Method for preparing WPU synthetic leather foaming layers based on pickering foam template method

Patent metadata

Field	Value
Publication number	US-12291622-B2
Application number	US-202117495010-A
Country	US
Kind code	B2
Filing date	Oct 6, 2021
Priority date	Dec 11, 2020
Publication date	May 6, 2025
Grant date	May 6, 2025

Abstract

The disclosure provides a new method for preparing a WPU synthetic leather foaming layer based on a Pickering foam template method. The key of the method is to use the soft waterborne polyurethane as raw materials, add waterborne crosslinking agent and hydrophobic inorganic solid particles as Pickering waterborne foam stabilizers to obtain Pickering waterborne foam slurry of polyurethane latex particles through high-speed emulsification; and dry the slurry to obtain the waterborne polyurethane foam layer. The preparation process does not use any organic solvents, is clean and environmentally-friendly, and is simple to operate, making it easier to realize industrialized production. In addition, the Pickering foam has strong interface stability, which effectively solves the problem of difficult adjustment of the pore size caused by the accumulation and collapse of bubbles during the drying process of the mechanical foaming method, and the prepared synthetic leather foam layer has good hygienic properties.

First claim

What is claimed is:

1. A method for preparing a waterborne polyurethane synthetic leather foaming layer based on a Pickering foam template method, comprising the following steps:
(1) selecting a soft waterborne polyurethane with a solid content of 20-40% as a raw material for the waterborne polyurethane synthetic leather foaming layer, adding a waterborne crosslinking agent thereto, and mixing uniformly to obtain a waterborne polyurethane slurry for synthetic leather;
(2) adding the waterborne polyurethane slurry for synthetic leather to an open container, then adding hydrophobic inorganic solid particles that can be adsorbed at a water-air interface as a foam stabilizer, wherein a mass ratio of the hydrophobic inorganic solid particles to the waterborne polyurethane slurry for synthetic leather is (0.05-0.2): 1, a volume of a mixed solution in the container is below ½ of a volume of the container, and air is used as a dispersed phase; after mixing uniformly, performing emulsifying and dispersing by a high-speed emulsifier for 0.5-2 h with a speed of 8000-15000 rpm/min to obtain a Pickering waterborne foam slurry containing polyurethane latex particles; and
(3) drying the Pickering waterborne foam slurry at 70-120° C. to obtain the waterborne polyurethane synthetic leather foaming layer based on the Pickering foam template method;
wherein the waterborne polyurethane slurry for synthetic leather is prepared by the following steps:
1) adding a hard segment monomer diisocyanate and a soft segment monomer polymer diol to a reactor in accordance with a molar ratio of (2-5):1, adding an appropriate amount of solvent acetone, and stirring and reacting for 1 h at a temperature of 60-90° C.; then adding a chain extender 2,2-dimethylolpropionic acid and 1,4-butanediol and 1-2 drops of a catalyst with a molar ratio of the chain extender to the soft segment monomer polymer diol of (1-4): 1, and conducting a reaction at a temperature of 70-90° C. for 3-6 h with a stirring speed of 100-2000 rpm to obtain a polyurethane polymer; wherein a ratio of the 2,2-dimethylolpropionic acid to the 1,4-butanediol is adjusted to make an amount of the 2,2-dimethylolpropionic acid account for 4-6 wt % of all reactants added;
2) adding triethylamine to the reactor, performing neutralization for 0.5-2 h at a temperature of 40-50° C. and a stirring speed of 1000-2000 rpm, adjusting a pH to 3-10; finally adding a certain amount of deionized water to a resulting reaction product, stirring for 10-30 min at a stirring speed of 8000-10000 rpm; and stirring for 1-2 h at a stirring speed of 1000-3000 rpm; and
3) removing acetone by rotary evaporation, and concentrating a resulting product to a solid content of 20%-40% to obtain the waterborne polyurethane slurry for synthetic leather.

2. The method for preparing the waterborne polyurethane synthetic leather foaming layer based on the Pickering foam template method according to claim 1 , wherein the soft waterborne polyurethane is a waterborne polyurethane with an elastic modulus of 20-45 MPa, the particle size is 50-300 nm, and the residual organic solvent content is less than 2% (by weight).

3. The method for preparing the waterborne polyurethane synthetic leather foaming layer based on the Pickering foam template method according to claim 1 , wherein the soft segment monomer polymer diol used in the preparation of soft waterborne polyurethane is one of polyether polyol, polyester polyol, hydroxy-terminated polysiloxane, and hydroxy-terminated polylactic acid with a molecular weight of 2000-10,000; the hard segment monomer diisocyanate is one of isophorone diisocyanate (IPDI) and hexamethylene diisocyanate (HDI); and the soft segment content of the polyurethane calculated by the added mass of the soft segment monomer and the hard segment monomer is 50-65 wt %.

4. The method for preparing the waterborne polyurethane synthetic leather foaming layer based on the Pickering foam template method according to claim 1 , wherein the waterborne crosslinking agent is one of polycarbodiimide, polyaziridine, and epoxy resin.

5. The method for preparing the waterborne polyurethane synthetic leather foaming layer based on the Pickering foam template method according to claim 1 , wherein the foam stabilizer is hydrophobic solid particles with a particle diameter of 10 nm-5 μm, including one of hydrophobic SiO 2 particles, clay and styrene particles, and the surface contact angle of the solid particles is 100-150°.

Assignees

• Univ Sichuan

Inventors

• Wang Chunhua
• Lin Wei
• To Ngai
• Sheng Yifeng
• Wu Jianhui

Classifications

• D06N2205/04

  Foam · CPC title

• D06N3/148

  (cyclo)aliphatic polyisocyanates · CPC title

• D06N3/0043

  characterised by their foraminous structure; Characteristics of the foamed layer or of cellular layers (foraminous structure obtained by stretching D06N3/0029) · CPC title

• C08J2375/08

  from polyethers · CPC title

• C08J9/0066

  Use of inorganic compounding ingredients · CPC title