Three-dimensional printing

Patent metadata

Field	Value
Publication number	US-12296387-B2
Application number	US-201917052860-A
Country	US
Kind code	B2
Filing date	Mar 15, 2019
Priority date	Mar 15, 2019
Publication date	May 13, 2025
Grant date	May 13, 2025

Abstract

Described herein are kits, methods, and systems for printing metal three-dimensional objects. In an example, described is a kit for three-dimensional printing comprising: powdered metal build material; and a binding fluid comprising a liquid vehicle, metal or metal precursor particles, and latex polymer particles dispersed in the liquid vehicle, wherein the latex polymer particles have an average particle size of from about 10 nm to about 300 nm, and wherein the metal or metal precursor particles comprise metal nanoparticles, metal oxide nanoparticles, metal oxide nanoparticles and a reducing agent, or combinations thereof.

First claim

What is claimed is:

1. A printing system for printing a three-dimensional object, the printing system comprising:
a supply of a first inkjet-printable binding fluid, the first binding fluid including a liquid vehicle and metal or metal precursor particles;
a supply of a second inkjet-printable binding fluid, the second binding fluid including a second liquid vehicle and latex polymer particles dispersed in the second liquid vehicle, wherein the latex polymer particles have an average particle size of from about 10 nm to about 300 nm, a glass transition temperature (Tg) ranging from about 160° C. to about 200° C., and have a weight average molecular weight ranging from about 10,000 Mw to 300,000 Mw;
a supply of metal powdered build material;
a build material distributor;
a fluid applicator for selectively dispensing the first and second binding fluids, wherein the fluid applicator is a thermal inkjet printhead or a piezoelectric inkjet printhead;
a heat source;
a controller; and
a non-transitory computer readable medium having stored thereon computer executable instructions to cause the controller to print the three-dimensional object by:
utilizing the build material distributor and the fluid applicator to iteratively form at least one layer of powdered metal build material having selective application of the first and second binding fluids; and
utilizing the heat source to heat the selectively applied first and second binding fluids on the powdered metal build material to form the three-dimensional object.

2. The printing system of claim 1 , wherein the powdered metal build material is selected from the group consisting of steels, bronzes, titanium and alloys thereof, aluminum and alloys thereof, nickel and alloys thereof, cobalt and alloys thereof, iron and alloys thereof, nickel cobalt alloys, gold and alloys thereof, silver and alloys thereof, platinum and alloys thereof, copper and alloys thereof, and combinations thereof.

3. The printing system of claim 1 , wherein the latex polymer particles are made from (A) a co-polymerizable surfactant selected from the group consisting of polyoxyethylene alkylphenyl ether ammonium sulfate, sodium polyoxyethylene alkylether sulfuric ester, polyoxyethylene styrenated phenyl ether ammonium sulfate, and mixtures thereof, and (B) styrene, p-methyl styrene, α-methyl styrene, methacrylic acid, acrylic acid, acrylamide, methacrylamide, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate, methyl methacrylate, hexyl acrylate, hexyl methacrylate, butyl acrylate, butyl methacrylate, ethyl acrylate, ethyl methacrylate, 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, propyl acrylate, propyl methacrylate, octadecyl acrylate, octadecyl methacrylate, stearyl methacrylate, isobornyl acrylate, tetrahydrofurfuryl acrylate, 2-phenoxyethyl methacrylate, benzyl methacrylate, benzyl acrylate, ethoxylated nonyl phenol methacrylate, ethoxylated behenyl methacrylate, polypropyleneglycol monoacrylate, isobornyl methacrylate, cyclohexyl methacrylate, cyclohexyl acrylate, t-butyl methacrylate, n-octyl methacrylate, lauryl methacrylate, tridecyl methacrylate, alkoxylated tetrahydrofurfuryl acrylate, isodecyl acrylate, isobornyl methacrylate, isobornyl acrylate, acetoacetoxyethyl methacrylate, or combinations thereof.

4. The printing system of claim 1 , wherein the latex polymer particles are present in the second inkjet-printable binding fluid in an amount ranging from about 2 wt % to about 30 wt % based on a total weight of the second inkjet-printable binding fluid.

5. The printing system of claim 1 , wherein the average particle size of the latex polymer particles ranges from about 50 nm to about 300 nm.

6. The printing system of claim 1 , wherein the metal or metal precursor particles are selected from the group consisting of metal nanoparticles, metal oxide nanoparticles, metal oxide nanoparticles with a reducing agent, and combinations thereof.

7. The printing system of claim 6 , wherein:
the metal or metal precursor particles are the metal oxide nanoparticles, and wherein the metal oxide nanoparticles are oxides of iron, nickel, silver, gold, copper, platinum, cobalt, manganese, vanadium, molybdenum, or combinations thereof; or
the metal or metal precursor particles are the metal nanoparticles, and wherein the metal nanoparticles are selected from the group consisting of nickel nanoparticles, silver nanoparticles, gold nanoparticles, platinum nanoparticles, and combinations thereof.

8. The printing system of claim 1 , wherein the metal or metal precursor particles have a mean particle diameter of less than about 200 nm.

9. The printing system of claim 1 , wherein the second liquid vehicle includes at least one coalescing solvent, and wherein the at least one coalescing solvent is present in the second inkjet-printable binding agent in an amount ranging from about 0.1 to about 50 wt %.

10. The printing system of claim 1 , wherein the second inkjet-printable binding fluid has a pH ranging from about 6.5 to about 9.

11. The printing system of claim 1 , wherein the second inkjet-printable binding fluid has a viscosity of less than about 10 cps.

12. The printing system of claim 1 , wherein the second inkjet-printable binding fluid consists of the second liquid vehicle and the latex polymer particles.

13. The printing system of claim 1 , wherein the latex polymer particles made of two different copolymer compositions have a core-shell configuration.

14. A kit for use in the printing system of claim 1 , the kit comprising:
the metal powdered build material;
the first inkjet-printable binding fluid; and
the second inkjet-printable binding fluid.

15. The kit of claim 14 , wherein the latex polymer particles are made from (A) a co-polymerizable surfactant selected from the group consisting of polyoxyethylene alkylphenyl ether ammonium sulfate, sodium polyoxyethylene alkylether sulfuric ester, polyoxyethylene styrenated phenyl ether ammonium sulfate, and mixtures thereof, and (B) styrene, p-methyl styrene, α-methyl styrene, methacrylic acid, acrylic acid, acrylamide, methacrylamide, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate, methyl methacrylate, hexyl acrylate, hexyl methacrylate, butyl acrylate, butyl methacrylate, ethyl acrylate, ethyl methacrylate, 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, propyl acrylate, propyl methacrylate, octadecyl acrylate, octadecyl methacrylate, stearyl methacrylate, isobornyl acrylate, tetrahydrofurfuryl acrylate, 2-phenoxyethyl methacrylate, benzyl methacrylate, benzyl acrylate, ethoxylated nonyl phenol methacrylate, ethoxylated behenyl methacrylate, polypropyleneglycol monoacrylate, isobornyl methacrylate, cyclohexyl methacrylate, cyclohexyl acrylate, t-butyl methacrylate, n-octyl methacrylate, lauryl methacrylate, tridecyl methacrylate, alkoxylated tetrahydrofurfuryl acrylate, isodecyl acrylate, isobornyl methacrylate, isobornyl acrylate, acetoacetoxyethyl methacrylate, or combinations thereof.

16. The kit of claim 14 , wherein the powered metal build material is selected from the group consisting of steels, bronzes, titanium and alloys thereof, aluminum and alloys thereof, nickel and alloys thereof, cobalt and alloys thereof, iron and alloys thereof, nickel cobalt alloys, gold and alloys thereof, silver and alloys thereof, platinum and alloys thereof, copper and alloys thereof, and combinations thereof.

17. The kit of claim 14 , wherein the metal or metal precursor particles are selected from the gro

Assignees

• Peridot Print Llc

Inventors

• Kasperchik Vladek
• Nauka Krzysztof
• Shaarawi Mohammed S

Classifications

• B22F1/17

  Metallic particles coated with metal · CPC title

• B22F1/054

  Nanosized particles · CPC title

• B22F1/18

  Non-metallic particles coated with metal · CPC title

• B22F10/14

  by jetting of binder onto a bed of metal powder · CPC title

• B22F2999/00

  Aspects linked to processes or compositions used in powder metallurgy · CPC title