Positive electrode active material for lithium rechargeable battery, method of producing the same, and lithium rechargeable battery including the same

Patent metadata

Field	Value
Publication number	US-12418026-B2
Application number	US-202519077316-A
Country	US
Kind code	B2
Filing date	Mar 12, 2025
Priority date	Aug 24, 2018
Publication date	Sep 16, 2025
Grant date	Sep 16, 2025

Abstract

A surface of a LiCoO 2 -based positive electrode active material to have a rock salt crystal structure is provided. Specifically, a positive electrode active material for a lithium rechargeable battery is provided, including: a core particle containing lithium cobalt oxide doped with aluminum (Al); and a coating layer positioned on a surface of the core particle and containing a cobalt (Co)-based compound having a rock salt crystal structure. A method of producing the positive electrode active material is also provided using a solid-phase method. The positive electrode active material can be applied to a positive electrode, lithium rechargeable battery, battery module, battery pack, and the like.

First claim

The invention claimed is:

1. A positive electrode active material for a lithium rechargeable battery, comprising: a core particle comprising lithium cobalt oxide doped with aluminum (Al); and
a coating layer on a surface of the core particle, wherein the coating layer comprises a cobalt-based compound having a rock salt crystal structure.

2. The positive electrode active material for a lithium rechargeable battery of claim 1 , wherein:
the cobalt-based compound having a rock salt crystal structure is cobalt (II) oxide.

3. The positive electrode active material for a lithium rechargeable battery of claim 1 , wherein: the coating layer further comprises cobalt, lithium cobalt oxide, or a combination thereof.

4. The positive electrode active material for a lithium rechargeable battery of claim 1 , wherein: the coating layer has an island form in which the surface of the core particle is coated with the cobalt-based compound having a rock salt crystal structure.

5. The positive electrode active material for a lithium rechargeable battery of claim 1 , wherein: a weight ratio (core particle:coating layer) of the core particle to the coating layer is 1,000:0.2 to 1,000:10.

6. The positive electrode active material for a lithium rechargeable battery of claim 1 , wherein: a thickness of the coating layer is 1 to 50 nm.

7. The positive electrode active material for a lithium rechargeable battery of claim 1 , wherein: a D50 particle diameter of the coating particle is 12 to 25 μm.

8. The positive electrode active material for a lithium rechargeable battery of claim 7 , wherein: the core particle comprises a region in which a crystal structure of the lithium cobalt oxide doped with Al is a layered structure.

9. The positive electrode active material for a lithium rechargeable battery of claim 8 , wherein: the region is represented by the following Formula 1,
Li a Co (1x-y-z) Al x M1 y M2 z O 2   [Formula 1]

wherein M1 and M2 are each independently one selected from the group consisting of Ti, Mg, Zr, Ba, Ca, Ta, Nb, and Mo, and
a, x, y, and z are values satisfying 0.95≤a≤1.05, 0<x≤0.02, 0≤y≤0.02, and 0≤z≤0.02, respectively.

10. The positive electrode active material for a lithium rechargeable battery of claim 1 , wherein: when the battery is stored at a temperature range of 50 to 80° C. for one week and then discharged at a voltage of 4.4 V, a Co elution amount per 1 g of the positive electrode active material is 100 to 200 ppm/g.

11. The positive electrode active material for a lithium rechargeable battery of claim 1 , wherein: when the battery is stored at a temperature of 60° C. for one week and then discharged at a voltage of 4.5 V, a Co elution amount per 1 g of the positive electrode active material may be 1,500 to 2,500 ppm/g.

12. A lithium rechargeable battery, comprising:
a positive electrode containing the positive electrode active material of claim 1 ;
an electrolyte; and
a negative electrode.

Assignees

• Lg Energy Solution Ltd

Inventors

• Jo Chi Ho
• Hur Hyuck
• Kim Seul Ki
• Jung Wang Mo
• Han Gi Beom

Classifications

• H01M4/46

  Alloys based on magnesium or aluminium · CPC title

• H01M10/0525

  Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries · CPC title