High-performance toothed belt made of EPDM

Patent metadata

Field	Value
Publication number	US-12196289-B2
Application number	US-202118257934-A
Country	US
Kind code	B2
Filing date	Nov 25, 2021
Priority date	Dec 18, 2020
Publication date	Jan 14, 2025
Grant date	Jan 14, 2025

Abstract

The present invention relates to elastomer toothed belts comprising a fabric spanning the teeth of the toothed belt, wherein the elastomer mixture forming the teeth contains a crosslinked ethylene-propylene rubber (EPM) and/or a crosslinked ethylene-propylene terpolymer rubber (EPDM) accounting for at least 70% by weight of the elastomer mixture based on the polymer proportion and wherein an interlayer is arranged between the fabric and the elastomer mixture forming the teeth which contains at least 70% by weight of hydrogenated acrylonitrile-butadiene rubber (HNBR) based on the polymer proportion of the interlayer. Such elastomer toothed belts are halogen-free and feature improved durability and good low-temperature stability properties. The present invention further relates to processes for producing such elastomer toothed belts and to the use of a layer of hydrogenated acrylonitrile-butadiene rubber (HNBR) in such toothed belts to increase service life, to improve low-temperature stability and to improve the adhesion between the teeth and the fabric.

First claim

The invention claimed is:

1. An elastomer toothed belt comprising:
a body having a length and sides arranged at a lateral distance to one another also having an inside, an outside and a plurality of teeth spaced apart from one another in a longitudinal direction on the inside and/or the outside;
a fabric that spans the plurality of teeth; and
an elastomer mixture that forms the teeth contains a crosslinked ethylene-propylene rubber (EPM) and/or a crosslinked ethylene-propylene terpolymer rubber (EPDM) which accounts for at least 70% by weight of the elastomer mixture based on the polymer proportion and wherein an interlayer containing at least 70% by weight of hydrogenated acrylonitrile-butadiene rubber (HNBR) based on the polymer proportion of the interlayer is arranged between the fabric and the elastomer mixture forming the teeth,
wherein the interlayer contains an additive that imparts electrical conductivity to the interlayer.

2. The belt of claim 1 , wherein the teeth contain the crosslinked ethylene-propylene rubber (EPM) and/or an ethylene-propylene terpolymer rubber (EPDM) in a proportion of at least 80% by weight based on the polymer proportion of the elastomer mixture forming the teeth.

3. The belt of claim 1 , wherein the body is formed from crosslinked ethylene-propylene rubber (EPM) and/or ethylene-propylene-terpolymer rubber (EPDM) as the elastomer.

4. The belt of claim 1 , wherein the crosslinked elastomer in the elastomer mixture from which the teeth are formed is a sulfur-crosslinked or peroxidically crosslinked elastomer.

5. The belt of claim 1 , wherein the interlayer contains at least 80% by weight of hydrogenated acrylonitrile-butadiene rubber (HNBR) based on the polymer proportion of the interlayer.

6. The belt of claim 1 , wherein the hydrogenated acrylonitrile-butadiene rubber has a degree of hydrogenation in the range from 70% to 99% and/or an acrylonitrile content of 18% to 47% by mass.

7. The belt of claim 1 , wherein the interlayer has a thickness in a range from about 10 to 500 μm and/or a Shore A hardness of less than 90.

8. The belt of claim 1 , wherein the additive for imparting electrical conductivity is in the form of carbon black.

9. The belt of claim 8 , wherein the interlayer contains a proportion of 20 to 70 parts of the carbon black based on 100 parts of polymer in the interlayer and wherein the elastomer toothed belt has an electrical resistance determined according to ISO 9563:2015 of less than 50 MΩ.

10. The belt of claim 1 , wherein the fabric is formed to an extent of more than 70% from polyamide.

11. The belt of claim 1 , wherein the fabric has a coating with a resorcinol/formaldehyde/latex, wherein the latex of the resorcinol/formaldehyde/latex has a vinylpyridine content of more than 50% by weight.

12. The belt of claim 1 , wherein the elastomer toothed belt has an electrical resistance determined according to ISO 9563:2015 of less than 5 MΩ.

13. The belt of claim 1 , wherein the hydrogenated acrylonitrile-butadiene rubber has a degree of hydrogenation in the range from 95% to 99% and an acrylonitrile content of 30% to 47% by mass.

14. The belt of claim 1 , wherein the interlayer has a thickness in a range from 50 μm to 200 μm.

15. A method for producing an elastomer toothed belt, the method comprising:
(i) providing a fabric;
(ii) applying a coating to the fabric, wherein the coating is formed from a coating composition that contains at least 70% by weight of hydrogenated acrylonitrile-butadiene rubber (HNBR) based on the polymer proportion in the coating composition, and wherein the coating composition contains an additive that imparts electrical conductivity to the coating, and
(iii) securing the fabric to an elastomer toothed belt body whose teeth are formed from an elastomer mixture containing at least 70% by weight, based on the polymer proportion of the elastomer mixture forming the teeth, a crosslinked ethylene-propylene rubber (EPM) and/or a crosslinked ethylene-propylene terpolymer rubber (EPDM) in such a way that the coating from step (ii) is arranged between the teeth and the fabric,
wherein the elastomer toothed belt has an electrical resistance determined according to ISO 9563:2015 of less than 5 MΩ.

16. The method of claim 15 , wherein the coating in step (ii) is carried out by applying a solution of the hydrogenated acrylonitrile-butadiene rubber to the fabric and subsequently evaporating the solvent or by calendering a film containing the hydrogenated acrylonitrile-butadiene rubber onto the fabric.

17. The method of claim 15 , wherein the process additionally comprises a step of applying an adhesion-promoting layer of resorcinol/formaldehyde/latex to the fabric prior to step (i), the resorcinol/formaldehyde/latex having a vinylpyridine content of more than 50% by weight.

18. The method of claim 15 , further comprising incorporating a layer of hydrogenated acrylonitrile-butadiene rubber (HNBR) arranged between ethylene-propylene rubber (EPM) and/or ethylene-propylene-terpolymer rubber (EPDM) teeth of the toothed belt and incorporating a fabric spanning the teeth for increasing the service life of the toothed belt and/or for improving the adhesion between the teeth and the fabric in a toothed belt and/or improving the low-temperature stability of the toothed belt.

19. An elastomer toothed belt comprising:
a body having a length and sides arranged at a lateral distance to one another also having an inside, an outside and a plurality of teeth spaced apart from one another in a longitudinal direction on the inside and/or the outside;
a fabric that spans the plurality of teeth; and
an elastomer mixture that forms the teeth contains a crosslinked ethylene-propylene rubber (EPM) and/or a crosslinked ethylene-propylene terpolymer rubber (EPDM) which accounts for at least 70% by weight of the elastomer mixture based on the polymer proportion and wherein an interlayer containing at least 70% by weight of hydrogenated acrylonitrile-butadiene rubber (HNBR) based on the polymer proportion of the interlayer is arranged between the fabric and the elastomer mixture forming the teeth,
wherein the fabric has a coating with a resorcinol/formaldehyde/latex, wherein the latex of the resorcinol/formaldehyde/latex has a vinylpyridine content of more than 50% by weight.

20. The belt of claim 19 , wherein the fabric is formed to an extent of more than 70% from linear aliphatic amide.

Assignees

• Contitech Antriebssysteme Gmbh
• Contitech Deutschland Gmbh

Inventors

• Teves Reinhard
• Sattler Heiko
• Michalk Jan
• Dikmans Antonius
• Kanzow Henning
• Kautz Stephanie

Classifications

• B29D29/08

  Toothed driving belts · CPC title

• B29K2309/08

  Glass · CPC title

• B29K2995/007

  Hardness · CPC title

• B29K2995/0077

  Yield strength; Tensile strength · CPC title

• B29K2009/00

  Use of rubber derived from conjugated dienes, as moulding material · CPC title