High temperature oxidation protection for composites

Patent metadata

Field	Value
Publication number	US-12246994-B2
Application number	US-202017079239-A
Country	US
Kind code	B2
Filing date	Oct 23, 2020
Priority date	Dec 27, 2019
Publication date	Mar 11, 2025
Grant date	Mar 11, 2025

Abstract

A method for forming an oxidation protection system on a composite structure are provided. The method includes applying a composite slurry to the composite structure, wherein the composite slurry comprises boron carbide, silicon carbide, borosilicate glass, an oxygen reactant compound including a silica forming component, and a carrier fluid and heating the composite structure to a temperature sufficient to form a boron-silicon-glass-oxygen reactant layer on the composite structure.

First claim

What is claimed is:

1. A method for forming an oxidation protection system on a composite structure, comprising:
applying a composite slurry to the composite structure, wherein the composite slurry comprises boron carbide, silicon carbide, borosilicate glass, an oxygen reactant compound including a silica forming component, and a carrier fluid, and wherein the oxygen reactant compound is between 1.0% and 10.0% of a dry weight of the composite slurry, the composite slurry comprises from 10% to 40% by weight the boron carbide, the oxygen reactant compound comprises particles having an average particle size of between 20 nm and 20 μm, the boron carbide comprises a boron compound powder comprising particles having an average particle size between 100 nm and 100 μm, and the silicon carbide comprises a silicon carbide powder comprising particles having an average particle size of between 500 nm and 20 μm, and the composite slurry is substantially free of phosphate; and
heating the composite structure to a temperature sufficient to form a boron-silicon-glass-oxygen reactant layer on the composite structure.

2. The method of claim 1 , wherein the oxygen reactant compound comprises silicon dioxide.

3. The method of claim 2 , further comprising applying a pretreatment composition to the composite structure between an outer surface of the composite structure and the composite slurry, the pretreatment composition comprising at least one of aluminum oxide or silicon dioxide.

4. The method of claim 2 , further comprising applying a pretreatment composition to the composite structure between an outer surface of the composite structure and the composite slurry, the pretreatment composition comprising silicon dioxide.

5. The method of claim 2 , wherein the composite slurry comprises about 21.1% by weight boron carbide having an average particle size of about 9.3 μm (0.0004 inch), about 27.1% by weight silicon carbide having an average particle size of about 1 μm (4×10 −5 inch), about 18.1% by weight borosilicate glass having an average particle size of about 12.3 μm (0.0005 inch), between about 0.5% and 0.6% by weight silicon dioxide, and about 33.2% by weight water; the borosilicate glass being comprised, in weight percentage of the borosilicate glass, of about 13% B 2 O 3 , about 61% SiO 2 , about 2% Al 2 O 3 , and about 4% Na 2 O.

6. The method of claim 1 , wherein a composition of the borosilicate glass comprises in weight percentage 13% B 2 O 3 , 61% SiO 2 , 2% Al 2 O 3 , and 4% sodium oxide (Na 2 O).

7. The method of claim 1 , wherein the heating the composite structure to the temperature sufficient to form a boron-silicon-glass-oxygen reactant layer on the composite structure includes:
performing a first temperature bake by heating the composite structure at a first temperature, and
subsequent to performing the low temperature bake, performing a second temperature bake by heating the composite structure at a second temperature that is greater than the first temperature, the first temperature is between about 150° F. and about 250° F., and the second temperature is between about 1600° F. and about 1700° F.

8. The method of claim 7 , wherein the first temperature bake is performed for between 10 minutes to 30 minutes and the second temperature bake is performed for between 1.5 hours to about 2.5 hours.

9. The method of claim 1 , wherein the silica forming component comprises at least one of SiO2, silicon, silicon carbide, silicon oxycarbide (SiOC), a silicate, or an organosilicate.

10. The method of claim 1 , wherein the oxygen reactant compound comprises particles having an average particle size of between 30 nm and 10 μm.

11. The method of claim 1 , wherein the oxygen reactant compound comprises particles having an average particle size of between 30 nm and 2.0 μm.

12. The method of claim 1 , wherein the boron carbide powder comprises a first group of particles having a first average particle size and a second group of particles having a second average particle size greater than the first average particle size.

Assignees

• Goodrich Corp

Inventors

• Poteet Steven A
• Pimentel Katherine Urena
• Sheehan Philip
• Weaver John

Classifications

• C04B41/89 Primary

  for obtaining at least two superposed coatings having different compositions · CPC title

• C04B2235/9684

  Oxidation resistance · CPC title

• C04B41/507

  Borides · CPC title

• C04B41/5059

  Silicon carbide · CPC title

• C04B41/5035

  Silica · CPC title