Polyethylene yarn, method for manufacturing the same, and skin cooling fabric comprising the same

Patent metadata

Field	Value
Publication number	US-12291802-B2
Application number	US-201917602704-A
Country	US
Kind code	B2
Filing date	Dec 27, 2019
Priority date	Dec 27, 2019
Publication date	May 6, 2025
Grant date	May 6, 2025

Abstract

Disclosed is a polyethylene yarn capable of providing a user with a soft tactile sensation as well as a cooling feeling or a cooling sensation, and also having improved weavability that enables the manufacture of a skin cooling fabrics having excellent pilling resistance, abrasion resistance, cuttability, and sewability, a method for manufacturing the same, and a skin cooling fabric including the same. In a strength-elongation curve of the polyethylene yarn obtained by measuring at ambient temperature, (i) elongation at strength of 1 g/d is 0.5 to 3%, (ii) elongation at strength of 3 g/d is 5.5 to 10%, and (iii) a difference between elongation at strength of 4 g/d and elongation at maximum strength is 5.5 to 25%, and the polyethylene yarn has toughness of 55 to 120 J/m 3 at ambient temperature.

First claim

The invention claimed is:

1. A polyethylene yarn,
wherein in a strength-elongation curve of the polyethylene yarn obtained by measuring at ambient temperature, (i) elongation at strength of 1 g/d is 1 to 3%, (ii) elongation at strength of 3 g/d is 6 to 10%, and (iii) a difference between elongation at strength of 4 g/d and elongation at maximum strength is 9 to 25%, and
the polyethylene yarn has toughness of 55 to 120 J/cm 3 at ambient temperature,
wherein the polyethylene var includes a polyethylene polymer having a weight average molecular weight (Mw) of 50,000 to 99,000 g/mol, a polydispersity index (PDI) of 5.5 to 9, and a melt index (MD) of 6 to 21 g/10 min at 190° C.

2. The polyethylene yarn of claim 1 , wherein
the polyethylene yarn has tensile strength of more than 4 g/d and 6 g/d or less, a tensile modulus of 15 to 80 g/d, elongation at break of 14 to 55%, and crystallinity of 60 to 85%.

3. The polyethylene yarn of claim 1 , wherein
the polyethylene yarn has a polydispersity index (PDI) of 5.5 to 7.0.

4. The polyethylene yarn of claim 1 , wherein
the polyethylene yarn has total fineness of 75 to 450 denier, and
the polyethylene yarn includes a plurality of filaments each having fineness of 1 to 5 denier.

5. The polyethylene yarn of claim 1 , wherein
the polyethylene yarn has a circular cross-section.

6. A skin cooling fabric formed of the polyethylene yarn of claim 1 ,
wherein the polyethylene var includes a polyethylene polymer having a weight average molecular weight (Mw) of 50,000 to 99,000 g/mol, a polydispersity index (PDI) of 5.5 to 9, and a melt index (MD) of 6 to 21 g/10 min at 190° C.,
wherein the skin cooling fabric at 20° C. has thermal conductivity in the thickness direction of 0.0003 to 0.0005 W/cm ° C., a heat transfer coefficient in the thickness direction of 0.01 to 0.02 W/cm 2 ° C., and a contact cold sensation (Q max ) of 0.1 W/cm 2 or more.

7. The skin cooling fabric of claim 6 , wherein
a pilling resistance of the skin cooling fabric measured according to ASTM D 4970-07 is grade 4 or higher, and
abrasion resistance of the skin cooling fabric measured according to the Martindale method as specified in KS K ISO 12947-2:2014 is 5000 cycles or more.

8. The skin cooling fabric of claim 6 , wherein
an area density of the skin cooling fabric is 75 to 800 g/m 2 .

Assignees

• Kolon Inc

Inventors

• Kim Jae-Hyung
• Kim Gi-Woong
• Kim Seong-Young
• Lee Sang-Mok
• Lee Sin-Ho
• Lee Young-Soo

Classifications

• D10B2321/021

  polyethylene · CPC title

• D01F6/04 Primary

  from polyolefins · CPC title

• D01D5/088 Primary

  Cooling filaments, threads or the like, leaving the spinnerettes · CPC title

• D01D5/08

  Melt spinning methods {(D01D5/0023 takes precedence)} · CPC title

• D01D5/12

  Stretch-spinning methods ({D01D5/098 takes precedence} finishing by stretching D02J1/22) · CPC title