Grain-oriented electrical steel sheet and manufacturing method of the same

Patent metadata

Field	Value
Publication number	US-12378676-B2
Application number	US-202017422401-A
Country	US
Kind code	B2
Filing date	Jan 16, 2020
Priority date	Jan 16, 2019
Publication date	Aug 5, 2025
Grant date	Aug 5, 2025

Abstract

This grain-oriented electrical steel sheet includes a steel sheet, an insulation coating disposed on the steel sheet, and a spinel present at a part on the steel sheet at an interface between the steel sheet and the insulation coating by being fitted into the insulation coating, in which an amount of the spinel is 5 to 50 mg/m 2 per unit area of a surface of the steel sheet.

First claim

The invention claimed is:

1. A grain-oriented electrical steel sheet comprising:
a steel sheet;
an insulation coating disposed on the steel sheet; and
a spinel formed on a part on the steel sheet at an interface between the steel sheet and the insulation coating, wherein the spinel protrudes from the steel sheet toward the insulation coating, wherein
an amount of the spinel is 5 to 50 mg/m 2 per unit area of a surface of the steel sheet, and
wherein the grain-oriented steel sheet does not contain a forsterite film.

2. A manufacturing method of a grain-oriented electrical steel sheet, which is a manufacturing method of the grain-oriented electrical steel sheet according to claim 1 , comprising:
an annealing separator applying process in which an annealing separator containing Al 2 O 3 and MgO is applied to a decarburization-annealed steel sheet;
a final annealing process in which final annealing is performed on the steel sheet;
a powder removing process in which a surplus annealing separator on a surface of the steel sheet after the final annealing process is removed; and
an insulation coating forming process in which the steel sheet after the powder removing process is coated with a coating liquid containing colloidal silica and is baked to form an insulation coating on the steel sheet, wherein
the Al 2 O 3 is formed of a mixed phase containing a κ phase and an α phase,
a BET specific surface area of the MgO is 5.0 m 2 /g or less, and
a proportion of a weight of the MgO in a total weight of the Al 2 O 3 and the MgO is 5 to 50%.

3. The manufacturing method of a grain-oriented electrical steel sheet according to claim 2 , wherein a proportion of the κ phase in the Al 2 O 3 is 5.0 to 50.0% by mass.

4. The manufacturing method of a grain-oriented electrical steel sheet according to claim 3 , wherein an application amount of the annealing separator in the annealing separator applying process is 5 to 20 g/m 2 .

5. The manufacturing method of a grain-oriented electrical steel sheet according to claim 2 , wherein an application amount of the annealing separator in the annealing separator applying process is 5 to 20 g/m 2 .

Assignees

• Nippon Steel Corp

Inventors

• Fujii Hiroyasu
• Takebayashi Seiki
• Ushigami Yoshiyuki
• Kataoka Takashi
• Okumura Shunsuke

Classifications

• C21D8/02

  during manufacturing of plates or strips (C21D8/12 takes precedence) · CPC title

• C22C38/06

  containing aluminium · CPC title

• C22C38/02

  containing silicon · CPC title

• C22C38/002

  containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60 · CPC title

• C22C38/001

  containing N · CPC title