Thermoset undercoating compositions compatible with free-radically cured overcoating for metal substrates

Patent metadata

Field	Value
Publication number	US-12371573-B2
Application number	US-202117998850-A
Country	US
Kind code	B2
Filing date	May 14, 2021
Priority date	May 15, 2020
Publication date	Jul 29, 2025
Grant date	Jul 29, 2025

Abstract

A thermoset undercoating composition for a food or beverage container or other packaging container, the thermoset undercoating composition comprising a binder polymer, an adhesion promoting additive comprising an aminoplast resin having at least one reactive group having an ethylenically unsaturated double bond that is reactive under free-radical curing conditions, an optional crosslinker configured to react with the binder polymer upon thermal curing of the thermoset undercoating composition, wherein the optional crosslinker preferably does not include groups that are reactive under free-radical curing conditions, and a liquid carrier.

First claim

What is claimed is:

1. A thermoset undercoating composition for a food or beverage container, the thermoset undercoating composition comprising:
a binder polymer;
an adhesion promoting additive comprising an aminoplast resin having at least one reactive group having an ethylenically unsaturated double bond that is reactive under free-radical curing conditions;
a crosslinker configured to react with the binder polymer upon thermal curing of the thermoset undercoating composition, wherein the crosslinker does not include groups that are reactive under free-radical curing conditions; and
a liquid carrier.

2. The thermoset undercoating composition of claim 1 , wherein the binder polymer comprises a polyether, a polyester, a polyolefin, an acrylic, a polyurethane, a polyamide, or a copolymer or mixture thereof, and wherein the binder polymer has a hydroxyl value of about 10 to about 150.

3. The thermoset undercoating composition of claim 2 , wherein the aminoplast resin is substantially non-reactive with the other ingredients of the thermoset undercoating composition during thermal curing.

4. The thermoset undercoating composition of claim 1 , wherein the aminoplast resin is derived from ingredients including an aldehyde (typically formaldehyde) and one or more of melamine, benzoguanamine, or urea.

5. The thermoset undercoating composition of claim 1 , wherein the ethylenically unsaturated double bond comprises a vinylic double bond.

6. The thermoset undercoating composition of claim 2 , wherein the aminoplast resin comprises a (meth)acrylated aminoplast resin optionally selected from one or more of a (meth)acrylated melamine resin, a (meth)acrylated benzoguanamine resin, or (meth)acrylated urea resin.

7. The thermoset undercoating composition of claim 1 , wherein the aminoplast resin comprises a (meth)acrylated melamine-formaldehyde resin.

8. The thermoset undercoating composition of claim 1 , wherein the aminoplast resin comprises at least one chemical group capable of undergoing self-crosslinking or crosslinking with the binder polymer or the crosslinker during thermal curing.

9. The thermoset undercoating composition of claim 2 , wherein the crosslinker is present and comprises at least one phenoplast resin, aminoplast resin that is chemically different from the adhesion promoting additive aminoplast resin, or blocked isocyanate resin.

10. The thermoset undercoating composition of claim 1 , wherein the thermoset undercoating composition, prior to curing, comprises a liquid carrier, and wherein the thermoset undercoating composition further comprises a pigment.

11. The thermoset undercoating composition of claim 5 , wherein the thermoset undercoating composition forms a white undercoating.

12. The thermoset undercoating composition of claim 11 , wherein the thermoset undercoating composition further comprises titanium oxide.

13. The thermoset undercoating composition of claim 1 , wherein ingredients of the thermoset undercoating composition, other than the adhesion promoting additive, are free of each of free-radical polymerizable double bonds, free-radical initiators, and substituents that would chemically react with the ethylenically unsaturated double bond of the adhesion promoting additive aminoplast resin under thermal curing conditions of up to 200 Celsius for up to 30 minutes.

14. The thermoset undercoating composition of claim 1 , wherein the thermoset undercoating composition comprises about 60 wt. % to about 99 wt. % of the binder polymer based on total resin solids in the undercoating composition and about 1 wt. % to about 40 wt. % of the the crosslinker based on total resin solids in the undercoating composition.

15. The thermoset undercoating composition of claim 2 , wherein the thermoset undercoating composition comprises about 0.05 wt. % to about 10 wt. % of the adhesion promoting additive aminoplast resin on a dry solids basis in the undercoating composition.

16. The thermoset undercoating composition of claim 6 , wherein the thermoset undercoating composition comprises about 0.05 wt. % to about 5 wt. % of the aminoplast resin on a dry solids basis in the undercoating composition.

17. The thermoset undercoating composition of claim 1 , wherein the thermoset undercoating composition comprises about 0.5 wt. % to about 1 wt. % of the aminoplast resin on a dry solids basis in the undercoating composition.

18. A method of forming a packaging article, the method comprising the steps of:
coating at least a portion of a metal substrate for a food or beverage container with a thermoset undercoating composition, the thermoset undercoating composition comprising:
a binder polymer;
a crosslinker configured to react with the binder polymer upon thermal curing of the thermoset undercoating composition, wherein the crosslinker does not include groups that are reactive under free-radical curing conditions; and
an adhesion promoting additive comprising an aminoplast resin having at least one reactive group having an ethylenically unsaturated double bond that is reactive under free-radical curing conditions;

thermally drying or curing the thermoset undercoating composition to form a cured thermoset undercoating on the metal substrate;
coating the dried or cured thermoset undercoating with a second coating composition comprising at least one of a free-radically curable composition or a thermally curable composition; and
curing the second coating composition to form at least one additional coating on the thermoset undercoating.

19. The method of claim 18 , wherein:
the metal substrate comprises aluminum or steel that has an average thickness of about 0.14 millimeters (mm) to about 0.50 mm,
the thermoset undercoating is on the metal substrate and the at least one additional coating is directly on the thermoset undercoating;
the at least one additional coating is a decorative overcoat comprising a free-radically curable or free-radically cured ink composition; and
the cured multi-layer coating system has an overall average coating thickness of about 3 μm to about 40 μm.

20. A packaging article for a food or beverage container, the article comprising:
a container, or a portion thereof, comprising:
a metal substrate; and
a multi-layer coating system applied on at least a portion of the metal substrate, the multi-layer coating system comprising:
(i) a dried or cured thermoset undercoating derived from a thermoset undercoating composition, the thermoset undercoating composition comprising:
a binder polymer;
a crosslinker configured to react with the binder polymer upon thermal curing of the thermoset undercoating composition, wherein the crosslinker does not include groups that are reactive under free-radical curing conditions; and
an adhesion promoting additive comprising an aminoplast resin having at least one reactive group having an ethylenically unsaturated double bond that is reactive under free-radical curing conditions; and

(ii) at least one additional coating on the dried or cured thermoset undercoating, the at least one additional coating derived from a second coating composition comprising at least one of a free-radically curable composition or a thermally curable composition.

Assignees

• Swimc Llc

Inventors

• Turgis Jean-Dominique
• Quereau Marie Edith

Classifications

• C09D167/00

  Coating compositions based on polyesters obtained by reactions forming a carboxylic ester link in the main chain (based on polyester-amides C09D177/12; based on polyester-imides C09D179/08); Coating compositions based on derivatives of such polymers · CPC title

• B65D25/34

  Coverings or external coatings (of containers made by folding or erecting blanks made of paper B65D5/62; covering or external coating for bottles or jars not otherwise provided for B65D23/08; wrappers B65D65/00) · CPC title

• B65D25/14

  Linings or internal coatings (of containers made by folding or erecting blanks made of paper B65D5/56 {; linings for domestic water storage heaters F24H1/183}) · CPC title

• C09D7/61

  inorganic · CPC title

• C09D7/65

  macromolecular (C09D7/41-C09D7/48 take precedence) · CPC title