Binder composition comprising polyamine(s) as well as 1,3-dihydroxyacetone, glycolaldehyde and/or glyceraldehyde for composite articles

Patent metadata

Field	Value
Publication number	US-12312472-B2
Application number	US-202118268989-A
Country	US
Kind code	B2
Filing date	Dec 22, 2021
Priority date	Dec 23, 2020
Publication date	May 27, 2025
Grant date	May 27, 2025

Abstract

The present invention relates to a binder composition comprising a) component A comprising polymer(s) A1 having primary and/or secondary amino groups, wherein polymer(s) A1 has(have) a primary and secondary amine group nitrogen content of at least 1 wt.-% and b) component B comprising component B1 which is 1,3-dihydroxyacetone, glycolaldehyde, glyceraldehyde or any mixture thereof, wherein the polymer(s) A1 has(have) a total weight average molecular weight M w,total of at least 800 g/mol.

First claim

The invention claimed is:

1. A binder composition comprising
a) component A comprising polymer(s) A1 having primary and/or secondary amino groups wherein polymer A1 has (have) a NC ps of at least 1 wt.-%, wherein the polymer(s) A1 comprise(s) polymerization product of
i) amino acids, and/or
ii) amines comprising at least two amino groups, wherein the amines are no amino acids, and amino acids, and/or
iii) amines comprising at least two amino groups, wherein the amines are no amino acids, and di and/or tricarboxylic acids, and optionally amino acids and/or
iv) at least two compounds defined in i) to iii),

and
b) component B comprising component B1 which is 1,3-dihydroxyacetone,
glycolaldehyde, glyceraldehyde or any mixture thereof, wherein polymer A1 has (have) a total weight average molecular weight M w,total of at least 800 g/mol,
wherein the number ratio of the sum of the numbers of primary and secondary amine groups of Component A1 to sum of the numbers of aldehyde and keto groups of component B1 is from 10:1 to 0.3:1.

2. A binder composition according to claim 1 , wherein polymer A1 has (have) a total weight average molecular weight M w,total of at least 1000 g/mol and at most 20,000 g/mol.

3. A binder composition according to claim 1 , wherein component B1 is a mixture of 1,3-dihydroxyacetone, glycolaldehyde and glyceraldehyde.

4. A binder composition according to claim 1 , wherein component B1 is a mixture consisting of
1 to 30 wt.-% 1,3-dihydroxyacetone,
10 to 50 wt.-% glycolaldehyde and 20 to 80 wt.-% glyceraldehyde,
based on the total weight of component B1, wherein the weight amounts of 1,3-dihydroxyacetone, glycolaldehyde, and glyceraldehyde in total are selected such that the total weight of the sum of dihydroxyacetone, glycolaldehyde, and glyceraldehyde is 100 wt. %.

5. A binder composition according to claim 1 comprising at least 10 wt.-% to 95 wt.-% polymer(s) A1 based on the total weight of the sum of polymer(s) A1 and component B1.

6. A binder composition according to claim 1 , wherein polymer(s) A1 comprise(s) or consist(s) of branched polymer(s).

7. A binder composition according to claim 6 , wherein polymer(s) A1 comprise(s) or consist(s) of branched polymer(s) having a degree of branching of at least 0.05.

8. A binder composition according to claim 1 , wherein the polymer A1 comprise(s) at least one polymer selected from the group consisting of
(i) polyalkyleneimines,
(ii) polyamides,
iii) block copolymers comprising polyalkleneimine segments and polyamide segments,
(iv) graft copolymers comprising polyalkyleneimine segments and polyamide segments and
(v) mixtures of at least two of (i), (ii), (iii) and/or (iv).

9. A binder composition according to claim 1 ,
wherein polymer(s) A1 comprises a polymerization product of amino acids, wherein optionally at least 50 wt.-% amino acids are used as monomers for the polymerization reaction based on total amount of monomers.

10. A binder composition according to claim 9 , wherein for the polymerization of 100 g polymer(s) A1 at least 15 g diamino carboxylic acid(s) are used.

11. A binder composition according to claim 1 , wherein the polymer(s) A1 comprise(s) or consist(s) of poly (amino acids).

12. A binder composition according to claim 1 wherein the binder composition comprises 50 to 90 wt.-%, of polymer(s) A1, and 10 to 50 wt.-%, of component B1, based on the total weight of the sum of polymer(s) A1 and component B1, wherein the weight amounts of the polymer(s) A1 and component B1 are selected such that the total weight of the sum of polymer(s) A1 and component B1 is 100 wt.-%.

13. A binder composition according to claim 1 , wherein the polymer(s) A1 comprise(s) or consist(s) of polylysine(s).

14. A binder composition according to claim 1 , wherein the polymer(s) A1 comprise(s) or consist(s) of at least one a polymerization product of:
i) 1,2-ethylenediamine, 1,3-propylenediamine, bis-(3-aminopropyl) amine, N-(2-aminoethyl)-1,3-propylenediamine, bis-(2-aminoethyl) amine, bis-N-(2-aminoethyl)-1,3-propylenediamine, N,N′-bis-(3-aminopropyl)-1,2-ethylenediamine, N,N-bis-(3-aminopropyl)-1,2-ethylenediamine, or mixtures thereof and
ii) adipic acid, succinic acid or mixtures thereof.

15. A reacted binder composition obtained by reacting the binder components A and B according to claim 1 .

16. A plastic material comprising the reaction product of component A and B according to claim 1 .

17. A composition kit comprising the binder composition according to claim 1 , wherein component A and component B are stored separately.

18. A lignocellulosic composite article comprising a plurality of lignocellulosic pieces, and a binder composition according to claim 1 or a reacted binder composition obtained by reacting the binder components A and B according to claim 1 .

19. The lignocellulosic composite article according to claim 18 , wherein the article is plywood, an oriented strand board, a chip board and/or a fiber board.

20. A multi-layer particle board comprising at least one core layer and at least one surface layer, wherein the surface layer comprises a binder composition according to claim 1 and the core layer comprises a binder selected form the group consisting of urea/formaldehyde binder, phenol/formaldehyde binder, melamine/urea/formaldehyde binder, PMDI binder and mixtures thereof.

21. The multi-layer particle board according to claim 20 , wherein the formaldehyde emission measured according to EN 717-2 is lower than 2.0 mg/m 2 h.

22. A lignocellulosic composite article comprising a plurality of lignocellulosic pieces, and a binder composition according to claim 1 or a reacted composition obtainable or obtained by reacting the binder components A and B according to claim 1 or a multi-layer particle board comprising at least one core layer and at least one surface layer, wherein the surface layer comprises a binder composition according to claim 1 and the core layer comprises a binder selected form the group consisting of urea/formaldehyde binder, phenol/formaldehyde binder, melamine/urea/formaldehyde binder, PMDI binder and mixtures thereof, wherein 3 to 15 wt.-% polymer(s) A1 and component B1 in total based on the total oven-dry weight of the lignocellulosic pieces are used for the preparation of the lignocellulosic composite article.

23. A process for the batchwise or continuous production of lignocellulosic composite articles which are single-layered lignocellulose-based boards or of multi-layered lignocellulose-based boards with a core and with at least one upper and one lower surface layer, comprising the following steps:
a) mixing the lignocellulosic particles with a binder composition for each layer, wherein the mixture for at least one layer comprises the binder composition according to claim 1 ,
b) layer-by-layer scattering of the mixtures of the individual layers to form a mat,
c) pressing the mat to a board at a temperature of 80 to 300° C. and at a pressure of 1 to 100 bar or
c′) pressing the mat to a board at a temperature of 80 to 200° C. and at a pressure of 0.1 to 100 bar, wherein a high-frequency electrical field is applied during pressing until 80 to 200° C. is reached in the center of the mat.

24. A process according to claim 23 with a core and with at least one upper and one lower surface layer, wherein the surface layer comprises a binder composition comprising:
a) component A comprising polymer(s) A1 having pri

Assignees

• Basf Se

Inventors

• Sommer Gereon Antonius
• Scherr Guenter
• Weinkoetz Stephan
• Servay Thomas
• Hamann Jessica Nadine
• Teles Joaquim Henrique
• Lunkwitz Ralph
• Tuerp David

Classifications

• C08G69/265

  from at least two different diamines or at least two different dicarboxylic acids · CPC title

• B27N3/002

  characterised by the type of binder (compositions of macromolecular compounds C08L) · CPC title

• B27N3/02

  from particles · CPC title

• C08G69/10 Primary

  Alpha-amino-carboxylic acids {(polysuccinimides C08G73/1092)} · CPC title

• C08G12/46

  Block or graft polymers prepared by polycondensation of aldehydes or ketones on to macromolecular compounds · CPC title