Assignees

• Dow Silicones Corp

Inventors

• Seitz Aaron
• Repollet-Pedrosa Milton H
• Nesbitt Rochelle
• Gordon Glenn

Classifications

• E04D7/00

  Roof covering {exclusively consisting of} sealing masses applied in situ; Gravelling of flat roofs · CPC title

• E04B1/947

  by closing openings in walls or the like in the case of fire (fire-proof doors E06B5/16) · CPC title

• E04B1/6801

  Fillings therefor · CPC title

• D06N3/128

  with silicon polymers · CPC title

• C09J2483/00

  Presence of polysiloxane · CPC title