Compositions and methods for well cementing

Patent metadata

Field	Value
Publication number	US-12325822-B2
Application number	US-202418419997-A
Country	US
Kind code	B2
Filing date	Jan 23, 2024
Priority date	Dec 10, 2021
Publication date	Jun 10, 2025
Grant date	Jun 10, 2025

Abstract

The effectiveness of expansive cement systems may be diluted when, during a well cementing operation, commingling takes place between the cement slurry and a spacer fluid, a drilling fluid, or both. Incorporating expansive agents in the spacer fluid or drilling fluid may reduce or negate the loss of expansion at the cement slurry/spacer interface or the cement slurry/drilling fluid interface, thereby promoting zonal isolation throughout the cemented interval.

First claim

The invention claimed is:

1. A composition, comprising:
an aqueous cement slurry; and
a non-aqueous additive comprising:
a suspension of an expanding agent comprising calcium oxide or a mixture of calcium oxide and calcined magnesium oxide; and
a viscosifying agent comprising hydrophobically modified biopolymers, the hydrophobically modified biopolymers comprising:
acetone-formaldehyde-sodium-bisulfate polymer; and
D-Glucopyranuronic acid, polymer with 6-deoxy-L-mannose, D-glucose, and D-mannose, calcium potassium sodium salt.

2. The composition of claim 1 , wherein the non-aqueous additive further comprises a hydrocarbon liquid, and wherein the hydrocarbon liquid is present in the non-aqueous additive at a concentration between 1 wt % and 99 wt %.

3. The composition of claim 2 , wherein the hydrocarbon liquid comprises alkanes, alkenes, alkynes, cycloalkanes, aromatic hydrocarbons, natural gas liquids, liquid paraffins, naphthas, mineral oils, crude oils, synthesized hydrocarbon liquids, fuel oils, diesels, gasolines, biomass derived hydrocarbon liquids, coal derived hydrocarbon liquids, kerosene, or mixtures thereof.

4. The composition of claim 1 , wherein the aqueous cement slurry comprises water, portland cement, pozzolan cement, gypsum cement, high alumina cement, slag cement, lime-silica blends, geopolymer cements, or combinations thereof.

5. The composition of claim 1 , wherein the calcined magnesium oxide is calcined at a temperature between 700° C. and 2000° C.

6. The composition of claim 1 , wherein the expanding agent is present in the non-aqueous additive at a concentration between 10 wt % and 80 wt %.

7. The composition of claim 1 , wherein the non-aqueous additive further comprises a dispersant comprising polynaphthalene sulfonate, sulfonated acetone formaldehyde condensate, polycarboxylate ethers, micro particles, or combinations thereof, and wherein the dispersant is present in the non-aqueous additive at a concentration between 0.1% and 20 wt %.

8. The composition of claim 1 , wherein the non-aqueous additive further comprises an emulsifier comprising polysorbates, sorbitan esters, or both, and wherein the emulsifier is present in the non-aqueous additive at a concentration between 0.01 wt % and 10 wt %.

9. The composition of claim 1 , further comprising a weighting agent, the weighting agent comprising silica, barite, hematite, ilmenite, manganese tetraoxide, or combinations thereof.

10. The composition of claim 9 , wherein a density of the composition varies between 10 lbm/gal (1200 kg/m 3 ) and 24 lbm/gal (2880 kg/m 3 ).

11. The composition of claim 1 , further comprising a weighting agent, the weighting agent comprising ceramic microspheres, glass microspheres, plastic beads, or combinations thereof.

12. The composition of claim 1 , wherein the expanding agent is the mixture of calcium oxide and calcined magnesium oxide.

13. The composition of claim 12 , wherein a weight ratio between the calcium oxide and the calcined magnesium oxide is between 10:90 and 90:10.

14. The composition of claim 12 , wherein a weight ratio between the calcium oxide and the calcined magnesium oxide is between 60:40 and 40:60.

15. The composition of claim 1 , wherein the expanding agent is encapsulated by a coating having a thickness between about 2 μm and about 80 μm.

16. The composition of claim 15 , wherein the coating comprises a polymer comprising a polyester, a polyacrylate, an epoxy, a polyhydroxy acid, a polypeptide, a polyesteramide, a polysulfide, a polysiloxane, a block copolymer comprising blocks joined through ester bonds, a block copolymer comprising blocks joined through amide bonds, or combinations thereof.

17. The composition of claim 15 , wherein the coating comprises silica.

18. The composition of claim 1 , further comprising:
a spacer fluid, comprising:
water;
a second expanding agent comprising calcium oxide, calcined magnesium oxide, or a mixture of calcium oxide and calcined magnesium oxide; and
a second viscosifying agent comprising an organophilic clay, hydrophobically modified silica, hydrophobically modified biopolymers, hydrophobically modified synthetic polymers, or combinations thereof.

19. The composition of claim 18 , wherein the second viscosifying agent is the hydrophobically modified biopolymers, the hydrophobically modified biopolymers comprising acetone-formaldehyde-sodium-bisulfate polymer and D-Glucopyranuronic acid, polymer with 6-deoxy-L-mannose, D-glucose, and D-mannose, calcium potassium sodium salt.

20. The composition of claim 19 , wherein a weight ratio between the acetone-formaldehyde-sodium-bisulfate polymer and the D-Glucopyranuronic acid, polymer with 6-deoxy-L-mannose, D-glucose and D-mannose, calcium potassium sodium salt in the second viscosifying agent is between 80:20 and 20:80.

Assignees

• Schlumberger Technology Corp

Inventors

• Jain Bipin
• Ashraf Shameed

Classifications

• C04B24/42

  Organo-silicon compounds · CPC title

• E21B33/14

  for cementing casings into boreholes · CPC title

• C04B14/368

  Baryte · CPC title

• C04B24/38

  Polysaccharides or derivatives thereof {(C04B24/243 takes precedence)} · CPC title

• C04B24/30

  Condensation polymers of aldehydes or ketones · CPC title