Abstract

Disclosed herein are coating compositions and/or coatings comprising a water-soluble resin mixture comprising a polyvinyl alcohol (PVOH) and a polyacrylic acid (PAA), and further comprising a colorant and/or an aversive agent, surfaces of substrates coated with the compositions, and methods of making and using the same.

First claim

What is claimed:

1. A coating composition, comprising:
a water-soluble resin mixture comprising
(a) a polyvinyl alcohol (PVOH) comprising a polyvinyl alcohol homopolymer, a polyvinyl alcohol copolymer having an anionic modification, or a combination thereof, and having a 4% solution viscosity at 20° C. of about 25 cP or less and a polyacrylic acid (PAA) homopolymer having a weight average molecular weight ( M w) in a range of 1000 Da to 300,000 Da, wherein the PVOH and PAA are in a ratio in a range of 80:20 to 20:80 by weight, respectively; and
(b) an aversive agent comprising a denatonium salt, sucrose octaacetate, quinine, a flavonoid, a quassinoid, or a combination thereof.

2. A coating composition, comprising:
a water-soluble resin mixture comprising
(a) a polyvinyl alcohol (PVOH) comprising a polyvinyl alcohol homopolymer, a polyvinyl alcohol copolymer having an anionic modification, or a combination thereof, and having a 4% solution viscosity at 20° C. of about 25 cP or less and a polyacrylic acid (PAA) homopolymer having a weight average molecular weight ( M w) in a range of 1000 Da to 300,000 Da, wherein the PVOH and PAA are in a ratio in a range of 80:20 to 20:80 by weight, respectively; and
(b) a colorant comprising a triphenylmethane dye, an azo dye, an anthraquinone dye, a perylene dye, an indigoid dye, a food, drug and cosmetic (FD&C) colorant, an organic pigment, an inorganic pigment, or a combination thereof, wherein the colorant is at a concentration±10% of the saturation point of the colorant.

3. The coating composition of claim 1 , wherein the PVOH is a PVOH homopolymer.

4. The coating composition of claim 1 , wherein the aversive agent comprises denatonium benzoate (DnBz) and the DnBz concentration is in a range of 1,000 to 20,000 ppm based on the total weight of the coating composition.

5. The coating composition of claim 1 , wherein the coating composition further comprises a colorant.

6. The coating composition of claim 5 , wherein the colorant comprises a triphenylmethane dye, an azo dye, an anthraquinone dye, a perylene dye, an indigoid dye, a food, drug and cosmetic (FD&C) colorant, an organic pigment, an inorganic pigment, or a combination thereof.

7. The coating composition of claim 5 , wherein the coating composition comprises water and the colorant is present in an amount of at least 15 parts colorant to 70 parts water.

8. The coating composition of claim 1 , wherein the coating composition comprises a colorant present in greater than or equal to 17% by weight of the solids content.

9. A coating, comprising:
a first water-soluble layer comprising the coating composition according to claim 1 that is dried first.

10. The coating of claim 9 , further comprising a second water-soluble layer comprising a dried second coating composition.

11. The coating of claim 10 , wherein the dried second coating composition is free of colorants.

12. The coating of claim 10 , wherein the dried second coating composition comprises a water-soluble polymer and the water-soluble polymer comprises a PVOH having a 4% solution viscosity at 20° C. of no more than about 10 cP.

13. The coating of claim 10 , wherein the dried second coating composition further comprises a plasticizer.

14. The coating of claim 13 , wherein the weight ratio of the PVOH of the dried second coating composition to plasticizer is about 4:1.

15. The coating of claim 14 , wherein the plasticizer of the dried second coating comprises glycerol, polyethylene glycol, propylene glycol, monoacetin, triacetin, triethyl citrate, sorbitol, 1,3-butanediol, D-glucono-1,5-lactone, or a combination thereof.

16. The coating of claim 9 , wherein the first water-soluble layer is provided on a surface of a substrate.

17. The coating of claim 9 , wherein the coating has an adhesion value of 3 or greater when coated on a nickel coated stainless steel substrate, according to the Adhesion Test.

18. The coating of claim 9 , wherein the coating has an average dissolution percent of about 17 or more according to the Dissolution Test.

19. The coating of claim 9 , wherein the coating has a thickness of no greater than 1 mil (25.4 μm).

20. A method for applying the coating composition of claim 1 to a surface of a substrate, the method comprising:
contacting the surface of the substrate with the coating composition.

21. The method of claim 20 , wherein the substrate comprises nickel coated stainless steel, aluminum coated steel, zinc coated steel, copper coated steel, tin coated steel, aluminum-zinc alloy, or a combination thereof.

22. The method of claim 20 , wherein the coating composition is applied to the surface of a substrate in a design comprising a ring, concentric circles, a matrix of dots, a grid pattern, or a combination thereof.

23. The method of claim 20 , wherein contacting the surface of the substrate with the coating composition comprises ink jet printing, needle deposition, dip coating, curtain coating, spray coating, pad printing, gravure printing, reverse gravure printing, or a combination thereof.

24. A method of deterring ingestion of a substrate, comprising applying to a surface of the substrate the coating composition according to claim 1 .

25. The method of claim 24 , wherein the surface of the substrate comprises metal, plastic, wood, glass, paper, composite, ceramic, stone, or rubber.

26. An article comprising a surface of a substrate, the surface comprising the coating according to claim 9 .

27. The article of claim 26 , wherein the surface of the substrate comprises metal, plastic, wood, glass, paper, composite, ceramic, stone, or rubber.

28. A kit comprising a substrate, comprising a surface of a substrate coated with the coating composition according to claim 1 and instructions to not wash, rinse, or otherwise contact the substrate surface with water or solvents.

Assignees

• Monosol Llc

Inventors

• Knight Jonathon
• Chang Hao

Classifications

• H01M50/124

  having a layered structure · CPC title

• H01M50/126

  comprising three or more layers · CPC title

• C09D133/02

  Homopolymers or copolymers of acids; Metal or ammonium salts thereof · CPC title

• C08K5/20

  Carboxylic acid amides · CPC title

• C08K5/105

  with phenols · CPC title