Wet accelerator, a method of preparing a wet accelerator and a method of producing a gypsum product

Patent metadata

Field	Value
Publication number	US-12398075-B2
Application number	US-202117761093-A
Country	US
Kind code	B2
Filing date	Feb 10, 2021
Priority date	Feb 25, 2020
Publication date	Aug 26, 2025
Grant date	Aug 26, 2025

Abstract

According to the present invention, there is provided a wet accelerator for use in the manufacture of a gypsum product, said wet accelerator comprising water, particles of calcium sulphate dihydrate and a stabiliser. Additionally, a method of preparing a wet accelerator and a method of producing a gypsum product are described.

First claim

The invention claimed is:

1. A wet accelerator for use in the manufacture of a gypsum product, said wet accelerator comprising
water,
particles of calcium sulphate dihydrate (CaSO 4 ·2H 2 O) wherein at least 50% of the particles of calcium sulphate dihydrate have a diameter of less than 5 μm,
and a stabiliser,
wherein said stabiliser comprises a soluble polymer of the formula;

wherein said stabiliser has an average molecular weight of between 500 and 10,000 g/mol inclusive;
wherein R 1 is selected from the group consisting of H and a cation; and
wherein m is any positive integer.

2. The wet accelerator of claim 1 , wherein the stabiliser has an average molecular weight of between 1000 and 5000 g/mol inclusive.

3. A wet accelerator for use in the manufacture of a gypsum product, said wet accelerator comprising
water,
particles of calcium sulphate dihydrate (CaSO 4 ·2H 2 O) wherein at least 50% of the particles of calcium sulphate dihydrate have a diameter of less than 5 μm, and a stabiliser,
wherein said stabiliser comprises a soluble polymer of the formula;

wherein R 1 is selected from the group consisting of H and a cation;
wherein m is any positive integer; and

wherein particles of calcium sulphate dihydrate form at least 10 wt. % and at most 50 wt. % of the wet accelerator.

4. The wet accelerator of claim 3 , wherein R 1 is H.

5. The wet accelerator of claim 4 , wherein the first pK a of said stabiliser is larger than or equal to 4.

6. The wet accelerator of claim 3 , wherein the stabiliser is present in an amount of at least 0.01 wt. % relative to the dry weight of the particles of calcium sulphate dihydrate.

7. The wet accelerator of claim 3 , wherein the stabiliser is present in an amount of at least 0.05 wt. % relative to the dry weight of the particles of calcium sulphate dihydrate.

8. The wet accelerator of claim 3 , wherein the stabiliser is present in an amount up to 5 wt. % relative to the dry weight of the particles of calcium sulphate dihydrate.

9. The wet accelerator of claim 3 , wherein the particles of calcium sulphate dihydrate form at least 15 wt. % and at most 45 wt. % of the wet accelerator.

10. The wet accelerator of claim 3 , wherein particles of calcium sulphate dihydrate form at least 20 wt. % and at most 40 wt. % of the wet accelerator.

11. A wet accelerator for use in the manufacture of a gypsum product, said wet accelerator comprising
water,
particles of calcium sulphate dihydrate (CaSO 4 ·2H 2 O), wherein at least 60% of the particles of calcium sulphate dihydrate have a diameter of less than 5 μm
and a stabiliser,
wherein said stabiliser comprises a soluble polymer of the formula;

wherein R 1 is selected from the group consisting of H and a cation; and
wherein m is any positive integer.

12. The wet accelerator of claim 11 , wherein at least 70% of the particles of calcium sulphate dihydrate have a diameter of less than 5 μm.

13. A wet accelerator for use in the manufacture of a gypsum product, said wet accelerator comprising
water,
particles of calcium sulphate dihydrate (CaSO 4 ·2H 2 O) wherein at least 50% of the particles of calcium sulphate dihydrate have a diameter of less than 5 μm,
and a stabiliser,
wherein said stabiliser comprises a soluble polymer of the formula;

wherein R 1 is selected from the group consisting of H and a cation;
wherein m is any positive integer; and
wherein said particles of calcium sulphate dihydrate have a surface area of between 5 and 30 m 2 /g.

14. A method of preparing the wet accelerator of claim 3 , the method comprising:
providing particles of inorganic material with the composition CaSO 4 (X)H 2 O, where X is in the range 0≤X≤2,
adding water,
adding said stabiliser, and
wet milling said particles of inorganic material.

15. The method of claim 14 , wherein X is equal to 0.5.

16. The method of claim 14 , wherein the stabiliser is present in an amount of at least 0.01 wt. % relative to the dry weight of the inorganic material.

17. The method of claim 14 , wherein the step of adding said stabiliser occurs after the step of adding said water, and said wet milling step begins after the addition of said water and before the addition of said stabiliser.

18. A method of producing a gypsum product comprising:
providing a slurry comprising water and inorganic material, said inorganic material comprising at least one of calcium sulphate hemihydrate and calcium sulphate anhydrite, providing the wet accelerator of claim 3 ,
introducing said wet accelerator into said slurry in an amount of between 0.1 and 4 wt. % of said inorganic material relative to the total dry weight of the constituents of the slurry and of the accelerator, and
allowing said slurry to set.

19. A method of producing a gypsum product comprising:
providing a slurry comprising water and inorganic material, said inorganic material comprising at least one of calcium sulphate hemihydrate and calcium sulphate anhydrite,
providing the wet accelerator of claim 1 ,
introducing said wet accelerator into said slurry in an amount of between 0.1 and 4 wt. % of said inorganic material relative to the total dry weight of the constituents of the slurry and of the accelerator, and
allowing said slurry to set.

20. A method of producing a gypsum product comprising:
providing a slurry comprising water and inorganic material, said inorganic material comprising at least one of calcium sulphate hemihydrate and calcium sulphate anhydrite, providing the wet accelerator of claim 11 ,
introducing said wet accelerator into said slurry in an amount of between 0.1 and 4 wt. % of said inorganic material relative to the total dry weight of the constituents of the slurry and of the accelerator, and
allowing said slurry to set.

21. A method of producing a gypsum product comprising:
providing a slurry comprising water and inorganic material, said inorganic material comprising at least one of calcium sulphate hemihydrate and calcium sulphate anhydrite,
providing the wet accelerator of claim 11 ,
introducing said wet accelerator into said slurry in an amount of between 0.1 and 4 wt. % of said inorganic material relative to the total dry weight of the constituents of the slurry and of the accelerator, and
allowing said slurry to set.

Assignees

• Saint Gobain Placo

Inventors

• Montigny Benoit
• Nguyen Christine
• Catteau Charlotte

Classifications

• C08L33/02

  Homopolymers or copolymers of acids; Metal or ammonium salts thereof · CPC title

• C04B2103/10

  Accelerators; Activators · CPC title

• C04B40/0039

  Premixtures of ingredients · CPC title

• C04B28/16 Primary

  containing anhydrite {, e.g. Keene's cement} · CPC title

• C04B24/2641

  Polyacrylates; Polymethacrylates · CPC title