Aluminum-chromium-zirconium alloys

Patent metadata

Field	Value
Publication number	US-12421576-B2
Application number	US-202017121601-A
Country	US
Kind code	B2
Filing date	Dec 14, 2020
Priority date	Feb 1, 2017
Publication date	Sep 23, 2025
Grant date	Sep 23, 2025

Abstract

Some variations provide an aluminum (Al) alloy containing at least 0.1 at % zirconium (Zr) and/or at least 0.1 at % chromium (Cr), wherein the aluminum alloy is in the form of an additively manufactured object. Other variations provide an aluminum-containing powder comprising Al particles, Cr particles, and Zr particles, wherein at least some of the Cr particles as well as at least some of the Zr particles are physically and/or chemically assembled on surfaces of the Al particles, and wherein the aluminum-containing powder contains at least 0.1 at % Zr and at least 0.1 at % Cr. In this invention, the combination of surface functionalization and additive manufacturing has fundamentally created a new composition space of valuable aluminum alloys. The disclosed Al alloys are strong, thermally stable, and corrosion-resistant.

First claim

What is claimed is:

1. An aluminum (Al) alloy containing at least 0.4 at % zirconium (Zr) and at least 1.0 at % chromium (Cr) and from 0 to 0.6 wt % manganese (Mn), wherein said aluminum alloy is in the form of an additively manufactured object, and wherein said aluminum alloy is characterized by a yield strength of at least 450 MPa.

2. The aluminum alloy of claim 1 , wherein said aluminum alloy contains at least 0.5 at % Zr.

3. The aluminum alloy of claim 1 , wherein said aluminum alloy contains at least 2.0 at % Cr.

4. The aluminum alloy of claim 1 , wherein said aluminum alloy contains at least 1.0 at % Zr.

5. The aluminum alloy of claim 1 , wherein said aluminum alloy contains no manganese.

6. The aluminum alloy of claim 1 , wherein the Zr/Cr ratio is selected from 0.1 to 10.

7. The aluminum alloy of claim 6 , wherein said Zr/Cr ratio is selected from 0.2 to 2.

8. The aluminum alloy of claim 1 , wherein said aluminum alloy contains precipitated intermetallic Al—Cr particulates and/or precipitated intermetallic Al—Zr particulates.

9. The aluminum alloy of claim 1 , wherein said aluminum alloy further contains one or more elements selected from the group consisting of Cu, Mg, Zn, Li, Fe, Si, Ag, V, Nb, Ta, Ti, Hf, Mo, W, Sc, Y, Ca, Be, Sr, La, Ce, Re, Ru, Os, Co, Ni, Pd, Pt, Ir, Rh, Au, Cd, Sn, Bi, Pb, B, C, N, O, H, S, Er, Pr, Nd, Sm, Gd, Tb, Dy, Ho, Tm, Yb, and Lu.

10. The aluminum alloy of claim 1 , wherein said aluminum alloy is characterized by a Vickers Pyramid Number of at least 50.

11. The aluminum alloy of claim 1 , wherein said aluminum alloy is characterized by a Vickers Pyramid Number of at least 75.

12. The aluminum alloy of claim 1 , wherein said aluminum alloy is characterized by a tensile strength of at least 400 MPa.

13. The aluminum alloy of claim 1 , wherein said aluminum alloy is thermally stable at 300° C.

14. The aluminum alloy of claim 1 , wherein said additively manufactured object is selected from the group consisting of a structural part, a coating, an ingot, a sheet, a plate, a rod, a wire, and combinations thereof.

15. A structure containing said aluminum alloy of claim 14 .

16. The aluminum alloy of claim 1 , wherein said aluminum alloy does not contain scandium.

17. The aluminum alloy of claim 1 , wherein said aluminum alloy has an additively manufactured microstructure with a crystallographic texture that is not solely oriented in an additive-manufacturing build direction, and wherein said additively manufactured microstructure contains a plurality of dendrite layers having differing primary growth-direction angles with respect to each other.

18. The aluminum alloy of claim 1 , wherein said aluminum alloy contains equiaxed grains nucleated by said Cr and/or by said Zr.

19. An aluminum (Al) alloy containing at least 0.4 at % zirconium (Zr) and at least 1.0 at % chromium (Cr) and from 0 to 0.6 wt % manganese (Mn), wherein said aluminum alloy is in the form of a fabricated object, and wherein said aluminum alloy is characterized by a yield strength of at least 450 MPa.

20. The aluminum alloy of claim 19 , wherein said aluminum alloy contains at least 0.5 at % Zr.

21. The aluminum alloy of claim 19 , wherein said aluminum alloy contains at least 2.0 at % Cr.

22. The aluminum alloy of claim 19 , wherein said aluminum alloy contains at least 1.0 at % Zr.

23. The aluminum alloy of claim 19 , wherein said aluminum alloy contains no manganese.

24. The aluminum alloy of claim 19 , wherein the Zr/Cr ratio is selected from 0.1 to 10.

25. The aluminum alloy of claim 19 , wherein said aluminum alloy contains precipitated intermetallic Al—Cr particulates, precipitated intermetallic Al—Zr particulates, and/or precipitated intermetallic Zr—Cr particulates.

26. The aluminum alloy of claim 19 , wherein said aluminum alloy further contains one or more elements selected from the group consisting of Cu, Mg, Zn, Li, Fe, Si, Ag, V, Nb, Ta, Ti, Hf, Mo, W, Sc, Y, Ca, Be, Sr, La, Ce, Re, Ru, Os, Co, Ni, Pd, Pt, Ir, Rh, Au, Cd, Sn, Bi, Pb, B, C, N, O, H, S, Er, Pr, Nd, Sm, Gd, Tb, Dy, Ho, Tm, Yb, and Lu.

27. The aluminum alloy of claim 19 , wherein said fabricated object is selected from the group consisting of a structural part, a coating, an ingot, a sheet, a plate, a rod, a wire, and combinations thereof.

28. The aluminum alloy of claim 19 , wherein said aluminum alloy does not contain scandium.

29. The aluminum alloy of claim 19 , wherein said aluminum alloy contains equiaxed grains nucleated by said Cr and/or by said Zr.

30. An aluminum (Al) alloy containing at least 0.4 at % zirconium (Zr) and at least 1.0 at % chromium (Cr) and from 0 to 0.6 wt % manganese (Mn), wherein said aluminum alloy is in the form of an additively manufactured object or a fabricated object, and wherein said aluminum alloy is characterized by a yield strength of at least 450 MPa.

Assignees

• Hrl Lab Llc

Inventors

• Martin John H
• Laplant Darby
• Miller Julie

Classifications

• C22C1/0416

  Aluminium-based alloys · CPC title

• B33Y70/00

  Materials specially adapted for additive manufacturing · CPC title

• B33Y80/00

  Products made by additive manufacturing · CPC title

• C22C2202/00

  Physical properties · CPC title

• B33Y10/00

  Processes of additive manufacturing · CPC title