Method for preparing conjugated diene-based polymer

Patent metadata

Field	Value
Publication number	US-12291630-B2
Application number	US-202017615386-A
Country	US
Kind code	B2
Filing date	Sep 23, 2020
Priority date	Sep 27, 2019
Publication date	May 6, 2025
Grant date	May 6, 2025

Abstract

The present invention relates to a method for preparing a conjugated diene-based polymer, characterized in using a dimer acid saponified material as an emulsifier in a polymerization initiation step and injecting a monomer and the emulsifier in three or more installments after initiating polymerization, and the conjugated diene-based polymer prepared by the preparation method of the present invention has excellent physical properties such as impact strength and reflection haze.

First claim

The invention claimed is:

1. A method for preparing a conjugated diene-based polymer, the method comprising:
injecting 30 to 50 parts by weight of a conjugated diene-based monomer among 100 parts by weight, 0.1 to 5 parts by weight of a dimer acid saponified material, and a polymerization initiator into a reactor in one batch, and initiating polymerization reaction (S1);
injecting the remaining conjugated diene-based monomer and an emulsifier in three or more installments according to a polymerization conversion ratio after initiating the polymerization reaction (S2); and
finishing the polymerization reaction at a point where the polymerization conversion ratio is 90 to 99% (S3),
wherein step S2 comprises:
injecting the conjugated diene-based monomer and the emulsifier at a point where the polymerization conversion ratio is 20 to 35% (S2-1);
injecting the conjugated diene-based monomer and the emulsifier at a point where the polymerization conversion ratio is 45 to 60% (S2-2); and
injecting the conjugated diene-based monomer and the emulsifier at a point where the polymerization conversion ratio is 70 to 80% (S2-3).

2. The method for preparing a conjugated diene-based polymer according to claim 1 , wherein step S2 is injecting the remaining conjugated diene-based monomer and the emulsifier in three or four installments.

3. The method for preparing a conjugated diene-based polymer according to claim 1 , wherein an amount of the conjugated diene-based monomer injected in installments is equal to or less than an amount of the conjugated diene-based monomer injected immediately before.

4. The method for preparing a conjugated diene-based polymer according to claim 1 , wherein
20 to 30 parts by weight of the conjugated diene-based monomer is injected in step S2-1,
15 to 25 parts by weight of the conjugated diene-based monomer is injected in step S2-2,
10 to 20 parts by weight of the conjugated diene-based monomer is injected in step S2-3, and
a total amount of the conjugated diene-based monomer injected in steps S2-1 to S2-3 is 70 parts by weight or less.

5. The method for preparing a conjugated diene-based polymer according to claim 1 , wherein the amount injected of the conjugated diene-based monomer injected in steps S2-1 to S2-3 satisfies the following Formula 1:
M 1≥ M 2≥ M 3  [Formula 1]

where M1, M2 and M3 are injection amounts of the conjugated diene-based monomer in steps S2-1, S2-2 and S2-3, respectively.

6. The method for preparing a conjugated diene-based polymer according to claim 1 , wherein the dimer acid is one or more selected among compounds represented by the following Chemical Formulae 1 to 6:

7. The method for preparing a conjugated diene-based polymer according to claim 1 , wherein the polymerization initiator is one or more among a water-soluble polymerization initiator, and a mixture of an oil-soluble polymerization initiator and an oxidation-reduction system catalyst.

8. The method for preparing a conjugated diene-based polymer according to claim 7 , wherein
the water-soluble polymerization initiator is one or more selected from the group consisting of potassium persulfate, sodium persulfate and ammonium persulfate,
the oil-soluble polymerization initiator is one or more selected from the group consisting of cumene hydroperoxide, diisopropylbenzene hydroperoxide, azobisisobutyronitrile, tert-butyl hydroperoxide, paramenthane hydroperoxide, and benzoyl peroxide, and
the oxidation-reduction system catalyst is one or more selected from the group consisting of sodium formaldehyde sulfoxylate, sodium ethylenediaminetetraacetate, ferrous sulfate, dextrose, sodium pyrophosphate, and sodium sulfite.

9. The method for preparing a conjugated diene-based polymer according to claim 1 , wherein the polymerization initiator is injected in 0.01 to 1 parts by weight based on 100 parts by weight of the conjugated diene-based monomer.

10. The method for preparing a conjugated diene-based polymer according to claim 1 , wherein a molecular weight regulator is further injected in step S1 and step S2, and
a total amount of the molecular weight regulator injected in step S1 and step S2 is less than 1 part by weight based on 100 parts by weight of the conjugated diene-based monomer.

11. The method for preparing a conjugated diene-based polymer according to claim 1 , wherein the emulsifier is one or more selected from the group consisting of a rosin acid saponified material, a fatty acid saponified material, a dimer acid saponified material and an oleic acid saponified material.

12. The method for preparing a conjugated diene-based polymer according to claim 1 , wherein an average particle diameter of the conjugated diene-based polymer is 1000 to 2000 Å.

13. The method for preparing a conjugated diene-based polymer according to claim 1 , further comprising:
injecting a coagulant, or a coagulant and an auxiliary coagulant for enlargement after finishing the polymerization reaction (S4),
wherein the average particle diameter of the conjugated diene-based polymer is 2500 to 4000 Å.

14. A method for preparing a graft copolymer, the method comprising graft polymerizing the conjugated diene-based polymer prepared by the preparation method according to claim 1 with an aromatic vinyl-based monomer and a vinyl cyan-based monomer.

15. A thermoplastic resin composition, comprising:
the graft copolymer prepared by the preparation method of claim 14 ; and
a copolymer comprising a derived unit from the aromatic vinyl-based monomer and a derived unit from the vinyl cyan-based monomer.

Assignees

• Lg Chemical Ltd

Inventors

• Jeong Young Hwan
• Kim Yoo Vin
• Lee Jin Hyoung
• Heo Jae Won
• Kim Young Min

Classifications

• C08F6/18

  Increasing the size of the dispersed particles · CPC title

• C08F4/40

  Redox systems · CPC title

• C08L55/02

  ABS [Acrylonitrile-Butadiene-Styrene] polymers · CPC title

• C08L25/12

  with unsaturated nitriles · CPC title

• C08L25/10

  with conjugated dienes · CPC title