Heterogeneous catalysts for the direct carbonylation of nitro aromatic compounds to isocyanates

Patent metadata

Field	Value
Publication number	US-12415780-B2
Application number	US-202217979955-A
Country	US
Kind code	B2
Filing date	Nov 3, 2022
Priority date	Apr 5, 2017
Publication date	Sep 16, 2025
Grant date	Sep 16, 2025

Abstract

A process for preparing an aromatic isocyanate by direct carbonylation of a nitro aromatic compound by reacting the nitro aromatic compound with carbon monoxide in the presence of a catalyst, characterized in that the catalyst contains a multi metallic material comprising one or more binary intermetallic phases of the general formula A x B y wherein:
A is one or more element selected from Ni, Ru, Rh, Pd, Ir, Pt and Ag, B is one or more element selected from Sn, Sb, Pb, Zn, Ga, In, Ge and As, x is in the range 0.1-10, y in is in the range 0.1-10.

First claim

The invention claimed is:

1. A catalyst for direct carbonylation of a nitroaromatic compound to a corresponding aromatic isocyanate, the catalyst containing a multi metallic material comprising one or more binary intermetallic phases of formula AxBy wherein:
A is Rh,
B is at least one element selected from the group consisting of Sn, Sb, Pb,
x is in the range 0.1-10,
y is in the range 0.1-10.

2. The catalyst according to claim 1 , wherein the multi metallic material comprises at least one component C, wherein component C contains A or B not being part of the intermetallic compound AxBy.

3. The catalyst according to claim 1 , wherein the multi metallic material comprises at least one component C, wherein component C contains at least one elements selected from the group consisting of O, N, C, H, Li, Na, K, Rb, Cs, Mg, Ca, Sr and Ba.

4. The catalyst according to claim 1 , wherein the multi metallic material comprises at least one binary intermetallic crystalline phases selected from the group consisting of RhPb, RhPb2, Rh4Pb5, Rh2Sn, RhSn, RhSn2, RhSn4, Rh2Sb, RhSb, RhSb2, RhSb3.

5. The catalyst according to claim 4 , wherein the multimetallic material comprises at least one binary intermetallic crystalline phases selected from the group consisting of RhPb, RhPb2, RhSb, Rh2Sb, RhSb2 and Rh2Sn.

6. The catalyst according to claim 1 wherein the multi metallic material is deposited on a carrier material.

7. A process for the production of a catalyst as defined in claim 6 comprising steps (i) to (iv):
(i) providing one or more precursors for elements A and B and optionally component C in the form of a solution;
(ii) depositing the metal precursors on a support material to form a composite material;
(iii reductive treatment of the composite material;
(iv) thermal treatment of the composite material.

8. The process according to claim 7 , wherein the solution comprises one or more solvents selected from the group consisting of water, alcohols, polyols, acids and bases.

9. The process according to claim 7 comprising the steps:
(iii) contacting the support material containing the metal precursors with one or more of reducing agents in solid, liquid or gaseous form selected from alcohols, hydrocarbons, amines, polyols, Zn-powder, H 2 , CO, CH 4 and C 2 H 4 , and
(iv) reducing the support material containing the metal precursors by thermal reduction under chemically inert conditions.

10. The process according to claim 9 , wherein step (iii) and (iv) are carried out in one single step.

Assignees

• Basf Se

Inventors

• Titlbach Sven
• Kuschel Andreas
• Lizandara Carlos
• Schunk Stephan A
• Rother Joerg
• Bechtel Juergen
• Drebov Nedko Stefanov
• Maixner Stefan
• Hinrichs Matthias
• Halabi Mohamed
• Mueller Imke Britta
• Fenyn Michaela

Classifications

• B01J37/16

  Reducing · CPC title

• B01J37/035

  Precipitation on carriers · CPC title

• B01J23/6445

  Antimony · CPC title

• B01J23/628

  with lead · CPC title

• B01J23/626

  with tin · CPC title