Hardfaced metal surface and method of manufacture

Patent metadata

Field	Value
Publication number	US-12366133-B2
Application number	US-202217750066-A
Country	US
Kind code	B2
Filing date	May 20, 2022
Priority date	Apr 6, 2018
Publication date	Jul 22, 2025
Grant date	Jul 22, 2025

Abstract

An apparatus is disclosed as including a first material volume with at least a hardened portion and a second material volume that includes at least two layers. The first material volume is composed of at least a hardenable alloy of steel. The at least two layers is located adjacent to a first surface comprising the hardened portion of the first material volume. The at least two layers includes a first layer composed of at least a ductile low-carbon alloy of steel and a second layer composed of at least a cobalt-based hardfacing over the first layer. The apparatus is applicable in preparing shear ram blocks and shear ram blades to provide a hardened blade edge with an adjacent hardfacing surface.

First claim

What is claimed is:

1. A shear ram blade comprising:
a material volume comprising a hardenable alloy of steel as a base of the shear ram blade and comprising a heat-treated portion of the hardenable alloy of steel as an edge of the shear ram blade, the heat-treated portion of a different hardness than the base; and
at least two layers welded over the base with the edge exposed to form an overlay.

2. The shear ram blade of claim 1 , wherein the overlay is located adjacent to a surface of the heat-treated portion.

3. The shear ram blade of claim 1 , further comprising:
at least a low-carbon alloy of steel forming a first of the at least two layers and a cobalt-based hardfacing over the first of the at least two layers to form a second of the at least two layers.

4. The shear ram blade of claim 1 , further comprising:
CrMoV Steel, NiCrMo Steel, or CrNiMo Steel as the material volume.

5. The shear ram blade of claim 1 , further comprising:
the heat-treated portion formed from an induction hardening process applied to the hardenable alloy of steel.

6. The shear ram blade of claim 1 , further comprising:
a transition zone formed adjacent to the heat-treated portion and in the material volume.

7. A blow-out preventer (BOP) stack assembly comprising:
a shear ram housing comprising at least one upper ram shear block, at least one lower ram shear block, and at least one lower shear blade that is comprised of a material volume comprising a hardenable alloy of steel as a base of the shear ram blade and comprising a heat-treated portion of the hardenable alloy of steel as an edge of the shear ram blade, the heat-treated portion of a different hardness than the base.

8. The BOP stack assembly of claim 7 , further comprising:
at least two layers to form an overlay located adjacent to a surface of the heat-treated portion of the at least one lower shear blade.

9. The BOP stack assembly of claim 8 , further comprising:
at least a low-carbon alloy of steel forming a first of the at least two layers and a cobalt-based hardfacing over the first of the at least two layers to form a second of the at least two layers of the at least one lower shear blade.

10. The BOP stack assembly of claim 7 , further comprising:
CrMoV Steel, NiCrMo Steel, or CrNiMo Steel as the material volume of the at least one lower shear blade.

11. The BOP stack assembly of claim 7 , further comprising:
the heat-treated portion formed from an induction hardening process applied to the hardenable alloy of steel of the at least one lower shear blade.

12. The BOP stack assembly of claim 7 , further comprising:
a transition zone formed adjacent to the heat-treated portion and in the material volume of the at least one lower shear blade.

13. The BOP stack assembly of claim 7 , further comprising:
the at least one lower ram shear block as a unibody structure comprising the at least one lower shear blade, and wherein the at least one upper ram shear block is a unibody structure comprising the at least one upper shear blade.

14. The BOP stack assembly of claim 7 , further comprising:
the at least one lower shear blade attached to the at least one lower ram shear block and the at least one upper shear blade attached to the at least one upper ram shear block.

15. A method for preparing a shear ram blade comprising a hardenable alloy of steel as a base and comprising a heat-treated portion of the hardenable alloy of steel as an edge, the method comprising:
providing an overlay over the base with the edge exposed;
heat-treating the shear ram blade till the heat-treated portion of the hardenable alloy of steel has a predetermined different hardness than the base; and
welding at least two layers over the base to form the overlay.

16. The method of claim 15 , further comprising:
forming CrMoV Steel, NiCrMo Steel, or CrNiMo Steel into a shape of a shear ram blade to be the base of the shear ram blade.

17. The method of claim 15 , further comprising:
welding at least a low-carbon alloy of steel to form a first of the at least two layers; and
welding a cobalt-based hardfacing as a second of the at least two layers that is over the first of the at least two layers.

18. The method of claim 15 , further comprising:
performing induction hardening as part of the heat-treating of the shear ram blade.

19. The method of claim 15 , further comprising:
monitoring the shear ram blade for a transition zone formed adjacent to the heat-treated portion, wherein the transition zone represents completion of the heat-treating of the shear ram blade.

Assignees

• Hydril Usa Distrib Llc

Inventors

• Gamble Jamie Clay
• Larson Eric
• Baker Brian
• Singh Daya
• Incavo Joseph
• Miller William
• Newbury Melissa
• Reinmuller Mark

Classifications

• E21B19/00

  Handling rods, casings, tubes or the like outside the borehole, e.g. in the derrick; Apparatus for feeding the rods or cables · CPC title

• E21B33/06 Primary

  Blow-out preventers {, i.e. apparatus closing around a drill pipe, e.g. annular blow-out preventers (rotating blow-out preventers E21B33/085)} · CPC title

• B32B15/013 Primary

  one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium · CPC title

• C21D1/42

  Induction heating · CPC title

• C22F1/10

  of nickel or cobalt or alloys based thereon · CPC title