Thermally curable film-forming compositions providing benefits in appearance and sag control performance

Patent metadata

Field	Value
Publication number	US-12173172-B2
Application number	US-201716956970-A
Country	US
Kind code	B2
Filing date	Dec 22, 2017
Priority date	Dec 22, 2017
Publication date	Dec 24, 2024
Grant date	Dec 24, 2024

Abstract

Disclosed are thermally curable film-forming compositions comprising a binder, a flow control system comprising a sag control agent, and less than 5.0 wt.-% of melamine-based components, based on the total weight of resin solids in the film-forming composition, as well as methods for forming a cured coating on a substrate and substrates comprising the cured coating layer.

First claim

What is claimed is:

1. A thermally curable film-forming composition comprising a binder, a flow control system comprising a sag control agent for controlling the viscosity of the film-forming composition applied to a surface,
wherein the film-forming composition comprises melamine-based components and the melamine-based components are present in the film-forming composition at less than 5.0 wt.-%, based on a total weight of resin solids in the film-forming composition, wherein the sag control agent comprises a reaction product of reactants consisting of an amine and an isocyanate,
wherein the film-forming composition does not have a complex viscosity, η*, below an initial complex viscosity η* 1 at any point during flash off and thermal curing; and
wherein the rheological properties of the film-forming composition are determined by first applying a large amplitude oscillatory shear at a frequency of 1 Hz and an amplitude of 10000% with a maximum shear rate of 628 s −1 followed 12 seconds after stopping the large amplitude oscillatory shear by determining an initial complex viscosity, η* 1 , at a stress of 1 Pa and frequency of 1 Hz at 25° C.;
and
wherein the large amplitude oscillatory shear is applied, and the initial complex viscosity, η* 1 , and the complex viscosity, η*, are determined using a rotational rheometer in oscillatory mode using a 25 mm ring plate, 0.15 mm gap, stress of 1 Pa, and frequency of 1 Hz.

2. The composition of claim 1 wherein the binder comprises an acrylic polyol.

3. The composition of claim 1 wherein the composition comprises 20 to 70 wt.-% of a polyol, based on the total weight of resin solids in the film-forming composition.

4. The composition of claim 1 wherein the flow control system comprises a sag control agent which comprises particulates at a temperature of 23° C. in the absence of a shear force and a solvent.

5. The composition of claim 1 , wherein the sag control agent comprises a urea-type sag control agent,
wherein the sag control agent comprises the reaction product of reactants consisting of toluene diisocyanate, 4,4′-methylene-bis(cyclohexyl isocyanate), isophorone diisocyanate, 2,2,4-trimethyl hexamethylene diisocyanate, 2,4,4-trimethyl hexamethylene diisocyanate, 1,6-hexamethylene diisocyanate, tetramethyl xylylene diisocyanate and/or 4,4′-diphenylmethylene diisocyanate with ethylamine, isomeric propylamines, butylamines, pentylamines, hexylamines, cyclohexylamine, and/or benzylamine.

6. The composition of claim 1 wherein the film-forming composition comprises 0.2 to 2 wt.-% of the sag control agent, based on the total amount of solids in the film-forming composition.

7. The composition of claim 1 further comprising a crosslinking agent.

8. The composition of claim 7 wherein the thermally curable film-forming composition is a two-component composition comprising a first component comprising a crosslinkable resin and a second component comprising the crosslinking agent, wherein the flow control system may be present in any of the first component or the second component or both.

9. The composition of claim 7 wherein the crosslinking agent comprises a polyisocyanate.

10. The composition of claim 7 wherein the film-forming composition comprises a binder having functional groups and a crosslinking agent having functional groups, wherein the functional groups in the binder are reactive with the functional groups in the crosslinking agent, and wherein the ratio of functional groups in the binder capable of reacting with the functional groups of the crosslinking agent to said functional groups in the crosslinking agent ranges from 0.8:1 to 1.2:1.

11. The composition of claim 1 further comprising a polymeric polyol resin.

12. The composition of claim 1 further comprising 30 to 60 wt.-% of an organic solvent, based on the total weight of the film-forming composition.

13. The composition of claim 1 comprising less than 1 wt.-% of a silica-based rheology control agent, based on the total amount of solids in the film-forming composition.

14. The composition of claim 1 having an initial complex viscosity η* 1 of at least 150 cP.

15. A method of forming a cured coating layer on a substrate comprising:
selecting a thermally curable film-forming composition having the following properties:
the film-forming composition comprises a binder, a flow control system comprising a sag control agent for controlling the viscosity of the film-forming composition applied to a surface, and melamine-based components, wherein the melamine-based components are present in the film-forming composition at less than 5.0 wt.-%, based on a total weight of resin solids in the film-forming composition;
wherein the sag control agent comprises a reaction product of reactants consisting of an amine and an isocyanate;
wherein the film-forming composition does not have a complex viscosity, η*, below an initial complex viscosity η* 1 at any point during flash off and thermal curing;
wherein the rheological properties of the film-forming composition are determined by first applying a large amplitude oscillatory shear at a frequency of 1 Hz and an amplitude of 10000% with a maximum shear rate of 628 s −1 followed 12 seconds after stopping the large amplitude oscillatory shear by determining the initial complex viscosity, η* 1 , at a stress of 1 Pa and frequency of 1 Hz at 25° C., and the large amplitude oscillatory shear is applied, and the initial complex viscosity, η* 1 , and the complex viscosity, η*, are determined using a rotational rheometer in oscillatory mode using a 25 mm ring plate, 0.15 mm gap, stress of 1 Pa, and frequency of 1 Hz;

applying the curable film-forming composition to at least a portion of a surface of the substrate; and
thermally curing the applied composition.

16. The method of claim 15 wherein applying the composition comprises spraying the composition onto at least a portion of a surface of the substrate to form a layer.

17. The method of claim 15 wherein thermally curing the composition applied to at least a portion of a surface of the substrate comprises maintaining the surface at a temperature in the range of from 20 to 25° C. for 2 to 15 minutes, followed by heating the at least partially coated substrate to an elevated temperature of at least 60° C. within 5 to 15 min and maintaining the at least partially coated substrate at said elevated temperature for at least another 15 min.

18. The method of claim 15 wherein the film thickness of the cured coating layer ranges from 25 to 75 μm.

19. A substrate comprising a cured coating layer obtained by applying the composition according to claim 1 to at least a portion of a surface of the substrate and thermally curing the applied composition.

20. The substrate of claim 19 wherein the composition is a clear coat composition and the substrate is a vehicle or a portion thereof which optionally may comprise an additional coating layer disposed below the coating layer obtained from the clear coat composition.

Assignees

• Ppg Ind Ohio Inc

Inventors

• Moyano Daniel F
• Luchansky Matthew S
• Stibbard Mitchell R

Classifications

• C08K5/21

  Urea; Derivatives thereof, e.g. biuret · CPC title

• C08K3/36

  Silica · CPC title

• C08J2375/06

  from polyesters · CPC title

• C08J7/08

  Heat treatment · CPC title

• B05D3/0254

  After-treatment · CPC title