Activation of self-passivating metals using reagent coatings for low temperature nitrocarburization in the presence of oxygen-containing gas

Patent metadata

Field	Value
Publication number	US-12435406-B2
Application number	US-202217731437-A
Country	US
Kind code	B2
Filing date	Apr 28, 2022
Priority date	Apr 28, 2021
Publication date	Oct 7, 2025
Grant date	Oct 7, 2025

Abstract

A method for low-temperature interstitial case formation on a self-passivating metal workpiece includes exposing the workpiece in a heated gaseous environment comprising oxygen to pyrolysis products of a nonpolymeric reagent comprising nitrogen and carbon.

First claim

We claim:

1. A method for low-temperature interstitial case formation on a self-passivating metal workpiece comprising exposing the workpiece in a heated gaseous environment comprising atmospheric oxygen to pyrolysis products of a nonpolymeric reagent comprising at least nitrogen and carbon.

2. The method of claim 1 , wherein the reagent comprises at least one functionality selected from a guanidine or melamine, and wherein pyrolyzing the nonpolymeric reagent in the gaseous environment comprising oxygen reduces residual reagent from an amount of residual reagent produced by pyrolyzing the nonpolymeric reagent in a gaseous environment that does not comprise oxygen.

3. The method of claim 1 , wherein the reagent is associated with HCl or Cl.

4. The method of claim 1 , wherein the reagent comprises at least one of guanidine, guanidine HCl, biguanide, biguanide HCl, 1,1-dimethylbiguanide, 1,1-dimethylbiguanide HCl, melamine, melamine HCl, and combinations thereof.

5. The method of claim 1 , wherein at least a portion of the workpiece comprises a cast, wrought, work hardened, precipitation hardened, partially annealed, fully annealed, formed, rolled, forged, machined, welded, stamped, additive manufactured, powder metal sintered, hot isostatic pressurized, and subtractive manufactured metal.

6. The method of claim 1 , wherein the case formation comprises at least one of case hardening, case formation for corrosion resistance, and case formation for abrasion resistance.

7. The method of claim 1 , wherein the case formation results in change in at least one property selected from magnetic, electrical, thermodynamic, bioactive, and mechanical properties as compared to a comparable workpiece that is identical except not subject to the exposing.

8. The method of claim 1 , further comprising maintaining a temperature of 700° C. or less during the exposing.

9. The method of claim 1 , further comprising maintaining the temperature at about 450° C. or less during the exposing.

10. The method of claim 1 , wherein the exposing is performed for a time period of 24 hours or less.

11. The method of claim 1 , wherein the exposing is performed for a time period of 8 hours or less.

12. The method of claim 1 , wherein the exposing is performed for a time period of 1 hour or less.

13. The method of claim 1 , wherein at least a portion of the metal workpiece comprises stainless steel including at least 2 wt. % Mo.

14. The method of claim 13 , wherein the stainless steel comprises at least 6 wt. % Mo.

15. The method of claim 1 , further comprising coating the reagent on at least a portion of the surface of the workpiece prior to the exposing.

16. The method of claim 1 , wherein the case formation results in a case layer on the workpiece at least about 1 μm thick.

17. The method of claim 1 , wherein the case formation results in a case layer on the workpiece at least about 14 μm thick.

18. A method for low-temperature interstitial case formation on a self-passivating metal workpiece comprising exposing the workpiece in a heated gaseous environment comprising atmospheric oxygen to pyrolysis products of at least one ligand-forming reagent.

19. The method of claim 18 , wherein the reagent comprises at least one functionality selected from a guanidine, urea, imidazole, and methylammonium.

20. The method of claim 18 , wherein the reagent is associated with HCl or Cl.

21. The method of claim 18 , wherein the reagent comprises at least one of guanidine HCl, biguanide HCl, dimethylbiguanide HCl, methylammonium Cl, and combinations thereof.

Assignees

• Swagelok Co
• Univ Case Western Reserve

Inventors

• Ernst Frank
• Johns Todd
• Edmonson Ronald
• Illing Cyprian Adair William
• Williams Peter C
• Semkow Christina

Classifications

• C23C8/32

  of ferrous surfaces · CPC title

• C23C8/26

  of ferrous surfaces · CPC title

• C21D1/06

  Surface hardening · CPC title

• C23C18/02

  by thermal decomposition · CPC title

• C23C8/30

  Carbo-nitriding · CPC title