Shrinkage reducer for mineral binder composition and its use

Patent metadata

Field	Value
Publication number	US-12448329-B2
Application number	US-202017439491-A
Country	US
Kind code	B2
Filing date	Mar 13, 2020
Priority date	Mar 15, 2019
Publication date	Oct 21, 2025
Grant date	Oct 21, 2025

Abstract

An additive, in particular a shrinkage reducing agent, for mineral binder compositions including at least one super absorbent polymer SAP and at least one defoamer D. Further, a mineral binder composition including the additive, processes and methods for the mixing thereof, and to hardened articles obtainable therefrom.

First claim

The invention claimed is:

1. An admixture for mineral binder compositions, comprising at least one superabsorbent polymer SAP and at least one defoamer D,
wherein the admixture does not comprise water,
wherein the at least one defoamer D is selected from the group consisting of mineral oils, vegetable oils, or white oils which may comprise a wax and/or hydrophobic silica, silicones, which can be modified by alkoxylation or fluorination, alkyl esters of phosphoric or phosphonic acid, alkoxylated polyols, and alkoxylated fatty alcohols, and
wherein the weight ratio of the at least one SAP to the at least one defoamer D is from 2:1-1:10.

2. The admixture according to claim 1 , wherein the at least one superabsorbent polymer SAP is selected from the group consisting of polyacrylamide, polyacrylonitrile, polyvinyl alcohol, isobutylene maleic anhydride copolymers, polyvinylpyrrolidone, homo- and copolymers of monoethylenically unsaturated carboxylic acids, which can be partially or fully neutralized, and co- and terpolymers of the monoethylenically unsaturated carboxylic acids with vinylsulfonic acid, (meth)acrylamidoalkylsulfonic acid, allylsulfonic acid, vinyltoluenesulfonic acid, vinylphosphonic acid, (meth)acrylamide, N-alkylated (meth)acrylamide, N-methylol (meth)acrylamide, N-vinylamide, N-vinylformamide, N-vinylacetamide, vinylpyrrolidon, hydroxyalkyl (meth)acrylate, ethylacrylate, methylacrylate, (meth)acrylic acid esters of polyethyleneglycolmonoallylethers, vinylacetate and/or styrene.

3. The admixture according to claim 1 , wherein at least one superabsorbent polymer SAP is a polyacrylic acid which can be partially or fully neutralized and which is crosslinked.

4. The admixture according to claim 1 , wherein the admixture is combined with an aqueous solution or dispersion, and the at least one SAP and the at least one defoamer D combined comprise an amount of up to 85 wt.-%, based on the total weight of the admixture and the aqueous solution or dispersion.

5. A mineral binder composition comprising the admixture according to claim 1 , wherein the mineral binder composition includes:
a) 10-65 wt.-% of at least one mineral binder,
b) 0.01-0.5 wt.-% of the at least one SAP,
c) 0.05-2 wt.-% of the at least one defoamer D,
d) 0-85 wt.-% of aggregates,
e) 0-10 wt.-% of other additives selected from the group consisting of plasticizers, superplasticizers, accelerators, retarders, rheology modifiers, anti-settling agents, pigments, corrosion inhibitors, fibers, strength enhancers, waterproofing additives, alkali-aggregate reaction inhibitors, chromate reducers, and/or anti-microbial agents, and
f) optionally water,

each based on the total dry weight of the mineral binder composition.

6. A mineral binder composition according to claim 5 , wherein the at least one mineral binder is a mixture of at least one CEM I or CEM II and at least one calcium sulfoaluminate cement.

7. A mineral binder composition according to claim 5 , wherein the mineral binder comprises
a) 0.1-8 wt.-%, each based on the dry weight of the mineral binder composition, of a CSA cement and
b) 2-64.9 wt.-%, each based on the dry weight of the mineral binder composition, of a CEM I and/or a CEM II.

8. A mineral binder composition according to claim 5 , wherein the mineral binder composition comprises
a) 0.02-1.0 wt.-% of a polycarboxylate ether composed of (meth)acrylic acid and methyl polyalkylene glycol (meth)acrylates and having a molecular weight Mw of 8,000 to 200,000 g/mol and
b) a maximum of 1 wt.-% of at least one thickener selected from the group consisting of starch, pectin, amylopectin, modified starch, cellulose, modified cellulose, casein, welan gum, xanthan gum, diutan gum, galactomannanes, alginates, tragacanth gum, dextran, polydextrose, and layered silicates, each based on the total weight of the mineral binder composition.

9. A method of producing a hardened article comprising the steps of
1) mixing a mineral binder composition according to claim 5 with water,
2) Optionally conveying the mixture obtained in 1) to the location of placing,
3) Placing the mixture obtained in 1) into any desired shape,
4) curing the mixture obtained in 1),

wherein step 1) is done in a continuous process by means of a static and/or dynamic mixer.

10. A process comprising forming an article by additive manufacturing from a material that includes a water-containing mineral binder composition of claim 5 .

11. A shaped article obtainable by curing a mineral binder composition according to claim 5 .

12. The admixture according to claim 1 , wherein the at least one defoamer D is selected from the group consisting of ethoxylated 2,4,7,9-tetramethyl-5-decyn-4,7-diol, a combination of fatty alcohol alkoxylate and polysiloxane, and a combination of a mineral oil and a silicone oil comprising hydrophobic silica.

Assignees

• Sika Tech Ag

Inventors

• Boon Gary
• Liard Maxime
• Lootens Didier
• Hauguel Lolita

Classifications

• C04B2111/34

  Non-shrinking or non-cracking materials · CPC title

• C04B2103/50

  Defoamers, air detrainers · CPC title

• C04B2103/44

  Thickening, gelling or viscosity increasing agents · CPC title

• C04B2103/0051

  Water-absorbing polymers, hydrophilic polymers · CPC title

• C04B40/0042

  Powdery mixtures · CPC title