Method for producing a catalytically active multi-element oxide containing the elements Mo, W, V and Cu

Patent metadata

Field	Value
Publication number	US-12343708-B2
Application number	US-202117918345-A
Country	US
Kind code	B2
Filing date	Apr 12, 2021
Priority date	Apr 21, 2020
Publication date	Jul 1, 2025
Grant date	Jul 1, 2025

Abstract

A process for producing a catalytically active multielement oxide comprising the elements Mo, W, V and Cu, wherein at least one source of the elemental constituents W of the multielement oxide is used to produce an aqueous solution, the resultant aqueous solution is admixed with sources of the elemental constituents Mo and V of the multielement oxide, drying of the resultant aqueous solution produces a powder P, the resultant powder P is optionally used to produce geometric shaped precursor bodies, and the powder P is or the geometric shaped precursor bodies are subjected to thermal treatment to form the catalytically active composition, wherein the aqueous solution used for drying comprises from 1.6% to 5.0% by weight of W and from 7.2% to 26.0% by weight of Mo, based in each case on the total amount of aqueous solution.

First claim

The invention claimed is:

1. A process for producing a catalytically active multielement oxide comprising the elements Mo, W, V, Cu and optionally Sb, wherein the ratio of the elements conforms to the general formula (I)
Mo12WaVbCucSbd   (I)

where
a=0.4 to 5.0,
b=1.0to 6.0,
c=0.2 to 1.8 and
d=0.0 to 2.0,
and the molar proportion of the element Mo in the total amount of all non-oxygen elements is from 5 to 95 mol %, which comprises
a) using at least one source of the elemental constituents W of the multielement oxide to produce an aqueous solution or aqueous suspension,
b) admixing the aqueous solution or aqueous suspension obtained in a) with sources of the elemental constituents Mo, V and optionally Sb of the multielement oxide,
c) admixing the aqueous solution or aqueous suspension obtained in b) with sources of the elemental constituents Cu and optionally Sb of the multielement oxide,
d) drying the aqueous solution or aqueous suspension obtained in c) and optionally comminuting to produce a powder P,
e) optionally using the powder P obtained in d), optionally with addition of one or more shaping auxiliaries and after homogeneous mixing, to obtain geometric shaped precursor bodies from the resulting mixture, and
f) subjecting the powder P obtained in d) or the geometric shaped precursor bodies obtained in e) to thermal treatment to form the catalytically active multielement oxide,
wherein the aqueous solution or aqueous suspension used in d) comprises from 1.6% to 5.0% by weight of W and from 7.2% to 26.0% by weight of Mo, based in each case on the total amount of aqueous solution or aqueous suspension.

2. The process according to claim 1 , wherein the aqueous solution or aqueous suspension obtained in c) is spray-dried in d).

3. The process according to claim 1 , wherein the stoichiometric coefficient a of the element W in the general formula (I) is from 1.0 to 2.0 and/or the stoichiometric coefficient b of the element V in the general formula (I) is from 2.5 to 4.5.

4. The process according to claim 1 , wherein the aqueous solution or aqueous suspension used in d) comprises from 2.3% to 3.8% by weight of W and/or comprises from 11.5% to 15.0% by weight of Mo, based in each case on the total amount of aqueous solution or aqueous suspension.

5. The process according to claim 1 , wherein water-soluble salts are used as the source of the elemental constituents Mo, V and/or W.

6. The process according to claim 1 , wherein the stoichiometric coefficient c of the element Cu in the general formula (I) is from 0.8 to 1.2.

7. The process according to claim 1 , wherein admixing is effected in b) or in c) with at least one source of the elemental constituents Sb of the multielement oxide.

8. A catalytically active multielement oxide comprising the elements Mo, W, V, Cu and optionally Sb, wherein the ratio of the elements conforms to the general formula (I)
Mo 12 W a V b Cu c Sb d   (I)

where
a=0.4 to 5.0,
b=1.0 to 6.0,
c=0.2 to 1.8 and
d=0.0 to 2.0,
and the molar proportion of the element Mo in the total amount of all non-oxygen elements is from 5 to 95 mol %, obtained by the process of claim 1 , wherein the BET surface area of the catalytically active multielement oxide is from 16 to 35 m 2 /g.

9. The catalytically active multielement oxide according to claim 8 , wherein the stoichiometric coefficient a of the element W in the general formula (I) is from 1.0 to 2.0 and/or the stoichiometric coefficient b of the element V in the general formula (I) is from 2.5 to 4.5.

10. The catalytically active multielement oxide according to claim 8 , wherein the BET surface area of the catalytically active multielement oxide is from 19 to 26 m 2 /g.

11. The catalytically active multielement oxide according to claim 8 , wherein the stoichiometric coefficient c of the element Cu in the general formula (I) is from 0.8 to 1.2.

12. The catalytically active multielement oxide according to claim 8 , wherein the catalytically active multielement oxide comprises the element Sb.

13. A process for producing an eggshell catalyst, which comprises applying a catalytically active multielement oxide according to claim 8 and optionally binder to the outer surface of a geometric shaped support body.

14. An eggshell catalyst consisting of a geometric shaped support body and the catalytically active multielement oxide according to claim 8 and optionally binder applied to the outer surface of the geometric shaped support body.

15. A process for preparing acrylic acid by gas phase catalytic oxidation of acrolein over a fixed catalyst bed, wherein the fixed catalyst bed comprises the catalytically active multielement oxide according to claim 8 .

Assignees

• Basf Se

Inventors

• Amakawa Kazuhiko
• Parishan Samira
• Walsdorff Christian
• Hubach Patrick
• Weinland Tobias

Classifications

• B01J35/613 Primary

  10-100 m2/g · CPC title

• C07C2523/888

  Tungsten · CPC title

• C07C51/235

  of —CHO groups or primary alcohol groups · CPC title

• B01J37/08

  Heat treatment {(B01J37/0009, B01J37/0018 take precedence)} · CPC title

• B01J37/0045

  Drying a slurry, e.g. spray drying · CPC title