Non-aqueous lithium power storage element

Patent metadata

Field	Value
Publication number	US-12199268-B2
Application number	US-202017760802-A
Country	US
Kind code	B2
Filing date	Oct 2, 2020
Priority date	Oct 4, 2019
Publication date	Jan 14, 2025
Grant date	Jan 14, 2025

Abstract

A non-aqueous lithium power storage element that includes a positive electrode, a negative electrode, a separator, and a non-aqueous electrolyte, the positive electrode having a positive electrode collector and a positive electrode active material layer that includes active carbon, and the non-aqueous lithium power storage element having configuration (1) and/or (2). (1) The negative electrode includes a negative electrode collector and a negative electrode active material layer (2) The non-aqueous electrolyte contains (A) LiPF 6 and/or LiBF 4 , (B) an imide lithium salt, and (C) an oxalate-complex lithium salt, the ratio of the mass of component (C) to the total mass of components (A) and (B) being 1.0-10.0 mass %.

First claim

The invention claimed is:

1. A non-aqueous lithium power storage element comprising a positive electrode, a negative electrode, a separator and a lithium ion-containing non-aqueous electrolyte, wherein:
the positive electrode has a positive electrode current collector and a positive electrode active material layer containing a positive electrode active material, formed on one or both sides of the positive electrode current collector,
the positive electrode active material layer further comprises carbon nanotubes and an alkali metal compound other than the positive electrode active material,
the positive electrode active material contains active carbon, and
the element is provided with at least one of the following constructions (1) and (2):
(1) the negative electrode includes a negative electrode current collector and a negative electrode active material layer on one or both sides of the negative electrode current collector,
the negative electrode active material layer includes a negative electrode active material, carbon nanotubes and a dispersing agent,
the negative electrode active material includes a carbon material, and
for all of the pixels in the bright field regions in a binarized SEM image taken of the negative electrode active material layer surface, where a set of the maximum inscribed circles encompassing each of the pixels is represented as a frequency distribution for each diameter, the area ratio Z1 which is the ratio of the total area of maximum inscribed circles with diameters of less than 100 nm occupying the total area of the maximum inscribed circles is 3.5% to 25.5%;
(2) the non-aqueous electrolyte solution comprises:
(A) at least one lithium salt from among LiPF 6 and LiBF 4 ,
(B) a lithium salt with an imide structure, and
(C) a lithium salt with an oxalate complex as the anion, and
the ratio of the mass of component (C) with respect to the sum of the mass of component (A) and the mass of component (B) in the non-aqueous electrolyte solution is 1.0 mass % to 10.0 mass %.

2. The non-aqueous lithium power storage element according to claim 1 , wherein the non-aqueous electrolyte solution comprises (B) a lithium salt with an imide structure, and component (B) is a lithium salt with an imide structure represented by the following formula (a):

{where R 1 and R 2 are each independently a hydrogen atom, halogen atom, alkyl group or alkyl halide group and at least one of R 1 and R 2 is a halogen atom or alkyl halide group}.

3. The non-aqueous lithium power storage element according to claim 1 , wherein the (B) lithium salt with an imide structure is a lithium salt selected from the group consisting of lithium bis(fluorosulfonyl)imide and lithium bis(trifluoromethane) sulfonimide.

4. The non-aqueous lithium power storage element according to claim 1 , wherein the non-aqueous electrolyte solution comprises (C) a lithium salt with an oxalate complex as the anion, and component (C) is at least one type of lithium salt selected from the group consisting of lithium bisoxalatoborate, lithium fluorooxalatoborate and lithium difluorooxalatoborate.

5. The non-aqueous lithium power storage element according to claim 1 , wherein the non-aqueous electrolyte solution comprises at least one type of nitrile compound in a range of 0.1 mol/L to 5 mol/L of the non-aqueous electrolyte solution.

6. The non-aqueous lithium power storage element according to claim 1 , wherein the non-aqueous electrolyte solution comprises at least one type of trinitrile compound selected from the group consisting of 2-amino-1,1,3-tricyano-1-propene, 1-butyl-3-methylimidazolium tricyanomethanide and lithium tricyanomethanide, in a range of 0.1 mol/L to 5 mol/L of the non-aqueous electrolyte solution.

7. The non-aqueous lithium power storage element according to claim 1 , wherein:
the negative electrode active material layer has a solid electrolyte interface (SEI) substance on the surface, and
the solid electrolyte interface (SEI) substance contains lithium oxalate represented by the following formula (b):

8. The non-aqueous lithium power storage element according to claim 1 , wherein in X-ray photoelectron spectroscopy (XPS) of the negative electrode active material layer, the ratio I1/I2, of the intensity I1 of peak P1 observed in the range of 289 eV to 290 eV and the intensity 12 of peak P2 observed in the range of 284 eV to 285 eV, is 0.1 or greater.

9. The non-aqueous lithium power storage element according to claim 1 , wherein the non-aqueous electrolyte solution comprises at least one type of ether compound selected from the group consisting of 1,2-dimethoxyethane, 1,2-diethoxyethane, tetrahydrofuran, 1,3-dioxane, 1,4-dioxane and 2-methyltetrahydrofuran, in the range of 1 mol/L to 10 mol/L in the non-aqueous electrolyte solution.

10. The non-aqueous lithium power storage element according to claim 1 , wherein in a binarized SEM image of the surface of the negative electrode active material layer, the area ratio Z2 of the total area of regions of 1,000 nm 2 to 5,000 nm 2 of the dark field regions among the total area of regions of 1,000 nm 2 to 20,000 nm 2 , is 63.0% to 92.0%.

11. The non-aqueous lithium power storage element according to claim 1 , wherein:
the mass ratio of the alkali metal compound with respect to the total mass of the positive electrode active material layer in the positive electrode, represented as C2 (mass %), is 0.1≤C2≤7.0, and
in a binarized SEM image of 1,280×890 pixels (1 pixel=9.96 nm) taken of the surface of the positive electrode active material layer of the positive electrode at a magnification of 10,000x, the area ratio Z′2 of the total area of maximum inscribed circles with diameters of less than 100 nm occupying the total area of the maximum inscribed circles is 7.5% to 35.0%, where a set of the maximum inscribed circles encompassing each of the pixels, for all of the pixels in the bright field regions, is represented as a frequency distribution for each diameter.

12. The non-aqueous lithium power storage element according to claim 11 , wherein
in the XRD (X-ray diffraction) spectrum measured for the positive electrode active material layer, there is a peak X2 with 20 in the range of 25.7° to 27.0°, and the half-width of the peak X2 is 0.1° to 0.5°, and
in the XRD (X-ray diffraction) spectrum measured for the negative electrode active material layer, there is a peak Y1 having a peak top with 20 in the range of 26.2° to 26.5°, and the half-width of the peak Y1 is 0.1° to 0.5°.

13. The non-aqueous lithium power storage element according to claim 11 , wherein
the total concentration of Fe atoms and Ni atoms in the negative electrode active material layer is 1 ppm to 500 ppm, and
the total concentration of Fe atoms and Ni atoms in the positive electrode active material layer is 1 ppm to 500 ppm.

14. The non-aqueous lithium power storage element according to claim 11 , wherein the alkali metal compound is at least one type selected from the group consisting of lithium carbonate, sodium carbonate and potassium carbonate.

15. The non-aqueous lithium power storage element according to claim 11 , wherein the mean fiber diameter of the carbon nanotubes is 2 nm or greater and less than 100 nm.

16. The non-aqueous lithium power storage element according to claim 15 , wherein:
the positive electrode active material further comprises a lithium transition metal

Assignees

• Asahi Chemical Ind

Inventors

• Takada Kazuaki
• Umetsu Kazuteru
• Nakamura Fumiya
• Yamahata Yusuke
• Kimura Yuima
• Matsushita Tadashi

Classifications

• H01M10/052

  Li-accumulators · CPC title

• H01M4/525

  of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy · CPC title

• H01M4/505

  of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy · CPC title

• H01M4/38

  of elements or alloys · CPC title

• H01M4/134 Primary

  Electrodes based on metals, Si or alloys · CPC title