Reforming catalyst and a method of modification and application thereof

Patent metadata

Field	Value
Publication number	US-12427507-B2
Application number	US-202017761160-A
Country	US
Kind code	B2
Filing date	Jul 23, 2020
Priority date	Feb 13, 2020
Publication date	Sep 30, 2025
Grant date	Sep 30, 2025

Abstract

The present disclosure provides a process for preparing a reforming catalyst, said process comprising: (a) impregnating at least one support with at least one promoter metal and at least one active metallic component to obtain a second catalytic precursor; (b) contacting the second catalytic precursor with at least one non-metallic component to obtain a third catalytic precursor; (c) coating the third catalytic precursor with at least one silanizing agent to obtain a coated third catalytic precursor; and (d) drying the coated third catalytic precursor to obtain a dried third catalytic precursor followed by calcination of the dried third catalytic precursor to obtain the reforming catalyst. The present disclosure also provides a reforming catalyst and the process for catalytically reforming a hydrocarbon feed stream by using the reforming catalyst.

First claim

We claim:

1. A process for preparing a reforming catalyst, the process consisting of:
first, impregnating at least one support with at least one promoter metal and at least one active metallic component to obtain a second catalytic precursor;
second, contacting the second catalytic precursor with aqueous HCl to obtain a third catalytic precursor;
third, coating the third catalytic precursor with tetraethyl orthosilicate at a temperature in a range of 20-35° C. to obtain a coated third catalytic precursor, wherein coating with tetraethyl orthosilicate improves an acidic character of the at least one support and improves a sinter resistance behavior of the at least one active metallic component; and
fourth, drying the coated third catalytic precursor to obtain a dried third catalytic precursor followed by calcination of the dried third catalytic precursor for a time period in a range of 3-7 hours at a temperature in a range of 400-600° C. to obtain the reforming catalyst.

2. The process as claimed in claim 1 , wherein the at least one support is selected from the group consisting of alpha-aluminium oxide, beta-aluminium oxide, gamma-aluminium oxide, delta-aluminium oxide, theta-aluminium oxide, SiO 2 , silica-alumina (SIRALs), titania, zirconia, zinc oxide, composites of alumina and zeolites, spinel structures, and combinations thereof, and is co-impregnated or sequentially impregnated with the at least one promoter metal and the at least one active metallic component.

3. The process as claimed in claim 1 , wherein impregnating the at least one support is done with an aqueous solution comprising the at least one promoter metal to obtain a first catalytic precursor, and
depositing an aqueous solution comprising the at least one active metallic component on the first catalytic precursor to obtain the second catalytic precursor.

4. The process as claimed in claim 1 , wherein the at least one promoter metal is selected from the group consisting of tin, rhenium, germanium, iridium, thallium, lead, indium, and combinations thereof and the at least one active metallic component is selected from the group consisting of platinum, palladium, ruthenium, rhodium, osmium, iridium, and combinations thereof.

5. The process as claimed in claim 1 , wherein the at least one support has a porosity in a range of 2-20 nm.

6. The process as claimed in claim 3 , wherein impregnating the at least one support comprises:
contacting the aqueous solution comprising the at least one promoter metal to the at least one support is carried out at a pH in a range of 1-4 for a time period in a range of 40-120 minutes at a temperature in a range of 40-60° C. at a speed in a range of 100-150 rpm, followed by drying at a temperature in a range of 40-120° C., under a pressure in a range of 30-200 mbar for a time period 20-90 minutes to obtain the first catalytic precursor.

7. The process as claimed in claim 3 , wherein depositing the aqueous solution comprising the at least one active metallic component on the first catalytic precursor comprises:
contacting the aqueous solution comprising the at least one active metallic component to the first catalytic precursor for a time period in a range of 40-120 minutes at a temperature in a range of 40-60° C. at a speed in a range of 100-150 rpm, followed by drying at a temperature in a range of 40-120° C., under a pressure in a range of 30-200 mbar for a time period 20-90 minutes to obtain the second catalytic precursor.

8. The process as claimed in claim 1 , wherein contacting the second catalytic precursor with aqueous HCl is carried out at a temperature in a range of 40-60° C. and under a pressure in a range of 30-200 mbar followed by drying at a temperature in a range of 60-120° C. for a time period in a range of 10-20 hours to obtain the third catalytic precursor.

9. The process as claimed in claim 1 , wherein contacting the second catalytic precursor with aqueous HCl is carried out at a temperature in a range of 450-600° C. for a time period in a range of 1-8 hours followed by drying at a temperature in a range of 60-120° C. for a time period in a range of 10-20 hours to obtain the third catalytic precursor.

10. The process as claimed in claim 1 , wherein contacting the third catalytic precursor with tetraethyl orthosilicate is carried out at a temperature in a range of 20-35° C. under a pressure in a range of 30-200 mbar for a time period in a range of 20-130 minutes to obtain the coated third catalytic precursor.

11. The process as claimed in claim 1 , wherein drying of the coated third catalytic precursor is carried out at a temperature in a range of 100-130° C. to obtain the dried third catalytic precursor followed by calcination of the dried third catalytic precursor to obtain the reforming catalyst.

12. A reforming catalyst prepared from the process as claimed in claim 1 .

Assignees

• Hindustan Petroleum Corp Ltd

Inventors

• Santhosh Kotni
• Reddy Sandiri Santhoshkumar
• Chelliahn Bennet
• Ramachandrarao Bojja
• Gnanasekaran Valavarasu

Classifications

• B01J35/60

  characterised by their surface properties or porosity · CPC title

• B01J35/19

  Catalysts containing parts with different compositions · CPC title

• B01J37/0236

  Drying, e.g. preparing a suspension, adding a soluble salt and drying · CPC title

• B01J37/0219

  the coating containing organic compounds · CPC title

• B01J37/0209

  involving a reaction between the support and a fluid · CPC title