Method for manufacturing insulation products based on mineral wool

Patent metadata

Field	Value
Publication number	US-12187642-B2
Application number	US-202117791309-A
Country	US
Kind code	B2
Filing date	Jan 5, 2021
Priority date	Jan 9, 2020
Publication date	Jan 7, 2025
Grant date	Jan 7, 2025

Abstract

The invention relates to a method for manufacturing insulation products based on mineral wool bound by an organic binder, comprising the following successive steps:
(a) providing mineral wool at room temperature, (b) applying, to the mineral wool, an aqueous thermosetting binder composition, (c) drying the mineral wool impregnated with the aqueous thermosetting binder composition to obtain thermosetting mineral wool, (d) shaping the thermosetting mineral wool, and (e) heating the shaped thermosetting mineral wool at a temperature for long enough to enable the constituents of the binder to be condensed and an insoluble binder to be formed.

First claim

The invention claimed is:

1. A method for manufacturing an insulation product comprising mineral wool bound by an organic binder, the method comprising the following successive steps:
(a) providing mineral wool at room temperature;
(b) applying, to the mineral wool, an aqueous thermosetting binder composition;
(c) drying the mineral wool impregnated with the aqueous thermosetting binder composition, to obtain thermosetting mineral wool;
(d) shaping the thermosetting mineral wool; and
(e) heating the shaped thermosetting mineral wool at a temperature for long enough to enable the constituents of the binder to be condensed and an insoluble binder to be formed.

2. The method according to claim 1 , wherein the mineral wool provided in step (a) is virgin mineral wool or recycled mineral wool, or a blend of virgin mineral wool and recycled mineral wool.

3. The method according to claim 1 , wherein during the step of applying the aqueous binder composition the mineral wool is at room temperature.

4. The method according to claim 1 , further comprising, between step (c) and step (d):
blending the thermosetting mineral wool with virgin mineral wool and/or with recycled mineral wool and/or with natural organic fibers.

5. The method according to claim 4 , wherein the natural organic fibers are plant fibers or animal fibers.

6. The method according to claim 4 , wherein 100 parts by weight of thermosetting mineral wool are blended with 10 to 400 parts by weight of virgin mineral wool and/or recycled mineral wool and/or natural organic fibers.

7. The method according to claim 1 , wherein the drying of mineral wool impregnated with aqueous binder composition in (c) is carried out by heating to a temperature comprised between 6° and 110° C.

8. The method according to claim 1 , wherein the thermosetting mineral wool comprises 3 to 20% by dry weight of thermosetting binder.

9. The method according to claim 1 , wherein an insulation product obtained in (e) has a density comprised between 4 and 150 kg/m 3 .

10. The method according to claim 1 , wherein an insulation product obtained in (e) has a thickness comprised between 20 mm and 500 mm.

11. The method according to claim 1 , wherein the aqueous binder composition comprises more than 50% by dry weight of a biosourced reagent.

12. The method according to claim 11 , wherein the biosourced reagent is at least one selected from the group consisting of a saccharides and a saccharide hydrogenation product.

13. The method according to claim 1 , wherein the shaping of the thermosetting mineral wool in (d) is carried out by molding and/or compressing the thermosetting mineral wool.

14. The method according to claim 1 , wherein the heating temperature in (e) is comprised between 130° C.

15. The method according to claim 4 , wherein the natural organic fibers are blended with the thermosetting mineral wool and the natural organic fibers are at least one selected from the group consisting of lignocellulosic fibers, cotton, and animal wools.

16. The method according to claim 4 , wherein 100 parts by weight of thermosetting mineral wool are blended with 20 to 300 parts by weight of virgin mineral wool and/or recycled mineral wool and/or natural organic fibers.

17. The method according to claim 7 , wherein the temperature of the heating is comprised between 7° and 100° C.

18. The method according to claim 1 , wherein the thermosetting mineral wool comprises 4 to 18% by dry weight of thermosetting binder.

Assignees

• Saint Gobain Isover

Inventors

• Seck Mamadou
• Delmee Mickael
• Guyot Pierrick

Classifications

• B29C70/28

  Shaping operations therefor · CPC title

• C03C13/06

  Mineral fibres, e.g. slag wool, mineral wool, rock wool · CPC title

• C03C25/26 Primary

  Macromolecular compounds or prepolymers · CPC title

• C03C25/28 Primary

  obtained by reactions involving only carbon-to-carbon unsaturated bonds · CPC title