Hybrid lithium metal cell with ionic liquid integrated cathode

Patent metadata

Field	Value
Publication number	US-12388079-B2
Application number	US-202217963479-A
Country	US
Kind code	B2
Filing date	Oct 11, 2022
Priority date	Oct 11, 2022
Publication date	Aug 12, 2025
Grant date	Aug 12, 2025

Abstract

A method of manufacturing a calendered cathode structure for a hybrid lithium metal cell includes depositing a first cathode coating layer without ionic liquid onto a cathode current collector, depositing a second cathode coating layer with ionic liquid onto the first coating layer, and depositing a third cathode coating layer without ionic liquid onto the second coating layer. A calendaring process is then performed on the cathode structure comprising the cathode current collector with the first, second, and third coating layers thereon such that a predetermined thickness and porosity for the cathode structure is achieved while at the same time the ionic liquid is spread throughout the cathode electrode without reaching the cathode current collector.

First claim

What is claimed is:

1. A method of manufacturing a calendered cathode structure for a hybrid lithium metal cell, the method comprises:
forming a cathode structure by:
depositing a first precursor composition onto a cathode current collector to form a first cathode coating layer, the first precursor composition including a composite polymer electrolyte, a cathode active material, and one or more conductive additives without ionic liquid;
depositing a second precursor composition onto the first cathode coating layer to form a second cathode coating layer, the second precursor composition including the composite polymer electrolyte, the cathode active material, one or more conductive additives and an ionic liquid; and
depositing a third precursor composition onto the second cathode coating layer to form a third cathode coating layer, the third precursor composition including the composite polymer electrolyte, the cathode active material, and one or more conductive additives without ionic liquid;

performing a calendering process on the cathode structure to form a cathode electrode on the cathode current collector from the first cathode coating layer, the second cathode coating layer, and the third cathode coating layer by feeding the cathode structure through a nip formed by a pair of calendering rolls to form a calendered cathode structure, the calendering process being carried out such that:
a cathode electrode of the calendered cathode structure has a predetermined thickness and porosity; and
the ionic liquid from the second cathode coating layer is distributed throughout the cathode electrode.

2. The method of claim 1 , wherein the first precursor composition and the third precursor composition are a same composition.

3. The method of claim 1 , wherein the second precursor composition is similar as the first and the third except that the second precursor composition includes the ionic liquid.

4. The method of claim 1 , wherein the first precursor composition, the second precursor composition, and the third precursor composition each comprise a slurry.

5. The method of claim 1 , wherein the first cathode coating layer, the second cathode coating layer, and the third cathode coating layer each have a thickness before the calendering process in a range from 30-60 microns.

6. The method of claim 5 , wherein the cathode electrode of the calendered cathode structure has a thickness in a range from 20-120 microns.

7. The method of claim 1 , wherein the calendering process is carried out such that the ionic liquid is uniformly distributed throughout the cathode electrode without contacting the cathode current collector.

8. A method of manufacturing a hybrid lithium metal cell for a lithium battery, the method comprising:
forming a cathode structure by:
depositing a first precursor composition onto a cathode current collector to form a first cathode coating layer, the first precursor composition including a composite polymer electrolyte and a cathode active material without ionic liquid;
depositing a second precursor composition onto the first cathode coating layer to form a second cathode coating layer, the second precursor composition including the composite polymer electrolyte, the cathode active material and an ionic liquid; and
depositing a third precursor composition onto the second cathode coating layer to form a third cathode coating layer, the third precursor composition including the composite polymer electrolyte and the cathode active material without ionic liquid;

performing a calendering process on the cathode structure to form a cathode electrode on the cathode current collector from the first cathode coating layer, the second cathode coating layer, and the third cathode coating layer by feeding the cathode structure through a nip formed by a pair of calendering rolls to form a calendered cathode structure, the calendering process being carried out such that:
a cathode electrode of the calendered cathode structure has a predetermined thickness and porosity; and
the ionic liquid from the second cathode coating layer is distributed throughout the cathode electrode;

depositing an ionic liquid-incorporated composite polymer electrolyte onto the cathode electrode; and
attaching a lithium metal anode of an anode structure to the ionic liquid-incorporated composite polymer electrolyte, the anode structure including an anode current collector on a side of the anode structure opposite from the ionic liquid-incorporated composite polymer electrolyte.

9. The method of claim 8 , wherein the first precursor composition and the third precursor composition have a same formulation.

10. The method of claim 8 , wherein the first precursor composition, the second precursor composition, and the third precursor composition each comprise a slurry.

11. The method of claim 8 , wherein the first cathode coating layer, the second cathode coating layer, and the third cathode coating layer each have a thickness before the calendering process in a range from 30-60 microns.

12. The method of claim 11 , wherein the cathode electrode of the calendered cathode structure has a thickness in a range from 20-120 microns.

13. The method of claim 8 , wherein the calendering process is carried out such that the ionic liquid is uniformly distributed throughout the cathode electrode without contacting the cathode current collector.

14. The method of claim 8 , wherein the lithium metal anode comprises a lithium metal deposited on the current collector using a thin film deposition or screen printing using stabilized lithium powder.

15. The method of claim 8 , wherein the lithium metal anode is attached onto the ionic liquid-incorporated composite polymer electrolyte.

16. The method of claim 8 , wherein the ionic liquid-incorporated composite polymer electrolyte serves as a separator for the hybrid lithium metal cell.

17. A method of manufacturing a cathode structure for a hybrid lithium metal cell, the method comprises:
forming a cathode structure by:
depositing a first precursor composition onto a cathode current collector to form a first cathode coating layer, the first precursor composition including a composite polymer electrolyte, a cathode active material and one or more conductive additives without ionic liquid;
depositing a second precursor composition onto the first cathode coating layer to form a second cathode coating layer, the second precursor composition including the composite polymer electrolyte, the cathode active material, one or more conductive additives and an ionic liquid; and
depositing a third precursor composition onto the second cathode coating layer to form a third cathode coating layer, the third precursor composition including the composite polymer electrolyte, the cathode active material and one or more conductive additives without ionic liquid;

compressing the cathode structure to form a cathode electrode on the cathode current collector from the first cathode coating layer, the second cathode coating layer, and the third cathode coating layer,
wherein the compressing is carried out such that the ionic liquid is uniformly distributed throughout the cathode electrode.

18. The method of claim 17 , wherein the first cathode coating layer, the second cathode coating layer, and the third cathode coating layer each have a thickness before the compressing in a range from 30-60 microns.

19. The method of claim 17 , wherein the cathode electrode has a thickness in a range from 20-120 microns.

20. The method of c

Assignees

• Sakuu Corp

Inventors

• Thokchom Joykumar
• Modjtahedi Ali
• Meng Yongtao
• Upreti Aditya
• Tariq Muhammad

Classifications

• H01M4/0435

  Rolling or calendering · CPC title

• H01M4/0414

  by screen printing · CPC title

• H01M4/0404 Primary

  by coating on electrode collectors · CPC title

• H01M2004/028

  Positive electrodes · CPC title

• H01M10/052

  Li-accumulators · CPC title