Dual cure polyurethane formulations for 3D printing applications

Patent metadata

Field	Value
Publication number	US-12296527-B2
Application number	US-202117453948-A
Country	US
Kind code	B2
Filing date	Nov 8, 2021
Priority date	May 13, 2019
Publication date	May 13, 2025
Grant date	May 13, 2025

Abstract

The present invention lies in the field of 3D printing methods. In particular, the invention relates to 3D printing methods for the production of a 3D part in a layer-by-layer manner, wherein the printable composition is a pasty polyurethane composition comprising at least one polyisocyanate resin, at least one monomer and/or prepolymer that is polymerizable by exposure to radiation and at least one photoinitiator, wherein the pasty polyurethane composition has a viscosity factor (1.5/15) of at least 2 at application temperature.

First claim

What is claimed is:

1. A method for additive manufacturing a three-dimensional part in a layer-by-layer manner, the method comprising:
(i) providing a carrier substrate to support the three-dimensional part and a print head connected to a reservoir of a reactive curable printable composition;
(ii) printing the reactive curable printable composition with the print head as extrudate strands onto the carrier substrate to form a first layer;
(iii) printing the reactive curable printable composition with the print head as extrudate strands onto the first layer to form a second layer;
(iv) optionally repeating step (iii) one or more times to form a third layer or the third layer and subsequent layer(s);
(v) exposing the formed layers to radiation directly after forming each layer and/or after forming all of the layers; and
(vi) curing the formed layers of the reactive curable printable composition to obtain the three-dimensional part,
wherein the reactive curable printable composition is a pasty polyurethane composition comprising:
at least one polyisocyanate resin;
at least one monomer and/or prepolymer that is polymerizable by exposure to radiation; and
at least one photoinitiator, wherein:

the pasty polyurethane composition has a first viscosity factor (1.5/15) of at least 2 and a second viscosity factor (5/50) at an application temperature,
the first viscosity factor (1.5/15) is the viscosity of the pasty polyurethane composition at a shear rate of 1.5/s divided by the viscosity of the pasty polyurethane composition at a shear rate of 15/s and the second viscosity factor (5/50) is the viscosity of the pasty polyurethane composition at a shear rate of 5/s divided by the viscosity of the pasty polyurethane composition at a shear rate of 50/s,
the pasty polyurethane composition has a viscosity at a shear rate of 1.5/s of at least 10 Pas, and
the first viscosity factor (1.5/15) is greater than the second viscosity factor (5/50).

2. The method of claim 1 , wherein the distance of the print head to the carrier substrate or an already formed layer is equal to or greater than the thickness of the printed extrudate strands.

3. The method of claim 1 , wherein the viscosity factor (1.5/15) at the application temperature is at least 3.0.

4. The method of claim 1 , wherein the application temperature is in a range of from 15° C. to 80° C.

5. The method of claim 1 , wherein the viscosity at the shear rate of 1.5/s is at least 20 Pas.

6. The method of claim 1 , wherein the at least one polyisocyanate resin is an aliphatic polyisocyanate resin.

7. The method of claim 1 , wherein the at least one monomer and/or prepolymer is a dual reactive compound.

8. The method of claim 1 , wherein the pasty polyurethane composition further comprises an isocyanate curing catalyst.

9. The method of claim 1 , wherein the pasty polyurethane composition further comprises at least one polyol.

Assignees

• Henkel Ag & Co Kgaa

Inventors

• Poeller Sascha
• Schiel Manuel
• Rossberg Tanja
• Ferencz Andreas
• Welters Tim
• Franken Uwe

Classifications

• B29K2105/0094

  having particular viscosity · CPC title

• B29K2105/007

  Paste, dough · CPC title

• B29K2105/0014

  Catalysts · CPC title

• B29K2105/0002

  monomers or prepolymers · CPC title

• B29K2075/00

  Use of {PU, i.e.} polyureas or polyurethanes {or derivatives thereof}, as moulding material · CPC title