Very high-strength, cold-rolled, dual steel sheets

Patent metadata

Field	Value
Publication number	US-12448661-B2
Application number	US-201816213455-A
Country	US
Kind code	B2
Filing date	Dec 7, 2018
Priority date	May 21, 2008
Publication date	Oct 21, 2025
Grant date	Oct 21, 2025

Abstract

The present invention provides a cold-rolled and annealed Dual-Phase steel sheet having a tensile strength from 980 to 1100 MPa. The composition includes the contents being expressed by weight: 0.055%≤C≤0.095%, 2%≤Mn≤2.6%, 0.005%≤Si≤0.35%, S≤0.005%, P≤0.050%, 0.1≤Al≤0.3%, 0.05%≤Mo≤0.25%, 0.2%≤Cr≤0.5%, Cr+2 Mo≤0.6%, Ni≤0.1%, 0.010≤Nb≤0.040%, 0.010≤Ti≤0.050%, 0.0005≤B≤0.0025%, and 0.002%≤N≤0.007%. The remainder of the composition includes iron and inevitable impurities resulting from the smelting. A microstructure of the steel sheet is 40 to 65% ferrite, 35 to 50% martensite and 0 to 10% bainite. A non-recrystallized ferrite fraction is less than or equal to 15%.

First claim

What is claimed is:

1. A cold-rolled and annealed Dual-Phase steel sheet comprising:
a composition comprising, the contents being expressed by weight:
0.055%≤C≤0.095%;

2%≤Mn≤2.6%;

0.005%≤Si≤0.35%;

S≤0.005%;

P≤0.050%;

0.1≤Al≤0.3%;

0.05%≤Mo≤0.25%;

0.2%≤Cr≤0.5%;

Cr+2Mo≤0.6%;

Ni≤0.1%;

0.010≤Nb≤0.040%;

0.010≤Ti≤0.050%;

0.0005≤B≤0.0025%; and

0.002%≤N≤0.007%;

a remainder of the composition comprising iron and the inevitable impurities resulting from smelting;
a tensile strength between 980 and 1100 MPa; and
a microstructure consisting of 40 to 65% ferrite, 35 to 50% martensite and 0 to 10% bainite, a non-recrystallized ferrite fraction being less than or equal to 15%.

2. The steel sheet as recited in claim 1 , wherein the composition of the steel contains, the content being expressed by weight: 0.12%≤Al≤0.25%.

3. The steel sheet as recited in claim 1 , wherein the composition of the steel contains, the content being expressed by weight: 0.10%≤Si≤0.30%.

4. The steel sheet as recited in claim 1 , wherein the composition of the steel contains, the content being expressed by weight: 0.15%≤Si≤0.28%.

5. The steel sheet as recited in claim 1 , wherein the composition of the steel contains, the content being expressed by weight: P≤0.015%.

6. The steel sheet as recited in claim 1 , wherein a microstructure of the steel sheet includes a surface area fraction of 35 to 50% martensite.

7. The steel sheet as recited in claim 6 , wherein a remainder of the microstructure consists of a surface area fraction of 50 to 65% ferrite.

8. The steel sheet as recited in claim 6 , wherein a remainder of the microstructure consists of surface area fractions of 1 to 10% bainite and 40 to 64% ferrite.

9. The steel sheet as recited in claim 1 , wherein a remainder of the microstructure consists of martensite and ferrite.

10. The steel sheet as recited in claim 1 , wherein a ratio of yield strength Re to strength Rm is such that: 0.6≤Re/Rm≤0.8.

11. The steel sheet as recited in claim 1 , wherein the steel sheet is continuously galvanized.

12. The steel sheet as recited in claim 1 , further comprising a galvannealed coating.

13. A structural or safety part for a motor vehicle comprising:
the steel sheet as recited in claim 1 .

14. The steel sheet as recited in claim 1 , wherein the composition consists of:
0.055%≤C≤0.095%;

2%≤Mn≤2.6%;

0.005%≤Si≤0.35%;

S≤0.005%;

P≤0.050%;

0.1≤Al≤0.3%;

0.05%≤Mo≤0.25%;

0.2%≤Cr≤0.5%;

Cr+2Mo≤0.6%;

Ni≤0.1%;

0.010≤Nb≤0.040%;

0.010≤Ti≤0.050%;

0.0005≤B≤0.0025%; and

0.002%≤N≤0.007%;

the remainder of the composition consisting of iron and the inevitable impurities resulting from smelting.

15. The steel sheet as recited in claim 1 , wherein the composition consists of:
0.055%≤C≤0.095%;

2%≤Mn≤2.6%;

0.15%≤Si≤0.28%;

S≤0.005%;

P≤0.015%;

0.12≤Al≤0.25%;

0.05%≤Mo≤0.25%;

0.2%≤Cr≤0.5%;

Cr+2Mo≤0.6%;

Ni≤0.1%;

0.010≤Nb≤0.040%;

0.010≤Ti≤0.050%;

0.0005≤B≤0.0025%; and

0.002%≤N≤0.007%;

the remainder of the composition consisting of iron and the inevitable impurities resulting from smelting.

16. The steel sheet as recited in claim 1 , wherein the tensile strength is from 1020 to 1030 MPa and wherein the elongation is from 10 to 14%.

17. The steel sheet as recited in claim 16 , wherein the microstructure includes 42 to 46% martensite.

18. The steel sheet as recited in claim 1 , wherein all of the ferrite in the microstructure is recrystallized ferrite.

19. The steel sheet as recited in claim 1 , wherein the microstructure consists of ferrite, 42 to 46% martensite and up to 8% bainite.

20. The steel sheet as recited in claim 1 , wherein the steel sheet is annealed at a temperature from 780 to 800° C. for 90 to 100 seconds.

21. The steel sheet as recited in claim 1 , wherein the steel sheet is heated at 2° C./s to an annealing temperature from 780 to 800° C. and annealed for 90 to 100 seconds.

22. The steel sheet as recited in claim 1 , wherein the steel sheet is cooled at a rate from 17 to 20° C./s after annealing.

23. The steel sheet as recited in claim 1 , wherein 0.38%≤Cr+2Mo≤0.512%.

24. The steel sheet as recited in claim 1 , wherein 0.27%≤Cr≤0.33%.

25. The steel sheet as recited in claim 24 , wherein 0.055%≤Mo≤0.104%.

26. The steel sheet as recited in claim 25 , wherein 0.062%≤C≤0.076%.

27. The steel sheet as recited in claim 1 , wherein 0.062%≤C≤0.076%.

28. The steel sheet as recited in claim 1 , wherein the martensite comprises islands of average size less than four microns.

29. The steel sheet as recited in claim 28 , wherein at least 50% of the islands have a ratio of their maximum dimension Lmax to their minimum dimension Lmin of less than or equal to 2.

30. The steel sheet as recited in claim 1 , wherein the martensite comprises islands of average size less than two microns, and at least 50% of the islands have a ratio of their maximum dimension Lmax to their minimum dimension Lmin of less than or equal to 2.

31. The steel sheet as recited in claim 1 , wherein the non-recrystallized ferrite fraction is 0%.

Assignees

• Arcelormittal

Inventors

• Moulin Antoine
• Sardoy Veronique
• Vinci Catherine
• Restrepo Gacess Gloria
• Watershoot Tom
• Goune Mohamed

Classifications

• C21D8/02

  during manufacturing of plates or strips (C21D8/12 takes precedence) · CPC title

• C23C2/36

  Elongated material · CPC title

• C23C2/06

  Zinc or cadmium or alloys based thereon · CPC title

• C22C38/58 Primary

  with more than 1.5% by weight of manganese · CPC title

• C22C38/54

  with boron · CPC title