High-strength high-toughness and wear-resistant composite steel plate and manufacturing method therefor

Patent metadata

Field	Value
Publication number	US-12359272-B2
Application number	US-201816766939-A
Country	US
Kind code	B2
Filing date	Nov 21, 2018
Priority date	Nov 28, 2017
Publication date	Jul 15, 2025
Grant date	Jul 15, 2025

Abstract

Disclosed is a high-strength high-toughness and wear-resistant composite steel plate, comprising a substrate layer and a composite layer of which a single side or double sides are composited on the substrate layer. The substrate layer is a carbon steel layer and the composite layer is a ultra-high manganese steel layer with a content of Mn element in the composite layer being about 16.00-25.00 wt. %. Further disclosed is a manufacturing method for making the high-strength high-toughness and wear-resistant composite steel plate. With high strength and hardness, high wear resistance and high toughness, the high-strength high-toughness and wear-resistant composite steel plate has excellent comprehensive performance.

First claim

What is claimed is:

1. A composite steel plate, comprising a substrate layer and a compounding layer compounded on both surfaces of the substrate layer, or consisting of a substrate layer and a compounding layer compounded on one surface of the substrate layer, wherein the substrate layer is a carbon steel layer, and the compounding layer is an ultra-high manganese steel layer, wherein the compounding layer has a Mn element content of 16.00-25.00 wt %, wherein
the substrate layer comprises a microstructure of martensite and residual austenite and comprises the following chemical elements in mass percentage: C: 0.10-0.25 wt. %; Si: 0.10-1.00 wt. %; Mn: 0.40-2.00 wt. %; Cr: 0.01-2.00 wt. %; Mo: 0.01-1.00 wt. %; Ni: 0.01-2.00 wt. %; Nb: 0.001-0.080 wt. %; B: 0.0005-0.0040 wt. %; Al: 0.010-0.080 wt. %; and the balance of Fe and other unavoidable impurities, and has a tensile strength of ≥1200 MPa, a yield strength of ≥1000 MPa, an elongation of ≥14%, a Brinell hardness of ≥400 HB, and a Charpy V-notch longitudinal impact energy at −40° C. of ≥60 J, and
the compounding layer comprises a microstructure of austenite and consists of the following chemical elements in mass percentage: C: 1.30-1.80 wt. %; Si: 0.20-1.50 wt. %; Mn: 16.00-25.00 wt. %; Cr: 0.01-3.00 wt. %; Mo: 0.01-1.00 wt. %; Ti: ≤0.060%; Al: 0.010-0.080 wt. %; and the balance of Fe and other unavoidable impurities, and has a tensile strength of ≥500 MPa, an elongation of ≥12%, a Brinell hardness of ≥170 HB, and a Charpy U-notch longitudinal impact energy at −40° C. of ≥40 J, and
wherein the composite steel plate is obtained by a rolling compounding process with a rolling-start temperature of 1120-1220° C. and a rolling-end temperature of 1050-1200° C.

2. The composite steel plate of claim 1 , wherein the substrate layer further comprises at least one of the following chemical elements: 0<V≤0.080 wt. % and 0<Ti≤0.060 wt. %.

3. The composite steel plate of claim 1 , wherein the chemical elements of the substrate layer further meet at least one of 0.20%≤(Cr/5+Mn/6+50B)≤0.55%, 0.10%≤(Mo/3+Ni/5+2Nb)≤0.42% and 0.02%≤(Al+Ti)≤0.12%.

4. A method for manufacturing the composite steel plate of claim 1 , wherein the method comprises the following steps:
(1) Preparing a substrate layer slab and a compounding layer slab;
(2) Assembling the slabs;
(3) Heating: heating temperature: 1150-1250° C., holding time: 1-3 hours;
(4) Compounding rolling: rolling-start temperature: 1120-1220° C., rolling-end temperature: 1050-1200° C., reduction rate being controlled at ≥50%; and
(5) Post-rolling cooling.

5. The method for manufacturing the composite steel plate according to claim 4 , wherein water cooling is used in step (5) to cool the composite steel plate to room temperature−300° C. at a cooling rate of ≥10° C./s.

6. The method for manufacturing the composite steel plate according to claim 4 , wherein air cooling is used in step (5) to cool the composite steel plate to room temperature, followed by step (6): offline quenching.

7. The method for manufacturing the composite steel plate according to claim 6 , wherein, in step (6), quenching temperature is 1050-1100° C., and holding time is (1.5×t) min, where t represents plate thickness in mm.

Assignees

• Baoshan Iron & Steel

Inventors

• Li Hongbin
• Yuan Xiangqian
• Jiao Sihai
• Yao Liandeng
• Liang Xiaojun

Classifications

• C21D8/02

  during manufacturing of plates or strips (C21D8/12 takes precedence) · CPC title

• C22C38/54

  with boron · CPC title

• C22C38/50

  with titanium or zirconium · CPC title

• C22C38/48

  with niobium or tantalum · CPC title

• C22C38/46

  with vanadium · CPC title