Method for halogenating isobutene-isoprene copolymer

Patent metadata

Field	Value
Publication number	US-12344699-B2
Application number	US-202117913325-A
Country	US
Kind code	B2
Filing date	Sep 15, 2021
Priority date	Sep 18, 2020
Publication date	Jul 1, 2025
Grant date	Jul 1, 2025

Abstract

The present invention relates to a method for halogenating an isobutene-isoprene copolymer by using an organic hypochlorite. By using the method of the present invention, a hydrogen halide byproduct may be rapidly recycled into a halogenating agent and reused. As a result, a halogenated isobutene-isoprene copolymer having the high content of secondary allyl halogen functional groups may be prepared by increasing the participation ratio of the halogenating agent in reaction and suppressing the rearrangement of the secondary allyl halogen functional groups. The halogenated isobutene-isoprene copolymer prepared according to the present invention may be effectively used in the crosslinking reaction with other rubber, and is industrially useful.

First claim

The invention claimed is:

1. A method for halogenating an isobutene-isoprene copolymer, the method comprising:
(S1) preparing a mixture solution comprising an isobutene-isoprene copolymer, an organic hypochlorite and a hydrocarbon solvent; and
(S2) reacting the mixture solution with a halogenating agent to halogenate the isobutene-isoprene copolymer.

2. The method for halogenating an isobutene-isoprene copolymer according to claim 1 , wherein the organic hypochlorite is a compound represented by the following Formula 1:

in Formula 1,
R is an alkyl group of 1 to 10 carbon atoms.

3. The method for halogenating an isobutene-isoprene copolymer according to claim 2 , wherein, in Formula 1,
R is an alkyl group of 4 to 10 carbon atoms, and
carbon adjacent to an oxygen atom in Formula 1 is tertiary carbon.

4. The method for halogenating an isobutene-isoprene copolymer according to claim 2 , wherein, in Formula 1, R is tert-butyl, tert-pentyl, 2-methylpentan-2-yl, 2,3-dimethylbutan-2-yl, 2-methylhexan-2-yl, 2,4-dimethylpentan-2-yl, 2,3-dimethylpentan-2-yl, or 2,3,3-trimethylbutan-2-yl.

5. The method for halogenating an isobutene-isoprene copolymer according to claim 1 , wherein step (S1) comprises mixing the isobutene-isoprene copolymer, the organic hypochlorite and the hydrocarbon solvent and stirring for 10 seconds to 60 minutes.

6. The method for halogenating an isobutene-isoprene copolymer according to claim 1 , wherein the mixture solution comprises 15 wt % or less of water based on a total weight of the mixture solution.

7. The method for halogenating an isobutene-isoprene copolymer according to claim 1 , wherein the organic hypochlorite is 0.1 to 2.0 equivalents based on 1 equivalent of the halogenating agent.

8. The method for halogenating an isobutene-isoprene copolymer according to claim 1 , wherein the halogenating agent is 0.2 to 0.8 equivalents based on 1 equivalent of the isobutene-isoprene copolymer.

9. The method for halogenating an isobutene-isoprene copolymer according to claim 1 , further comprising (S3) reacting with a basic material after step (S2).

10. The method for halogenating an isobutene-isoprene copolymer according to claim 9 , wherein step (S3) is performed at 10 to 40° C. for 3 minutes to 30 minutes.

11. The method for halogenating an isobutene-isoprene copolymer according to claim 1 , wherein the halogenating agent is a bromine molecule (Br 2 ) or a chlorine molecule (Cl 2 ).

12. The method for halogenating an isobutene-isoprene copolymer according to claim 1 , wherein the mixture solution further comprises an alcohol.

13. The method for halogenating an isobutene-isoprene copolymer according to claim 12 , wherein the alcohol is one or more selected from the group consisting of methanol, ethanol, propanol, isopropyl alcohol, 1-butanol, 2-butanol and tert-butanol.

14. The method for halogenating an isobutene-isoprene copolymer according to claim 12 , wherein the alcohol is 0.1 to 20 parts by weight based on 100 parts by weight of the hydrocarbon solvent.

15. The method for halogenating an isobutene-isoprene copolymer according to claim 12 , wherein the alcohol is injected into the mixture solution in step (S1) before initiating halogenation.

16. The method for halogenating an isobutene-isoprene copolymer according to claim 1 , wherein the halogenation in step (S2) is performed at 10 to 80° C. for 10 seconds to 60 minutes.

Assignees

• Lg Chemical Ltd

Inventors

• Baek Jong Yeol
• Jeong Moon Gon
• Choi Gyeong Shin
• Kim Won Hee

Classifications

• C08F236/08

  Isoprene · CPC title

• C08F210/10

  Isobutene · CPC title

• C08F8/22

  by reaction with free halogens · CPC title

• C08F8/24 Primary

  Haloalkylation · CPC title

• C08F8/20 Primary

  Halogenation · CPC title