Method of producing porous body of water-insoluble polymer

Patent metadata

Field	Value
Publication number	US-12227630-B2
Application number	US-202016998664-A
Country	US
Kind code	B2
Filing date	Aug 20, 2020
Priority date	Aug 29, 2019
Publication date	Feb 18, 2025
Grant date	Feb 18, 2025

Abstract

Provided is a method of producing a porous body of a water-insoluble polymer, the method being excellent in terms of simplicity. The method of producing a porous body of a water-insoluble polymer disclosed here includes the steps of: preparing a solution in which a water-insoluble polymer is dissolved in a mixed solvent containing a good solvent for the water-insoluble polymer and a poor solvent for the water-insoluble polymer; and removing the mixed solvent from the solution by vaporization. The poor solvent has a boiling point higher than a boiling point of the good solvent. A porous body is obtained by removing the mixed solvent by vaporization to form pores.

First claim

What is claimed is:

1. A method of producing a porous body of a water-insoluble polymer, the method comprising the steps of:
preparing a solution in which a water-insoluble polymer is dissolved in a mixed solvent containing a good solvent for the water-insoluble polymer and a poor solvent for the water-insoluble polymer; and
removing the mixed solvent from the solution by vaporization, wherein
the poor solvent has a boiling point higher than a boiling point of the good solvent,
a porous body is obtained by removing the mixed solvent by vaporization to form pores,
the water-insoluble polymer is an ethylene-vinyl alcohol copolymer,
the good solvent is dimethyl sulfoxide or a mixed solvent of water and propyl alcohol,
the poor solvent is propylene carbonate, or an ether group-containing monool, and
the porous body is a separation membrane.

2. The production method according to claim 1 , wherein the boiling point of the poor solvent is at least 10° C. higher than the boiling point of the good solvent.

3. The production method according to claim 1 wherein the porous body has one main surface and another main surface, and the porous body has a three-dimensional network-shaped porous structure in which pores are connected from the one main surface to the another main surface.

4. The production method according to claim 1 wherein the obtained porous body has a porosity 61.5% or more.

5. The production method according to claim 1 wherein the obtained porous body has a porosity 72.4% or more.

6. The production method according to claim 1 wherein the obtained porous body has an average pore diameter of 0.9 μm or more and 5 μm or less.

7. The production method according to claim 4 wherein the obtained porous body has an average pore diameter of 0.9 μm or more and 5 μm or less.

8. The production method according to claim 1 wherein an average degree of polymerization of the ethylene-vinyl alcohol copolymer is 100 or more and 200,000 or less.

9. The production method according to claim 1 wherein a content of ethylene units in the ethylene-vinyl alcohol copolymer 20 mol % or more and 50 mol % or less.

10. The production method according to claim 1 wherein a content of ethylene units in the ethylene-vinyl alcohol copolymer 25 mol % or more and 45 mol % or less.

11. The production method according to claim 1 wherein, in the preparing step, a mixing amount of the water-insoluble polymer is 1 part by mass or more and 40 parts by mass or less relative to 100 parts by mass of the good solvent, and a mixing amount of the poor solvent is 10 parts by mass or more and 400 parts by mass or less relative to 100 parts by mass of the good solvent.

12. The production method according to claim 1 wherein, in the preparing step, a mixing amount of the water-insoluble polymer is 10 parts by mass or more and 30 parts by mass or less relative to 100 parts by mass of the good solvent, and a mixing amount of the poor solvent is 30 parts by mass or more and 100 parts by mass or less relative to 100 parts by mass of the good solvent.

Assignees

• Toyota Motor Co Ltd

Inventors

• Matsunobu Kohei
• Minakuchi Akio
• Uyama Hiroshi
• Yoshizawa Chiaki

Classifications

• C08J9/28 Primary

  by elimination of a liquid phase from a macromolecular composition or article, e.g. drying of coagulum · CPC title

• C08J2329/04

  Polyvinyl alcohol; Partially hydrolysed homopolymers or copolymers of esters of unsaturated alcohols with saturated carboxylic acids · CPC title

• C08J2201/0502

  the liquid phase being organic · CPC title

• B32B5/18

  characterised by features of a layer {of} foamed material · CPC title

• B29C67/20

  for porous or cellular articles, e.g. of foam plastics, coarse-pored {(chemical aspects of working up macro-molecular substances to porous or cellular articles C08J9/00)} · CPC title