Application of nano layered double hydroxide in cartilage regeneration and preparation thereof

Patent metadata

Field	Value
Publication number	US-12337076-B2
Application number	US-202418822374-A
Country	US
Kind code	B2
Filing date	Sep 2, 2024
Priority date	May 16, 2022
Publication date	Jun 24, 2025
Grant date	Jun 24, 2025

Abstract

Application methods of a nano layered double include: applying the nano layered double hydroxide in promoting chondrogenic differentiation of human umbilical cord-derived mesenchymal stem cells, and applying the nano layered double hydroxide in preparing drugs for promoting cartilage regeneration, promoting intervertebral disc repair, or treating intervertebral disc degeneration. Compared to human umbilical cord-derived mesenchymal stem cells without an addition of the nano layered double hydroxide, the human umbilical cord-derived mesenchymal stem cells with the addition of the nano layered double hydroxide have a better and faster ability to differentiate into chondrocytes and broad application prospects.

First claim

What is claimed is:

1. A method for preparing a nano layered double hydroxide (LDH), comprising:
step 1, preparing 60 milliliters (mL) salt solution by using 6 millimoles (mmol) magnesium nitrate and 2 mmol ferric nitrate, wherein a mole ratio of magnesium ion to ferric ion is 3:1;
step 2, preparing 40 ml of 0.016 moles per liter (M) sodium hydroxide solution by using double-distilled water with carbon dioxide removed as a solvent;
step 3, adding the 60 mL salt solution of step 1 to the 40 ml of 0.016 M sodium hydroxide solution of step 2 with stirring while continuously supplying nitrogen gas to obtain a first suspension;
step 4, transferring the first suspension to a hydrothermal synthesis reactor and then heating the first suspension at 100 degrees Celsius (C) for 18 hours to obtain a second suspension;
step 5, centrifuging the second suspension at 20000 gravitational accelerations (g) for 15 minutes (min) to obtain a product, washing the product twice with double-distilled water with carbon dioxide removed to obtain a gel-like material, and storing the gel-like material in a refrigerator at 4° C.; and
step 6, drying the gel-like material of step 5 in a vacuum drying oven to obtain the nano LDH; and
wherein the nano LDH is used to promote chondrogenic differentiation of human umbilical cord-derived mesenchymal stem cells.

2. A method for preparing a nano LDH, comprising:
step 1, preparing 60 mL salt solution by using 6 millimoles (mmol) magnesium nitrate and 2 mmol ferric nitrate, wherein a mole ratio of magnesium ion to ferric ion is 3:1;
step 2, preparing 40 ml of 0.016 moles per liter (M) sodium hydroxide solution by using double-distilled water with carbon dioxide removed as a solvent;
step 3, adding the 60 mL salt solution of step 1 to the 40 mL of 0.016 M sodium hydroxide solution of step 2 with stirring while continuously supplying nitrogen gas to obtain a first suspension;
step 4, transferring the first suspension to a hydrothermal synthesis reactor and then heating the first suspension at 100 degrees Celsius (° C) for 18 hours to obtain a second suspension;
step 5, centrifuging the second suspension at 20000 g for 15 min to obtain a product, washing the product twice with double-distilled water with carbon dioxide removed to obtain a gel-like material, and storing the gel-like material in a refrigerator at 4° C.; and
step 6, drying the gel-like material of step 5 in a vacuum drying oven to obtain the nano LDH; and
wherein the nano LDH is used to prepare drugs for promoting cartilage regeneration.

Assignees

• Univ Tongji

Inventors

• Zhu Rongrong
• Cheng Liming

Classifications

• A61L2430/06

  for cartilage reconstruction, e.g. meniscus · CPC title

• A61L2400/12

  Nanosized materials, e.g. nanofibres, nanoparticles, nanowires, nanotubes; Nanostructured surfaces · CPC title

• A61L27/3834 Primary

  Cells able to produce different cell types, e.g. hematopoietic stem cells, mesenchymal stem cells, marrow stromal cells, embryonic stem cells · CPC title

• A61L27/047 Primary

  Other specific metals or alloys not covered by A61L27/042 - A61L27/045 or A61L27/06 · CPC title

• C01P2004/22

  with a polygonal circumferential shape · CPC title